- Polymer Property : Tensile Strength at Break = 16200 psi
Polymer Property : Tensile Strength at Break = 16200 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 112 MPa | 16200 psi | ASTM D638 |
| PolyOne Stat-Tech™ PC-15CF/000 Black Polycarbonate (PC) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound.. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL36ELH PC LNP* Lubricomp* DFL36ELH is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Low Extractible, Easy Moldi.. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ISO 527-1/-2 |
| DSM Arnite® CCT GF20 (T-X01415) PBT-20% Glass Reinforced (European Grade)
(discontinued **) Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame .. |
|||
| Tensile Strength at Break | 111.7 MPa | 16200 psi | ASTM D638 |
| Covestro Petlon® 4835 Semi-Crystalline PET, 35% Mineral/Glass Fiber
(discontinued **) Characteristics: Flame Retardant: Good Processability, Low Warpage, High RigidityApplications: Appliance, Telecommunication and Electrical HousingsProcessing: Injection Molding (Melt Temperature: 49.. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ISO 527 |
| Nilit FRIANYL A63 CV-CU 0550 Nylon 6.6 for injection molding, 5% carbon fiber reinforced, 50% copper filled Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL36ELH PC (Asia Pacific) LNP* Lubricomp* DFL36ELH is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Noryl PX7446 PPE+PS This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ISO 527 Type 1A |
| Solvay TECHNYL® eXten D218 V30 Nylon 6.10, 30% glass fiber, Conditioned Description: TECHNYL® eXten D 218 V30 is a 30% Glass Fiber reinforced and heat stabilized product suitable to the manufacturing of all injection molded parts. This material is available in black... |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP RX05495 PA 66 LNP LUBRICOMP* RX05495 is a compound based on Nylon 66 resin containing Glass Bead, Graphite, Glass Fiber. Added features of this material include: Easy Molding. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics ULTEM CRS5111 PEI (Asia Pacific) 10% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 and 5 VA listing. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON DE0021E PC LNP STAT-KON* DE0021E is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Easy Molding, Flame Retardant, Electrically Conductive. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON DE0021E PC (Asia Pacific) LNP STAT-KON* DE0021E is a compound based on Polycarbonate resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Easy Molding. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® ENH4550 PBT 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® ENH4550 PBT (Asia Pacific) 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® ENH4550 PBT (Europe-Africa-Middle East) 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® K4560 PBT 30% glass reinforced PBT. Impact modified, high flow, hydrolytically stable. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® K4560 PBT (Europe-Africa-Middle East) 30% glass reinforced PBT. Impact modified, high flow, hydrolytically stable. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON ZE0039 MODIFIED POLYPHENYLENE (Asia Pacific) LNP* Stat-kon* ZE0039 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Stat-kon ZE0039 MODIFIED POYPHENYLENE LNP* Stat-kon* ZE0039 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Stat-kon ZE0039 MODIFIED POYPHENYLENE (Asia Pacific) LNP* Stat-kon* ZE0039 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON ZE0039 PPO LNP* STAT-KON* ZE0039 is a compound based on PPO resin containing 15% Carbon Fiber. Added features of this grade includes: Flame Retardant, Electrically Conductive. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP PFW53U PA 6 LNP THERMOCOMP* PFW53U is a compound based on Nylon 6 resin containing 15% Glass Fiber, 15% Wollastinite. Added features of this material include: UV Stabilized. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP PFW53U PA 6 (Asia Pacific) LNP* THERMOCOMP* PFW53U is a compound based on Nylon 6 resin containing Glass Fiber, Mineral. Added features of this material include: UV Stabilized. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics LNP Verton NV0061EV_GY7E148 PC+ABS Preliminary data for 30% long fiber single pellet non-halogen FR color filled PC/ABSThis data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP JX91198 PES LNP LUBRICOMP* JX91198 is a compound based on Polyethersulfone resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON DEL339XF PC (Asia Pacific) LNP* Stat-kon* DEL339XF is a compound based on Polycarbonate resin containing PTFE, Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant,.. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ASTM D638 |
| Unitika AXG-1500-300 Conditioned Characteristics: Glass-reinforced grades of the AX1500 resin, excellent in heat and chemical resistancesFavorable rigidity and dimensional accuracyInformation provided by Unitika Ltd. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | 50%RH; ISO 527-1/-2 |
| DuPont Performance Polymers Zytel® 80G33HS1L BK104 Nylon 66
(Unverified Data**) 33% Glass Reinforced Toughened Heat Stabilized Polyamide 66 Zytel 80G33HS1L BK104 is a 33% glass fiber reinforced heat stabilized black polyamide 66 resin with outstanding impact resistance develope.. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL369XF PC (Asia Pacific) LNP* Lubricomp* DFL369XF is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant. |
|||
| Tensile Strength at Break | 112 MPa | 16200 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL36HL PC LNP LUBRICOMP* DFL36HL is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Low Extractable, Healthcare. |
|||