Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 176 MPa | 25500 psi | ASTM D638 |
LNP Thermocomp® LF-1006 Polyetheretherketone, Glass Fiber Reinforcement
(discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names.. |
|||
Tensile Strength at Break | 176 MPa | 25500 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP LF006 PEEK LNP THERMOCOMP* LF006 is a compound based on Polyetheretherketone resin containing 30% Glass Fiber. |
|||
Tensile Strength at Break | 176 MPa | 25500 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP QF007 PA 6/10 LNP* THERMOCOMP* QF007 is a compound based on Nylon 6/10 resin containing 35% Glass Fiber. |
|||
Tensile Strength at Break | 176 MPa | 25500 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP QF007 PA 6/10 (Asia Pacific) LNP* Thermocomp* QF007 is a compound based on Nylon 6/10 resin containing Glass Fiber. |
|||
Tensile Strength at Break | 176 MPa | 25500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON REF42I PA 66 LNP* STAT-KON* REF42I is a compound based on Nylon 6/6 containing Proprietary Fillers. Added feature of this grade is: Electrically Conductive. |
|||
Tensile Strength at Break | 176 MPa | 25500 psi | ASTM D638 |
Chase Plastics CP Pryme® N130GL (DAM) Nylon 6, 30% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
Tensile Strength at Break | 176 MPa | 25500 psi | ASTM D638 |
Chase Plastics CP Pryme® N130L Nylon 6, 30% Glass Fiber Reinforced, Lubricated Features: LubricatedForm: PelletsInformation provided by Chase Plastics. |