Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527 |
Nilit FRIANYL B63 TF-GV 1530 Nylon 6 for injection molding, 15% PTFE lubricated, 30% glass fiber reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | <= 150 MPa | <= 21800 psi | ISO/R527 |
Polykemi AB SCANAMID 66 A12^ F20 FR6 Nylon 66, Glass Fiber Reinforced, Flame Retardant Information provided by Polykemi AB |
|||
Tensile Strength at Break | >= 150 MPa | >= 21800 psi | 50 mm/min; ISO 527-1,2 |
Qualchem Danamid AFGFH-30 Polyamide 66, 30% Glass Fiber Reinforced with glass fiber. Heat stabilized, for long-lasting use at 120-140°C.Information provided by Qualchem Zrt. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ASTM D638 |
LNP Thermocomp® LF-1004 Polyetheretherketone, Glass Fiber Reinforcement
(discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names.. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ASTM D683 |
Loxim 330 01V0 Nylon 6 Information provided by Loxim Industries |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527 |
Grupo Repol Dinalon® B1X25 G30V0 PA6 30% Glass Fiber, V0 Red Phosphorus and Halogen Free Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527-1/-2 |
Lanxess Durethan® DP BKV 240 H2.0 901510 Copolyamide, 40% Glass Fiber CoPA, injection molding grade, 40% glass fibers reinforced, elastomer-modified, good heat-ageing resistance |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527-1/-2 |
Lanxess Durethan® DP 2131/20 W1 901317 Nylon 6, 20% Glass Fiber PA 6, injection molding grade, 20% glass fibers, better surface finish and resistance to alcoholic calcium chloride-solution than BKV 20 H2.0, weather resistance, good heat-ageing resistance |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | Conditioned; ISO 527-1/-2 |
Lanxess Durethan® DP BKV 60 H2.0 EF 900116 Nylon 6, 60% Glass Fiber PA 6, injection molding grade, 60% glass fibers, low viscosity, good flowability (Easy Flow), good heat-resistanceApplication Examples: gearbox housings, spring holders, automotive door handles |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527-1/-2 |
Lanxess Pocan® B 3235 901510 PBT, 30% Glass Fiber PBT, 30% glass fibers, injection molding |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527 |
Solvay TECHNYL® A 718 V30 PA66, 30% glass fiber, DRY Description: TECHNYL A 718 V30 is a polyamide 66 reinforced with glass fiber and thermal stabilized for injection moldingColors: it is sailed on natural and black colorAvailable in: Latin AmericaMai.. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP IF007 PA 6/12 (Asia Pacific) LNP* THERMOCOMP* IF007 is a compound based on Nylon 6/12 resin containing Glass Fiber. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP QF0069 PA6.10 LNP* THERMOCOMP* QF0069 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOTUF PF00AIS PA 6 (Asia Pacific) LNP* THERMOTUF* PF00AIS is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 218 V35 Black 34 NG PA66, 35% glass fiber, Conditioned Description: TECHNYL® A 218 V35 Black 34 NG is a polyamide 66, reinforced with 35% of glass fiber, heat stabilized, for injection molding. The product is available in black color.Benefits: This p.. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527-1/-2 |
DSM Stanyl® 46HF5041LW Nylon 46-40% Glass Reinforced (European and Asian Grade) (Dry) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | 5 mm/min; ISO 527 |
CP-Polymer-Technik Wellamid® 6000 GVZ 45 HWCP 45% Glass Fiber Nylon 6, Impact Resistant, Good Surface Finish, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® TSG-30/4 V0 PA666-GF30 FR Product description: Grilon TSG-30/4 V0 is a heat stabilized, flame retardant, self-extinguishing engineering thermoplastic, reinforced with glass-fiber 30% (by weight) based on a semi-crystalline P.. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® TSG-50 PA666-GF50 Product description: Grilon TSG-50 is a heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 50% glass fibers. Grilon TSG-50 has the following important properties: High stiffne.. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527 |
Eurotec® Tecomid® NA40 KG30 NL 0B PA6.6, 30% glass fiber/glass bead reinforced, natural Information provided by Eurotec® |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® LC-3H black PA12-CF30 Product description: Grilamid LC-3H BLACK is a Polyamide 12 injection molding product reinforced with 30 % carbon fibers. The product is inherently black and is only available in this color.Main Att.. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | 5 mm/min; ISO 527 |
Eurostar Starflam PF0069 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded Starflam PF0069 is a Flame Retardant, Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | 0.2 in/min; ASTM Test |
BASF Petra® 7030 GY6128 30% Glass Filled PET Petra 7030 GY6128 is a grey pigmented, high flow 30% glass fiber reinforced injection molding compound based on post-consumer and post-industrial recycled polyethylene terephthalate feedstock. It o.. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527-1/-2 |
BASF Ultramid® S3WG6 Balance 30% Glass Filled PA 610 (Dry) Description: BASF supplies polyamide 610 for processing by injection molding under the trade name Ultramid® Balance which is produced by polycondensation of hexamethylene diamine and sebacic acid. .. |
|||
Tensile Strength at Break | 150 MPa @Temperature 20.0 °C |
21800 psi @Temperature 68.0 °F |
|
BASF Ultrason E 2010 G6 30% Glass Filled PES Ultrason E 2010 G6 is a 30% glass reinforced, medium viscosity injection molding PES grade with high rigidity and strength. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® LM70G35HSLX BK314 Nylon 66
(Unverified Data**) 35% Glass Reinforced Heat Stabilized Laser Markable Polyamide 66 Zytel LM70G35HSLX is a 35% glass fiber reinforced heat stabilized lubricated polyamide 66 for injection molding. It is well suited fo.. |
|||
Tensile Strength at Break | 150 MPa @Temperature 23.0 °C |
21800 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Rynite® 530 BK503 PET
(Unverified Data**) Rynite® 530 BK503 is a 30% glass reinforced modified polyethylene terephthalate with outstanding balance of strength, stiffness, and toughness, excellent electrical properties, surface appearance, .. |