Polymer Property : Tensile Strength at Break = 16500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	114 MPa	16500 psi	ASTM D638
Polymer Resources PPX/NY G20 PPO/Nylon 66 Alloy , 20% Glass Reinforced Polyphenylene Oxide/Nylon 66 Alloy , 20% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informa..
Tensile Strength at Break	114 MPa	16500 psi	ASTM D638
Ravago Manufacturing Americas Hylon® N1240MGHL BK Nylon 6/6 Available in North America Filler: Glass Fiber Reinforcement -15% Filler by Weight, Mineral -25% Filler by WeightAdditive: Heat Stabilizer and Lubricant Features: Lubricated, Low Warpage and Heat S..
Tensile Strength at Break	114 MPa	16500 psi	Type I, 5.1 mm/min; ASTM D638
PolyOne Edgetek® PC-15CF/000 FCR Polycarbonate (PC) The Edgetek™ Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for ..
Tensile Strength at Break	114 MPa @Temperature 23.0 °C	16500 psi @Temperature 73.4 °F	ISO 527
DuPont Performance Polymers Crastin® SK645FR BK851 PBT (Unverified Data**) Crastin® SK645FR BK851 is a flame retardant , 30% glass reinforced black polybutylene terephthalate molding resin. It is recognized as UL94V-0 at 0.75mm.Information provided by DuPont Performance P..
Tensile Strength at Break	114 MPa	16500 psi	ISO 527
Nilit FRIANYL B63 HS-GV25 Nylon 6 for injection molding, 25% glass fiber reinforced Nylon 6 for injection molding, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	114 MPa	16500 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL36HL PC (Asia Pacific) LNP* LUBRICOMP* DFL36HL is a compound based on Polycarbonate resin containing PTFE, Glass Fiber. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	114 MPa	16500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Noryl PX7446 PPE+PS This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	114 MPa	16500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RFI12 PA 66 LNP* LUBRICOMP* RFI12 is a compound based on Nylon 66 resin containing 10% Glass Fiber, 2% Silicone. Added feature of this material is: Wear Resistant.
Tensile Strength at Break	114 MPa	16500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® V4860HR PBT 30% glass reinforced PBT, UL94 V-0 rated, Hydrolytically stable, Impact Modified.
Tensile Strength at Break	114 MPa	16500 psi	ASTM D 638
SABIC Innovative Plastics LNP Thermocomp DF0069E PC (Asia Pacific) LNP* Thermocomp* DF0069E is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.This data was supplied by SABIC..
Tensile Strength at Break	114 MPa	16500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DF006HL PC LNP THERMOCOMP* DF006HL is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Low Extractible, Healthcare.
Tensile Strength at Break	114 MPa	16500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF006LXN PC LNP* THERMOCOMP* DF006LXN is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material are: Low Extractable, NSF Listed.
Tensile Strength at Break	114 MPa	16500 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP JF004E PES (Asia Pacific) LNP* Thermocomp* JF004E is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break	114 MPa	16500 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP JF004EXP PES LNP* THERMOCOMP* JF004EXP is a compound based on Polyethersulfone resin containing 20% Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break	114 MPa	16500 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-KON DEL339XF PC (Asia Pacific) LNP* Stat-kon* DEL339XF is a compound based on Polycarbonate resin containing PTFE, Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant,..
Tensile Strength at Break	114 MPa	16500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® IQ420HP PBT Environmentally responsible, low carbon footprint Valox iQ* resin - Valox* iQ420HP resin is made using iQ-PBT resin and 30% glass fiber reinforcement. Valox* iQ420HP may be used for the production..
Tensile Strength at Break	114 MPa	16500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® V4860HR PBT (Europe-Africa-Middle East) 30% glass reinforced PBT, UL94 V-0 rated, Hydrolytically stable, Impact Modified.
Tensile Strength at Break	114 MPa	16500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF006 PC LNP* Thermocomp* DF006 is a compound based on Polycarbonate resin containing 30% Glass Fiber.
Tensile Strength at Break	114 MPa	16500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP LX97024 PEEK (Europe-Africa-Middle East) LNP* LUBRICOMP* LX97024 is a compound based on Polyetheretherketone containing Glass Fiber, PTFE. Added features include: Internally Lubricated, Easy Molding.
Tensile Strength at Break	114 MPa	16500 psi	ISO 527-1
Vyncolit A2990 Glass Fiber Reinforced Novolac Phenolic Resole resin based, glass fiber reinforced. Good mechanical properties, combined with superior electrical insulation properties. Among others used for commutator applicationsInformation provided by ..
Tensile Strength at Break	114 MPa	16500 psi	0.2 in/min; ASTM Test
BASF Ultramid® A3EG3 15% Glass Filled PA66 (Dry) Ultramid A3EG3 is a 15% glass fiber reinforced injection molding PA66 grade. It conforms to FDA requirements of 21 CFR 177.1500.