Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | >= 17.65 MPa | >= 2560 psi | ISO 527 |
LG Chemical LUTENE XL8080TR PE Compound Description: LUTENE XL8080TR has excellent electrical properties for medium and high voltage power cable insulation and especially it shows improved water tree resistance and has thermal aging prope.. |
|||
Tensile Strength at Break | 17.7 MPa | 2560 psi | ASTM D638 |
Teknor Apex APEX® 4855-LF Polyvinyl Chloride, Flexible Notes: RoHS Compliant Features: Flame Retardant; Good UV Resistance; Sunlight Resistant (720 hours) Uses: Building Wire Jacketing Agency Ratings: UL QMTT2 .E73402 Wire Types: SEC Forms: PelletsInfor.. |
|||
Tensile Strength at Break | 17.7 MPa | 2560 psi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FC 2181 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2181 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
Tensile Strength at Break | 17.7 MPa | 2560 psi | |
Zeon Chemicals Nipol® DN1201L Terpolymer Elastomer Nipol DN1201L is a low-temperature polymerized terpolymer of acrylonitrile, butadiene and isoprene. This polymer is intended to give better physical and processing characteristics than a regular nit.. |
|||
Tensile Strength at Break | 17.7 MPa | 2560 psi | |
Zeon Chemicals Nipol® DN1201 Terpolymer Elastomer Nipol DN1201 is a low-temperature polymerized terpolymer of acrylonitrile, butadiene and isoprene. This polymer is intended to give better physical and processing characteristics than a conventional.. |