Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | <= 160 MPa | <= 23200 psi | ISO/R527 |
Polykemi AB SCANMID 6 B/C12^ F30 Nylon 6, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 160 MPa @Temperature 23.0 °C |
23200 psi @Temperature 73.4 °F |
ISO 527-2/5 |
PolyOne Bergamid™ B70 W25 G45 H Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ASTM D638 |
LNP Stat-Kon® LC-1003 EM Polyetheretherketone, Carbon Fiber Reinforcement
(discontinued **) Features: Good Moldability, Electrically ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; howev.. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527 |
Grupo Repol Dinalon® B1X25 G30W PA6 30% Glass Fiber, Reduced Water Abs. Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527-1/-2 |
Lanxess Durethan® BKV 130 H2.0 901510 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer-modified, electroplateable, improved notched impact strength and energy absorption under biaxial impact load, good heat-ageing resistance |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527-1/-2 |
Lanxess Durethan® BKV 25 H2.0 LT 904040 Nylon 6, 25% Glass Fiber PA 6, injection molding grade, 25% glass fibers, good heat-ageing resistance, laser-weldable |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ASTM D638 |
Mitsui Arlen™ CH230N 30% Glass Fiber-Reinforced Modified Nylon 6T, Flame Retardant (DAM) ARLEN™ is a heat resistant, modified polyamide 6T developed by Mitsui Chemicals, Inc. With a high melting point (320°C) and a rigidity level comparable to super engineering plastics, it poss.. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RFN16S PA 66 LNP LUBRICOMP* RFN16S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% MOS2. Added features of this material include: Heat Stabilized, Wear Resistant. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM 2310EPR PEI (Asia Pacific) 30% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® V9290 PET (Europe-Africa-Middle East) 45% GF PET, Glass, Mold Release, Heat Stabilized, |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP LF006EL PEEK (Europe-Africa-Middle East) LNP* THERMOCOMP* LF006EL is a compound based on Polyetheretherketone resin containing Glass Fiber. Added features include: Easy Molding. FDA Compliant Raw Materials. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP PF1006HI005 PA 6 (Europe-Africa-Middle East) High Impact Nylon 6 compound containing Glass Fiber. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RF006XXH PA 66 LNP* THERMOCOMP* RF006XXH is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this material is: Healthcare. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp PF006 PA 6 (Europe-Africa-Middle East) 30% glass fibre reinforced Polyamide 6 injection moulding resin.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP PF006U PA 6 (Europe-Africa-Middle East) UV stabilized, 30% glass fibre reinforced Polyamide 6 injection moulding resin. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527-93 |
Wellman Wellamid® GF33-66 XE-BKDX9 33% Glass Fiber Reinforced Nylon 66 Description: Glass Fiber Reinforced Nylon 66Information provided by Wellman. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527-1/-2 |
DSM Akulon® K224-G0 (Cond.) 50% Glass Reinforced Nylon 6 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527-1/-2 |
DSM Akulon® Ultraflow™ K-FHG0 Nylon 6-50% Glass Reinforced (European Grade) (Cond) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® FE270050 BK099 Nylon 66
(Unverified Data**) 30% Glass/Mineral Reinforced Polyamide 66Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Minlon® EFE6053 BK413 Nylon 66
(Unverified Data**) 40% Mineral/Glass Reinforced Polyamide 66 Minlon EFE6053 BK413 is a 40% mineral/glass reinforced heat stabilized polyamide 66 resin for injection molding.Information provided by DuPont Performance P.. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | 5 [mm/min]; ISO 527-1/2 |
Akro-Plastic Akromid® A3 GF 40 (1258) PA 6.6 Conditioned, 40% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat.. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | 5 [mm/min]; ISO 527-1/2 |
Akro-Plastic Akromid® B3 GF 25 (2471) PA 6 Dry, 25% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur.. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RF0069XZ PA 66 LNP THERMOCOMP* RF0069XZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant. |
|||
Tensile Strength at Break | 160 MPa | 23200 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® LBV-50H FWA black 9225 PA12-GF50 Product Description: Grilamid LBV-50H FWA black 9225 is a 50% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: High stiffness combine.. |