Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 171 MPa | 24800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM SF2350 PEI Blend High flow Ultem blends for thin wall application |
|||
Tensile Strength at Break | 171 MPa | 24800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM SF2350 PEI Blend (Asia Pacific) High flow Ultem blends for thin wall application |
|||
Tensile Strength at Break | 171 MPa | 24800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem SF2350 PEI Blend (Europe-Africa-Middle East) High flow Ultem blends for thin wall applicationThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 171 MPa | 24800 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON RX05489 PA 66 (Asia Pacific) LNP* STAT-KON* RX05489 is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated. |
|||
Tensile Strength at Break | 171 MPa | 24800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP QF008 PA 6/10 (Asia Pacific) LNP* Thermocomp* QF008 is a compound based on Nylon 6/10 resin containing Glass Fiber. |
|||
Tensile Strength at Break | 171 MPa | 24800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP QF008 PA6.10 LNP* THERMOCOMP* QF008 is a compound based on Nylon 6/10 resin containing 40% Glass Fiber. |
|||
Tensile Strength at Break | 171 MPa | 24800 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp QF008R PA 6/10 LNP* Thermocomp* QF008R is a compound based on Nylon 6/10 containing Glass Fiber. Characteristics of this grade are: Easy Release.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 171 MPa | 24800 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp QF008S PA 6/10 LNP* Thermocomp* QF008S is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas .. |
|||
Tensile Strength at Break | 171 MPa | 24800 psi | ASTM D638 |
SABIC Innovative Plastics LNP VERTON RV008E PA 66 LNP* VERTON* RV008E is a compound based on Nylon 66 resin containing 40% Long Glass Fiber. Added features of this material include: Easy Molding, Structural. |
|||
Tensile Strength at Break | 171 MPa | 24800 psi | ASTM D638 |
SABIC Innovative Plastics LNP VERTON RV008E PA 66 (Asia Pacific) LNP* VERTON* RV008E is a compound based on Nylon 66 resin containing Long Glass Fiber. Added features of this material include: Easy Molding. |
|||
Tensile Strength at Break | 171 MPa | 24800 psi | ASTM D638 |
Unitika RUN35-C25 Weather resistant PA6, Dry Weather resistant, noncoating, external exposure-compatibleInformation provided by Unitika Ltd. |
|||
Tensile Strength at Break | 171 MPa | 24800 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ GF 1800 43 Natural Nylon 612 with 43% Glass Fiber
(discontinued **) Molded Test Bars: Dry as Molded |
|||
Tensile Strength at Break | 171 MPa | 24800 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp QF008S PA 6/10 (Asia Pacific) LNP* Thermocomp* QF008S is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia Paci.. |