Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	138 MPa	20000 psi	ASTM D638
PolyOne Trilliant™ HC HC6600-0010 ESD Black Polyamide 66 (Nylon 66) Information provided by PolyOne
Tensile Strength at Break	138 MPa	20000 psi	ASTM D638
Polymer Resources NY66-IMG33 Nylon, 33% Glass Reinforced, Impact Modified (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide..
Tensile Strength at Break	137.9 MPa	20000 psi	ASTM D638
Ensinger ENSILON® 6/6 GF30 Extruded Nylon 6/6, 30% glass-fiber-reinforced (PA66) (discontinued **) ENSILON 6/6 GF30 is a 30% glass-fiber-reinforced nylon 6/6 material whose important properties include high tensile and flexural strength, stiffness, excellent heat deflection, and superior abrasion..
Tensile Strength at Break	138 MPa	20000 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RFL36XXZ PA 66 (Asia Pacific) LNP Lubricomp is a compound based on PA66 resin containing glass fiber, PTFE. It is an internally lubricated compound that provide excellent chemical resistance, strength and wear/friction propertie..
Tensile Strength at Break	138 MPa	20000 psi	ASTM D638
Techmer ES PlaslubeÂ® J-4/35/TF/15 NAT PA6/12
Tensile Strength at Break	138 MPa	20000 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RFB66 PA 66 LNP* THERMOCOMP* RFB66 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 30% Glass Bead.
Tensile Strength at Break	138 MPa	20000 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP XF006S PA LNP* THERMOCOMP* XF006S is a compound based on Amorphous Nylon containing 30% Glass Fiber. Added feature of th is grade is: Heat Stabilized.
Tensile Strength at Break	138 MPa @Temperature 23.0 °C	20000 psi @Temperature 73.4 °F	DAM; ISO 527
DuPont Performance Polymers Zytel® PLUS PLSFR95G15DH2 BK269 Nylon (Unverified Data**) Zytel® PLSFR95G15DH2 BK269 is 15% glass reinforced, flame retardant black PA using SHIELD Technology, only from DuPont, exceptional resistance in hot air & hot engine oil.Information provided by Du..
Tensile Strength at Break	138 MPa	20000 psi	5 mm/min; ISO 527
Eurostar Staramide BG6ST01 PA6, Glass Fiber Filled, Impact Modified, Injection Molded Staramide BG6ST01 is an Impact Modified and Glass Fiber Reinforced, Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
Tensile Strength at Break	138 MPa	20000 psi	ASTM D638
Polymer Resources PEI-G20 Polyetherimide, 20% Glass Reinforced (Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.