Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 88.0 - 90.0 MPa | 12800 - 13100 psi | ISO.527 DN.53455 |
Polimersan Plastics POLIKES® (PA 6 G) Cast Polyamide POLIKES® PA6 G (CAST POLYAMIDE) is a plastic with high physical, electrical and chemical resistance. Its resistance is high especially against strokes and loads. Its temperature resistance is high.. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | ASTM D638 |
SABIC Innovative Plastics LNP KONDUIT PTF2BXXX PA 6 LNP KONDUIT* PTF2BXXX is a compound based on Nylon 6 resin containing 10% Glass Fiber, 55% Proprietary Thermal Filler. Added features of this material include: Thermally Conductive. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | ASTM D638 |
SABIC Innovative Plastics LNP KONDUIT PTF2BXXX PA 6 (Asia Pacific) LNP KONDUIT* PTF2BXXX is a compound based on Nylon 6 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DFL349 PC (Asia Pacific) LNP LUBRICOMP* DFL349 is a compound based on Polycarbonate resin containing Flame Retardant, Glass Fiber, PTFE. Added features of this material include: Flame Retardant. |
|||
Tensile Strength at Break | 88.3 MPa | 12800 psi | ASTM D638 |
Ravago Manufacturing Americas Enviramid™ N1315HL BK Post Consumer Recycle Nylon 66, 15% Glass Filled Heat Stabilized, Lubricated, Black, and made from EnViramid™ Post Consumer Recycled NylonInformation provided by Ravago. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC LNP* Lubricomp* DFL23 is a compound based on Polycarbonate resin containing 15% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU (Asia Pacific) LNP* Lubricomp* GFL36L is a compound based on Polysulfone resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer (Asia Pacific) LNP* Lubricomp* KCL34A is a compound based on Acetal Homopolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP KFL36 Acetal Copolymer LNP* LUBRICOMP* KFL36 is a compound based on Acetal Copolymer resin containing 30% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RA004 PA 66 LNP LUBRICOMP* RA004 is a compound based on Nylon 66 resin containing 20% Aramid. Added features of this material include: Wear Resistant. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM D9065 PEI Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP 2X98703 ETFE LNP* THERMOCOMP* 2X98703 is a compound based on ETFE Copolymer resin containint Proprietary Filler(s). |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | Nominal Stress, brk, Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX810 PPE+PS+PA 10% Glass Reinforced PPE+PA Alloy. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM AUT210 PEI Transparent, Thermoplastic Polyimide (TPI). Glass transition Temperature (Tg) of 227degC. Haze onset temperature of 212degC (SABIC IP method). Very low outgassing and plateout, for automotive lighti.. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM AUT210 PEI (Europe-Africa-Middle East) Transparent Polyetherimide (Tg 227 degC). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature o.. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS LNP* THERMOCOMP* ZF0049 is a compound based on PPE+PS resin containing 20% Glass Fiber. Added feature of this material is: Flame Retardant. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX4610 PPE+PA Noryl GTX* GTX4610 resin is a high performance, 10% glass filled blend of PPE/PA that exhibits an excellent balance of non-halogenated flame retardance, dimensional stability, high heat resistance, .. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX4610 PPE+PA (Europe-Africa-Middle East) Noryl GTX* GTX4610 resin is a high performance, 10% glass filled blend of PPE/PA that exhibits an excellent balance of non-halogenated flame retardance, dimensional stability, high heat resistance, .. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX810 PPE+PS+PA (Asia Pacific) GR 10%. Increased stiffness of 200000 psi (3000 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: lighting. |
|||
Tensile Strength at Break | 88.3 MPa | 12800 psi | |
Master Bond EP45HTAO Heat Resistant Epoxy for Structural Bonding Description: Master Bond Polymer Compound EP45HTAO is a two component thermally conductive epoxy compound for high performance structural bonding, and casting. It is suitable for applications where .. |
|||
Tensile Strength at Break | 88.3 MPa | 12800 psi | ASTM D638 |
Plastics Group Polifil® 71MR Mineral-Reinforced Nylon 6/6 (DAM) Polifil® GFN/MRN 6/6 reinforced series of compounds offer superior strength, rigidity and creep resistance. Glass fibers provide excellent thermal and dimensional stability while maintaining good h.. |
|||
Tensile Strength at Break | 88.3 MPa | 12800 psi | ASTM D638 |
PlastxWorld CEVIAN®-N GRSJ1 10% GF SAN resin Glass fiber reinforced SAN resin. These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
Tensile Strength at Break | 88.0 - 90.0 MPa | 12800 - 13100 psi | DIN 53455 |
Zell-Metall Engineering Plastics Zellamid 1100 Zellamid® 1100 is the registered trademark for Zell-Metalls cast nylon 6 in different qualities.Our standard quality is a heavy duty, high impact, wear and heat resistant polyamide. It offers .. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | ASTM D638 |
Unitika M2350 PA6, Dry Nano composite nylonInformation provided by Unitika Ltd. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | 5 mm/min; ISO 527 |
Eurostar Starflam A28UL PA66, Flame Retardant, Injection Molding Staramide A28UL is Unfilled, Halogen Free and Red Phosphorous Free, Flame Retardant Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength at Break | 88.0 MPa | 12800 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP 2X04505 ETFE LNP* THERMOCOMP* 2X04505 is a compound based on ETFE resin containing Proprietary Filler(s). |