Polymer Property : Tensile Strength at Break = 84.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	<= 84.0 MPa	<= 12200 psi	ISO/R527
Polykemi AB POLYfill PPH GF5020 HC Polypropylene Homopolymer, Glass Fiber Reinforced Information provided by Polykemi AB
Tensile Strength at Break	84.0 MPa	12200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP KFL36 Acetal Copolymer LNP* LUBRICOMP* KFL36 is a compound based on Acetal Copolymer resin containing 30% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.
Tensile Strength at Break	84.0 MPa	12200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP KFL36 Acetal Copolymer (Asia Pacific) LNP* Lubricomp* KFL36 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	84.0 MPa	12200 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RN001S PA 66 LNP* LUBRICOMP* RN001S is a compound based on Nylon 66 resin containing 2% MOS2. Added features of this material include: Wear Resistant, Heat Stabilized.
Tensile Strength at Break	84.0 MPa	12200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Ultem HFATX200 PEI+PCE High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	84.0 MPa	12200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® VIC4311 PBT VALOX VIC4311 is a 30% glass filled, impact modified PBT with excellent epoxy adhesion. Automotive underhood applications such as ignition coil housings.
Tensile Strength at Break	84.0 MPa	12200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® VIC4311 PBT VALOX VIC4311 is a 30% glass filled, impact modified PBT with excellent epoxy adhesion. Automotive underhood applications such as ignition coil housings.
Tensile Strength at Break	84.0 MPa	12200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics XenoyÂ® 1760 PBT+PC 11% Glass Reinforced PBT+PC alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors.
Tensile Strength at Break	84.0 MPa	12200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics XenoyÂ® 1760E PBT+PC 11% Glass Reinforced alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors. High flow version of Xenoy 1760 resin.
Tensile Strength at Break	84.0 MPa	12200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics XenoyÂ® 1760E PBT+PC 11% Glass Reinforced alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors. High flow version of Xenoy 1760 resin.
Tensile Strength at Break	84.0 MPa	12200 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP 5C004 FP-V (PVDF) LNP* THERMOCOMP* 5C004 is a compound based on Polyvinylidene Fluoride resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break	84.0 MPa	12200 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF002ERJ PC LNP THERMOCOMP* DF002ERJ is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Healthcare.
Tensile Strength at Break	84.0 MPa	12200 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DX06408 PC LNP THERMOCOMP* DX06408 is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
Tensile Strength at Break	84.0 MPa	12200 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DX06409 PC LNP* THERMOCOMP* DX06409 is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Healthcare.
Tensile Strength at Break	84.0 MPa	12200 psi	ISO 527
SABIC Innovative Plastics LNP Thermocomp OF004AER PPS LNP* Thermocomp* OF004AER is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.This data was supplied by SA..
Tensile Strength at Break	84.0 MPa	12200 psi	ISO 527
SABIC Innovative Plastics LNP Thermocomp OF004AER PPS (Asia Pacific) LNP* Thermocomp* OF004AER is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.This data was supplied by SA..
Tensile Strength at Break	84.0 MPa	12200 psi	ASTM D 638
SABIC Innovative Plastics LNP Thermocomp P1000P PA 6 (Asia Pacific) LNP* Thermocomp* P1000P is a compound based on Nylon 6 resin. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break	84.0 MPa	12200 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific) LNP* Thermocomp* ZF0049 is a compound based on PPE+PS Blend resin containing Flame Retardant. Added features of this material include: Flame Retardant.
Tensile Strength at Break	84.0 MPa	12200 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP XFL21R PA LNP* LUBRICOMP* XFL21R is a compound based on Amorphous Nylon resin containing 5% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Mold Release.
Tensile Strength at Break	84.0 MPa	12200 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF002ER PC LNP THERMOCOMP* DF002ER is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Easy Molding. Mold Release
Tensile Strength at Break	84.0 MPa	12200 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP KF002XXP Acetal Copoly LNP* Thermocomp* KF002XXP is a compound based on Acetal Copolymer resin containing 10% Glass Fiber. Added features of this material include: Chemically Coupled.
Tensile Strength at Break	84.0 MPa	12200 psi	ASTM D 638
SABIC Innovative Plastics LNP Thermocomp P1000P PA 6 LNP* Thermocomp* P1000P is a compound based on Nylon 6 resin. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	84.0 MPa	12200 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS LNP* THERMOCOMP* ZF0049 is a compound based on PPE+PS resin containing 20% Glass Fiber. Added feature of this material is: Flame Retardant.
Tensile Strength at Break	84.0 MPa	12200 psi	ASTM D 638
SABIC Innovative Plastics LNP Thermotuf VFM53 PA 66 LNP THERMOTUF* VFM53 is a compound based on Nylon resin containing Glass Fiber, Mineral. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas..
Tensile Strength at Break	84.0 MPa	12200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GFN1410V PPE+PS (Europe-Africa-Middle East) Noryl* GFN1410V resin is a blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 10 % glass reinforcement. The resin is suitable for injection molding. Noryl GFN1410V resin has..
Tensile Strength at Break	84.0 MPa	12200 psi	DIN EN ISO 527
Wolf Kunststoff ZEDEX® ZX-324 A3A PEEK Main Characteristics: Hard; Stiff; Tough; High fatigue strength; Good water resistance; Sufficient UV and weather resistance; Flame retardant; Good machinability; FDA compliant LABS; PTFE and Silico..
Tensile Strength at Break	84.0 MPa	12200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON KX97157 Acetal Copolymer (Europe-Africa-Middle East) LNP* STATKON* KX97157 is a compound based on Acetal resin containing Carbon. Added features include : Electrically Conductive, Impact Modified.
Tensile Strength at Break	84.0 MPa	12200 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DX06409 PC (Asia Pacific) LNP* Thermocomp* DX06409 is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.