Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 193 MPa | 28000 psi | ASTM D638 |
Oxford Polymers Oxnilon 66-43GF 43% Glass Fiber Filled Nylon 66 for Injection Molding 43% Glass Fiber Filled Nylon 66 for Injection MoldingInformation provided by Oxford Polymers. |
|||
Tensile Strength at Break | 193 MPa | 28000 psi | ASTM D638 |
Polymer Resources NY6-G33 Nylon 6, 33% Glass Reinforced Nylon 6, 33% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are teste.. |
|||
Tensile Strength at Break | 193 MPa | 28000 psi | ASTM D638 |
Polymer Resources NY6-G33-[color]-H Nylon 6, 33% Glass Reinforced, Heat Stabilized Nylon 6, 33% Glass Reinforced, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon.. |
|||
Tensile Strength at Break | 193 MPa | 28000 psi | ASTM D638 |
Polymer Resources NY6-G33-[color]H Nylon, 33% Glass Reinforced, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
Tensile Strength at Break | 193 MPa | 28000 psi | ASTM D638 |
Ravago Manufacturing Americas Hylon® N1033HL Nylon 6/6 (DAM) Information provided by Ravago. |
|||
Tensile Strength at Break | 193 MPa | 28000 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Edgetek® NY-20CF/000 BLACK Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
Tensile Strength at Break | 193 MPa | 28000 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ GF 1200 A 33 HS Black 22 Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil.. |
|||
Tensile Strength at Break | 193 MPa | 28000 psi | Conditioned; ASTM D638 |
Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0.. |
|||
Tensile Strength at Break | 193 MPa | 28000 psi | 73°F; ASTM D638 |
Ravago Manufacturing Americas Hylon® N1035HLHR Nylon 6/6 (DAM)
(discontinued **) Information provided by Ravago. |
|||
Tensile Strength at Break | 193 MPa | 28000 psi | ASTM D638 |
Ravago Manufacturing Americas Hylon® N1035HHR Nylon 66, 35% Glass Filled
(discontinued **) Heat Stabilized, Hydrolysis Resistant in Automotive CoolantInformation provided by Ravago. |
|||
Tensile Strength at Break | 193 - 228 MPa | 28000 - 33000 psi | Copper butt joint |
Lucas-Milhaupt BRAZE 452 Characteristics:Braze 452 is a free-flowing, low temperature filler metal commonly used to replace cadmium-bearing filler metals of similar silver content. This alloy is best suited for narrow gap .. |
|||
Tensile Strength at Break | 193 MPa | 28000 psi | ISO 527 Type 1A |
Solvay TECHNYL® C 218 V33 PA6, 33% glass fiber, Eh 0 Description: Polyamide PA6, reinforced with 33% of glass fiber, heat stabilized, for injection molding.Applications: It has good mechanical properties, it is used in all sectors of industry, offerin.. |
|||
Tensile Strength at Break | 193 MPa | 28000 psi | ISO 527 |
Solvay Technyl® C218V30 30% Glass Filled, Heat Stabilized Nylon 6 Information provided by Rhodia; Rhodia has been acquired by Solvay. |
|||
Tensile Strength at Break | 193 MPa | 28000 psi | ASTM D638 |
Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Conditioned) Amodel® AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater th.. |
|||
Tensile Strength at Break | 193 MPa | 28000 psi | ASTM D638 |
Techmer ES Electrafil® J-4/25/CF/15 BK PA6/12 |
|||
Tensile Strength at Break | 193 MPa | 28000 psi | ASTM D638 |
Techmer ES Electrafil® M-1322 PA66 / PA6 |
|||
Tensile Strength at Break | 193 MPa | 28000 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp EF008E PEI LNP* Thermocomp* EF008E is a compound based on Polyetherimide resin containing Glass Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas.. |
|||
Tensile Strength at Break | 193 MPa | 28000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP VC006 SUPER TOUGH NYLON LNP* THERMOTUF* VC006 is a compound based on Super Tough Nylon resin containing 30% Carbon Fiber. Added features of this material include: High Impact, Electrically Conductive. |