Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
Polymer Resources NY66-GP1 General Purpose Nylon 66 General Purpose Nylon 66, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry.. |
|||
Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
Polymer Resources NY66-MD-[color]-H Nylon 66, 2% MoS2 Nylon 66, 2% Molybdenum Disulfide for Lubrication and Wear, Heat StabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, te.. |
|||
Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
Polymer Resources NY66-MD02 Nylon, 2% Molybdenum disulfide for lubrication and wear (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
Ravago Manufacturing Americas Hylon® N1013HL Nylon 6/6 (Cond) Information provided by Ravago |
|||
Tensile Strength at Break | 82.7 MPa | 12000 psi | 5.1 mm/min; ASTM D638 |
PolyOne Edgetek® NL-10GF/000 BLACK Polyamide 612 (Nylon 612) The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for .. |
|||
Tensile Strength at Break | 82.7 MPa | 12000 psi | 5.1 mm/min; ASTM D638 |
PolyOne Edgetek® X PS-154200101 WHITE Polybutylene Terephthalate (PBT) Information provided by PolyOne |
|||
Tensile Strength at Break | 82.7 MPa | 12000 psi | 2 in/min; ASTM D638 |
RheTech Products G30P100-00 30% Glass Fiber Reinforced Polypropylene, Natural Applications: Fender apronsUnderhood componentsStructural componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
Polymer Resources NY66-MD02-[color]-H Nylon, 2% Molybdenum disulfide for lubrication and wear, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
Polymer Resources NY66-MD2 Nylon 66, 2% MoS2 Nylon 66, 2% Molybdenum Disulfide for Lubrication and WearProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon.. |
|||
Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
Ravago Manufacturing Americas Hylon® N1000EL Nylon 6/6 (DAM)
(discontinued **) Information provided by Ravago |
|||
Tensile Strength at Break | >= 82.7 MPa | >= 12000 psi | |
Master Bond EP45HTND-2 Chemically Resistant, Non-Drip Epoxy Description: Master Bond EP45HTND-2 is a two component epoxy system for high performance bonding, sealing and coating. It is used for applications requiring solid temperature resistance and capable .. |
|||
Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
Chase Plastics CP Pryme® N100HL (Dry) Nylon 6, Heat Stabilized, Lubricated Features: Heat stabilizedLubricatedForm: PelletsInformation provided by Chase Plastics. |
|||
Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
A. Schulman SCHULAMID® 66 MF40 Mineral Filled Nylon 66 Information provided by A. Schulman. |
|||
Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
Plastics Group Polifil® 82MR Mineral-Reinforced Nylon 6 (DAM) Polifil® GFN/MRN 6 reinforced series of compounds provide good heat and dimensional stability and offer extended or continuous stability under high temperatures. These have been found useful in ind.. |
|||
Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
A. Schulman SCHULAMID® 66 MF40 Mineral Filled Nylon 66 Information provided by A. Schulman. |
|||
Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
A. Schulman SCHULAMID® 66 MF40 Mineral Filled Nylon 66 Information provided by A. Schulman. |