Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
SABIC MG500026 Linear Low Density Polyethylene for Compounding Product Description: MG500026 is a Linear Low Density Polyethylene grade with a narrow molecular weight distribution primarily suitable for compounding applications. It is in the powder form and h.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | |
ExxonMobil LL 5202.09 Compounding Resin
(discontinued **) LL 5202.09 is a linear low density polyethylene resin designed to provide good processability and ease of blending. The granular form of LL 5202.09 makes for efficient blending with pigments, slip .. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ISO 527 |
SABIC Innovative Plastics LNP Lubricomp FX00617 PE (Asia Pacific) LNP* Lubricomp* FX00617 is a compound based on Polyethylene resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP PDXF89080 PE LNP* LUBRICOMP* PDXF89080 is a compound based on Polyethylene containing Proprietary Fillers. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength at Break | >= 8.00 MPa | >= 1160 psi | |
Silikony Polskie Polsil Gum 100/50 HTV Silicone Rubber Polsil Gum is a general purpose master batch compound, vulcanizing at high temperature after addition of vulcanizing agent. Silicone rubber obtained from Polsil® GUM shows useful properties: agei.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP ZF0089 PPE+PS LNP* THERMOCOMP* ZF0089 is a compound based on PPE+PS resin containing 40% Glass Fiber. Added features of this material include: Exceptional Processing, Flame Retardant. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | 500mm/min; ASTM D638 Type IV Specimen |
Westlake EM182AA Low Density Polyethylene WESTLAKE low-density polyethylene EM182 is a low density formulation used for injection molding. It is an outstanding material for molding lids and other container closures because it processes easi.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ISO 527-2 |
Total LDPE 1200 MN 18 C Low Density Polyethylene - Injection Molding and Compounding LDPE 1200 MN 18 C is a low density polyethylene made by a high pressure autoclave process without antioxidant.Application examples: flexible molding, handles, closures, household items, toys, variou.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
ELASTO UK Dryflex® 660700S SEBS Based Material, Semi-Filled Qualities, 70A Hardness, Natural The 660-series is recommended when the properties of the produced detail requires the advantages of the 500-series in combination with the 600-series. A semi-filled material can therefore combine t.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
ELASTO UK Mediprene™ 660440M TPE, Medical Applications, 44A Hardness All Mediprene™ compounds are designed and manufactured for use in medical and pharmaceutical applications. In both medical and food contact areas, high application demands are found, such as:Low e.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ISO R 527 |
Fainplast Compounds GS 58 Flexible PVC, Injection Molding for Footwear Antislip soles |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ISO R 527 |
Fainplast Compounds GS 60/B Flexible PVC, Injection Molding for Footwear Bicoloured soles |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ISO R 527 |
Fainplast Compounds GS 60/R1 Flexible PVC, Injection Molding for Footwear Anti-accident soles |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ISO R 527 |
Fainplast Compounds GS 6520 Flexible PVC, Injection Molding for Footwear Soles |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ISO R 527 |
Fainplast Compounds PH 50/AM-UV Flexible PVC, Transparent Extrusion Gaskets anti mould and anti-UV |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ISO R 527 |
Fainplast Compounds PM 5580 Flexible PVC, Lead Free Gaskets for frames |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
Aclo Accucomp Polyethylene LD0109L Low Density |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
Azdel SuperLite® SL552000-100 PP Resin Matrix / 55% Glass Fiber (10 mm Molded Thickness) AZDEL SuperLite® SL552000-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 8.02 MPa | 1160 psi | Longitudinal; ASTM D3759 |
3M Highland™ 3565 Label Protection Tape 3M™ Highland™ Label Protection Tape 3565 has a clear, strong, moisture-resistant film backing and a strong adhesive that holds well to many treated and finished surfaces. It is used for the attach.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
Arkema Group LOTADER® 8200 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride LOTADER 8200 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized under high pressure in an autoclave process. Due to its properties (reactivity, fluidity), LOTADER 82.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM-D638 |
Braskem IP2418 LDPE Injection Molding Polyethylene IP2418 is a low-density polyethylene with good processability and high fluidity, flexibility, and mechanical strength. It does not contain additives. Its applications include injection molding and b.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | 500mm/min; ASTM D638 Type IV Specimen |
Westlake EMAC® SP2403 24% Ethylene-Methyl Acrylate Copolymer Westlake EMAC® SP2403 is a 24% EMA copolymer designed for extrusion coating, tie-layers, compounding, and extrusions where flexibility, compatibility, low heat seal temperatures, or high coefficien.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | |
LATI Latimass 53/11-02 D030 PP Homopolymer, Impact Modified Specific density compound based on Polypropylene homopolymer (PPh), impact modified. Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation.. |