Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 107 MPa | 15500 psi | ASTM D638 |
Niche Polymer PA66GF13BK Nylon 66, 13% Glass Fiber Filled Information provided by Niche Polymer |
|||
Tensile Strength at Break | 107 MPa | 15500 psi | ASTM D638 |
Niche Polymer PA66GF13N Nylon 66, 13% Glass Fiber Filled Information provided by Niche Polymer |
|||
Tensile Strength at Break | 107 MPa | 15500 psi | ASTM D638 |
Polymer Resources TP-IG30 Polybutylene Terephthalate, 30% Glass Reinforced, Reduced Warpage Polybutylene Terephthalate, 30% Glass Reinforced, Reduced WarpageProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.. |
|||
Tensile Strength at Break | 107 MPa | 15500 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Edgetek® PC-20GF/000 Polycarbonate (PC) Information provided by PolyOne |
|||
Tensile Strength at Break | 107 MPa | 15500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DCL32 PC (Europe-Africa-Middle East) LNP* LUBRICOMP* DCL32 is a compound based on Polycarbonate resin contqaining Carbon Fiber, PTFE. Added features include; Internally Lubricated, Electrically Conductive. |
|||
Tensile Strength at Break | 107 MPa | 15500 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DX05474 PC LNP* STAT-KON* DX05474 is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding, Flame Retardant, Mold .. |
|||
Tensile Strength at Break | 107 MPa | 15500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® K4560 PBT 30% glass reinforced PBT. Impact modified, high flow, hydrolytically stable. |
|||
Tensile Strength at Break | 107 MPa | 15500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DF005 PC LNP* Thermocomp* DF005 is a compound based on Polycarbonate containing 25% Glass Fiber. |
|||
Tensile Strength at Break | 107 MPa | 15500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP JF003E PES LNP* THERMOCOMP* JF003E is a compound based on Polyethersulfone resin containing 15% Glass Fiber. Added features of this material include: Easy Molding. |
|||
Tensile Strength at Break | 107 MPa | 15500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP JF004LZ PES LNP* Thermocomp* JF004LZ is a compound based on PES containing 20% Glass Fiber. Added features include: Extrusion Grade, Low Extractible. |
|||
Tensile Strength at Break | 107 MPa | 15500 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOTUF RF002I PA 66 (Asia Pacific) LNP* THERMOTUF* RF002I is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
Tensile Strength at Break | 107 MPa | 15500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP VERTON MV00ES PP LNP* VERTON* MV00ES is primarily a concentrate used for blending purposes. This is a 70% long glass fiber Polypropylene compound. Added features of this grade are: Heat Stabilized |
|||
Tensile Strength at Break | 107 MPa | 15500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH7114 PPE+HIPS (Asia Pacific) Noryl* NH7114 resin is a 20% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve UL94 flame ratings while offering an exceptional balance of streng.. |
|||
Tensile Strength at Break | 107 MPa | 15500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH7114 PPE+HIPS (Europe-Africa-Middle East) Noryl* NH7114 resin is a 20% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve UL94 flame ratings while offering an exceptional balance of streng.. |
|||
Tensile Strength at Break | 107 MPa | 15500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP Noryl_HM3020 PPE+PS LNP* Thermocomp* Noryl_HM3020 compound is a 30% Glass/Mineral filled, high modulus grade. DTUL 248F (120C). UL94 V-1/5VA rated in black and gray. |
|||
Tensile Strength at Break | 107 MPa | 15500 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP PX92248 PA 6 LNP* THERMOCOMP* PX92248 is a compound based on Nylon 6 resin containing Proprietary Filler(s). |
|||
Tensile Strength at Break | 107 MPa | 15500 psi | ASTM D638 |
Chase Plastics CP Pryme® PC120R Polycarbonate, 20% Glass Fiber Reinforced Features: Good mold releaseForm: PelletsInformation provided by Chase Plastics. |