Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 73.8 MPa | 10700 psi | 2 in/min; ASTM D638 |
RheTech Products FRG130-01 30% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Flame Retardant, Black Applications: Electrical component housingsSunroof componentsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycolac® INP562 ABS+SAN SABIC INP562 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pellet.. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® INP563 ABS SABIC INP563 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pellet.. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® INP563 ABS+SAN SABIC INP563 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pellet.. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM XH1015 TPI Resin Thermoplastic Polyimide Extem* XH1015 Resin. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM XH1015 TPI Resin (Asia Pacific) Thermoplastic Polyimide Extem* XH1015 Resin. |
|||
Tensile Strength at Break | <= 74.0 MPa | <= 10700 psi | ISO/R527 |
Polykemi AB SCANMID 6 B12^ NH6 Nylon 6, Flame Retardant, Halogen Free Information provided by Polykemi AB |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HPS4 PC (Europe-Africa-Middle East) Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI).EtO, steam, e-beam, and gamma sterilizable... |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP 9X06483 PA 46 LNP* Lubricomp* 9X06483 is a compound based on a Nylon 4/6 containing PTFE. Added feature of this grade is: Heat Stabilized. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | ASTM D638 |
LG Chemical EG920 PMMA, General Purpose Grade for Extrusion General purpose grade with excellent stress cracking resistanceIntended mainly for exterior applicationsRecommended mainly for sheets, pipes, and profilesFeatures: Excellent transparency and eleganc.. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | ASTM D638 |
Kotec Carbotex KG-10MRA Polycarbonate, 10% Glass Fiber Reinforced Features: Glass fiber 10% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E .. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | ASTM D638 |
Kotec Carbotex KGN-10MRA Polycarbonate, Flame Retardant, 10% Glass Fiber Reinforced Features: Glass fiber 10% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E .. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | 50 mm/min; ISO 527-1,-2 |
Ineos ABS Lustran® ABS 150G10 10% Glass Fiber Reinforced Grade |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP Noryl_NF1520 PPE+PS LNP* Lubricomp* Noryl_NF1520 compound is a 20% glass reinforced, 15% PTFE. Wear resistant; 211F HDT @ 264 psi. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RL002 PA 66 (Europe-Africa-Middle East) LNP* Verton* RL002 is a compound based on Nylon 66 resin containing PTFE. |
|||
Tensile Strength at Break | 73.8 MPa | 10700 psi | ASTM D638 |
Techmer ES Elastoblend® PA6 IM 407 L Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impact Modified and LubricatedInformation provided by TP Composites, Inc. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP UAL22S PPA LNP* LUBRICOMP* UAL22S is a compound based on Polyphthalamide resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON RFD02 PA 66 LNP* STAT-KON* RFD02 is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP AX04518 ABS LNP* THERMOCOMP* AX04518 is a compound based on ABS resin containing proprietary filler(s). |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DF002 PC LNP THERMOCOMP* DF002 is a compound based on Polycarbonate resin containing 10% Glass Fiber. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP IB008 PA 6/12 (Europe-Africa-Middle East) LNP* Thermocomp* IB008 is a compound based on Nylon 6/12 resin containing Glass Bead. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON 9X06519 Cyclic Olefinic Copolymer LNP STAT-KON* 9X06519 is a compound based on Cyclic Olefinic Copolymer resin containing 30% Carbon Fiber. Added features of this material include: Clean Compounding System, Electrically Conductive... |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON 9X06519 Cyclic Olefinic Copolymer (Asia Pacific) LNP STAT-KON* 9X06519 is a compound based on Cyclic Olefinic Copolymer resin containing Carbon Fiber. Added features of this material include: Clean Compounding System. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 9085 PEI Blend (Asia Pacific) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 9085 PEI Blend (Europe-Africa-Middle East) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 55/55 with low toxicity, smoke and flame evolution. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | ISO 527 |
SABIC Innovative Plastics LNP Thermocomp IF002 PA 6/12 LNP* Thermocomp* IF002 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | ISO 527 |
Eurostar Staramide 6 80E7 PA6, Injection Molded Staramide 6 80E7 is a high density, Polyamide 6, Injection Molding Resin (also known as 680E7)Information provided by Eurostar. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | ISO 527 - 1 & - 2 |
Asahi Kasei Tenac® 7054 Homopolymer Acetal Resin High-flow grade with high crystallization rate for higher productivity.Information provided by Asahi Kasei Corporation. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527-2 |
BASF Ultrason® P 3010 PPSU Unreinforced Polyphenylsulfone Description: Medium viscosity injection-molding and extrusion grade with good toughness and chemical resistance (stress crack resistance), resistant against superheated steam. The property profile m.. |
|||
Tensile Strength at Break | 74.0 MPa | 10700 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DFL329 PC LNP LUBRICOMP* DFL329 is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated. |