- Polymer Property : Tensile Strength at Break = 2760 psi
Polymer Property : Tensile Strength at Break = 2760 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO 527 |
| Polimeri Europa Eraclene® MM 74 U High Density Polyethylene - Injection Molding Eraclene MM 74 U is a gas phase high density polyethylene resin (HDPE) with antioxidants, suitable for injection molding application.This grade has a narrow molecular weight distribution. The polym.. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON MX12407C PP LNP* STAT-KON* MX12407C is a compound based on Polypropylene resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP MB006S PP LNP THERMOCOMP* MB006S is a compound based on Polypropylene resin containing 30% Glass Bead. Added features of this material include: Heat Stabilized. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO R 527 |
| Silon Taborex TA 1132 HD Chemically-Crosslinkable HDPE Compound TABOREX TA 1132 HD is a crosslinkable compound made of Silane grafted ethylene polymer. This graft polymer constitutes together with a Masterbatch containing the crosslinking catalyst a “SIOPLA.. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP SH1100A PA12 LNP* Thermocomp* SH1100A is a Nylon 12, High Specificy Gravity compound containing proprietary fillers. |
|||
| Tensile Strength at Break | >= 19.0 MPa | >= 2760 psi | ASTM D638 |
| UBE PAE1200U2 Electronic Grade Nylon Elastomer Description: UBESTA Nylon 12 has an excellent termite resistance than other plastics. UBESTA contributes as a material for jacket and sheath which lay for telephone and telegram Communication System.. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 |
| UBE V206 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO 527-2/50 |
| ExxonMobil Exxtral™ CMU 201 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin designed for automotive interior covered applications such as retainers in which a good stiffness toughness balance is required.Availa.. |
|||
| Tensile Strength at Break | 19.0 - 22.0 MPa | 2760 - 3190 psi | ASTM D638 |
| Daikin NEOFLON NP-40 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding, transfer molding, compression molding.Applications: Films and s.. |
|||
| Tensile Strength at Break | 19.03 MPa | 2760 psi | JIS-K-6723 |
| Denka VINYKON W7300E PVC, W grade for non-migratory sheath and special items A PVC resin compound offering excellent physical properties and workability. A broad product lineup is available, including hard and soft grades, as well as those for extrusion and injection molding.. |
|||
| Tensile Strength at Break | >= 19.0 MPa | >= 2760 psi | ISO R 527 |
| Fainplast Compounds CKL 90/40 Flexible PVC, Sheathing Lead Free General purposes (75°C) |
|||
| Tensile Strength at Break | >= 19.0 MPa | >= 2760 psi | ISO R 527 |
| Fainplast Compounds FK 90/1 Flexible PVC, Insulation Lead Free Oil resistant insulation |
|||
| Tensile Strength at Break | 19.0 - 22.0 MPa | 2760 - 3190 psi | ASTM D638 |
| Daikin NEOFLON NP-20 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding, injection molding.Applications: Wire and cable coatings, films,.. |
|||
| Tensile Strength at Break | >= 19.0 MPa | >= 2760 psi | ISO R 527 |
| Fainplast Compounds FR 95/1 Flexible PVC, Insulation General purposes |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO R 527 |
| Fainplast Compounds PHT 0144 Flexible PVC, Transparent Extrusion Profiles high temperatures |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 |
| Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness) AZDEL SuperLite® SL551000-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
| Tensile Strength at Break | >= 19.0 MPa | >= 2760 psi | ASTM D4745-11 |
| Adamas Adalon® 113 PTFE, 23/2% Carbon/Graphite Filled Information provided by Adamas, HPM |
|||
| Tensile Strength at Break | >= 19.0 MPa | >= 2760 psi | ASTM D4894 |
| Adamas Adalon® 206 PTFE, 15/5% Glass/MoS2 Filled Information provided by Adamas, HPM |
|||
| Tensile Strength at Break | >= 19.0 MPa | >= 2760 psi | ASTM D4894 |
| Adamas Adalon® 215 PTFE, 17% Glass Filled, Blue Information provided by Adamas, HPM |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO R 527 |
| Addiplast Addilene H 520 T40 Polypropylene Homopolymer Mineral reinforced, improved rigidityInformation provided by Addiplast. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO R 527 |
| Addiplast Addilene H 530 N30 Polypropylene Homopolymer Good surface appearanceInformation provided by Addiplast. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO R 527 |
| Addiplast Addilene H 532 N30 Polypropylene Homopolymer Good surface appearanceInformation provided by Addiplast. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO R 527 |
| Addiplast Addilene PMD 50258 Polypropylene Copolymer For electroplatingInformation provided by Addiplast. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 |
| Arkema Group OREVAC® 9307 Y EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre.. |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 |
| Aclo Accutech Polypropylene Copolymer CP0436T30L1 Talc Reinforced |
|||
| Tensile Strength at Break | >= 19.0 MPa | >= 2760 psi | ISO R 527 |
| Fainplast Compounds CKL 63/K Flexible PVC, Sheathing Lead Free Opaque sheath |
|||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO R 527 |
| Fainplast Compounds PH 90/A Flexible PVC, Transparent Extrusion Profiles, UL 94 Class V1 |
|||