Polymer Property : Tensile Strength at Break = 82.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	82.0 MPa	11900 psi	ASTM D638
Niche Polymer PPCG40BK Copolymer PP, 40% Glass Fiber Filled Information provided by Niche Polymer
Tensile Strength at Break	<= 82.0 MPa	<= 11900 psi	ISO/R527
Polykemi AB SCANMID 6 B11^ FC Nylon 6 Information provided by Polykemi AB
Tensile Strength at Break	82.0 MPa	11900 psi	STN EN ISO 527-2
Plastcom SLOVAMID 6 BT LS Polyamide 6, UV Stabilized FeaturesPA 6 for injection moulding with the content of UV stabilizer predetermines products for external use, eg. seats for sport stadiums, covers of electrical appliances. Delivered in natural an..
Tensile Strength at Break	82.0 MPa	11900 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI (Asia Pacific) LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	82.0 MPa	11900 psi	ASTM D 638
SABIC Innovative Plastics LNP Lubricomp KFL22 Acetal Copolymer LNP* Lubricomp* KFL22 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP f..
Tensile Strength at Break	82.0 MPa	11900 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 4000 PEI Glass fiber, PTFE, and Graphite filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 listing.
Tensile Strength at Break	82.0 MPa	11900 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem HFATX200 PEI+PCE High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	82.0 MPa	11900 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem HFATX200 PEI+PCE (Asia Pacific) High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break	82.0 MPa	11900 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem HFATX200 PEI+PCE (Europe-Africa-Middle East) High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength at Break	82.0 MPa	11900 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem HTX1010F PEI (Asia Pacific) Higher impact, Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break	82.0 MPa	11900 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® 4012 PBT (Europe-Africa-Middle East) VALOX 4012 is a 10% high strength glass fibre reinforced PBT injection moulding resin with improved mechanical properties. Applications: connectors.
Tensile Strength at Break	82.0 MPa	11900 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® K4530 PBT (Europe-Africa-Middle East) 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors.
Tensile Strength at Break	82.0 MPa	11900 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP AF006 ABS (Europe-Africa-Middle East) LNP* Thermocomp* AF006 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber.
Tensile Strength at Break	82.0 MPa	11900 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP AF006XXZ ABS (Europe-Africa-Middle East) LNP* Thermocomp* AF006XXZ is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber.
Tensile Strength at Break	82.0 MPa	11900 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DX06411 PC LNP* THERMOCOMP* DX06411 is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Healthcare.
Tensile Strength at Break	82.0 MPa	11900 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DX06411 PC (Asia Pacific) LNP* Thermocomp* DX06411 is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
Tensile Strength at Break	82.0 MPa	11900 psi	ASTM D 638
SABIC Innovative Plastics LNP Thermocomp RFZ71S PA 66 (Asia Pacific) LNP* Thermocomp* RFZ71S is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for t..
Tensile Strength at Break	82.0 MPa	11900 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-LOY PF303 PA 6 (Asia Pacific) LNP* Stat-loy* PF303 is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Antistat.
Tensile Strength at Break	82.0 MPa	11900 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL GTX GTX8408 PPE+PA Noryl GTX* GTX8408 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is glass filled and suitable for injection molding. The elongation of this material is higher than GTX8410W..
Tensile Strength at Break	82.0 MPa	11900 psi	DIN EN ISO 527
Wolf Kunststoff ZEDEX® ZX-410 A4A Polymer Alloy ZX-410 is a bearing material with excellent properties and a very affordable price.Main Characteristics: Hard, Stiff, Tough; High dimensional stability; High chemical resistance; High water resistan..
Tensile Strength at Break	82.0 MPa	11900 psi	ASTM D638
Toyobo T-661 Nylon 66, Standard Grade (DAM) Features: Non-reinforced, Standard GradeInformation provided by Toyobo.
Tensile Strength at Break	82.0 MPa	11900 psi	ISO 527
Ecomass® 4301TU74 Tungsten Filled Polyphthalamide Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applicationsTungsten Powder Filled Polyphthalamide (PPA)Very Good ToughnessInformation provided by Technical Polymers
Tensile Strength at Break	82.0 MPa	11900 psi	5 mm/min; ISO 527
CP-Polymer-Technik Wellamid® 6000 GS 40 HWCP 40% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Strength at Break	82.0 MPa	11900 psi	ASTM D 638
Cossa Polimeri ESTASAN SAN 0840 GF Styrene Acrylonitrile SAN with 20% glass fiber reinforcementExcellent dimensional stability, good heat resistanceInformation provided by Cossa Polimeri S.r.l.
Tensile Strength at Break	82.0 MPa	11900 psi	ISO 527
Eurostar Starflam PZ0052E PA6, 25% Glass Filled, Injection Molded PZ0052E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding (also known as PF1005Z222 or PA625GFUZ22)Information provided by Polymer Technolo..
Tensile Strength at Break	82.0 MPa @Temperature 80.0 °C	11900 psi @Temperature 176 °F	ISO Data
BASF Petra® 330 FR BK-112 30% Glass Filled PET Petra 330 FR BK-112 is a 30% glass reinforced, flame retardant PET, pigmented black injection molding compound rated UL94 V-0 in a 1/64 inch thickness. The product is designed for injection molding..
Tensile Strength at Break	82.0 MPa	11900 psi	ISO R 527
Addiplast Addilene H 511 V30 Polypropylene Homopolymer Glass fiber reinforced, high modulus and improved stiffnessInformation provided by Addiplast.
Tensile Strength at Break	82.0 MPa	11900 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOTUF PX06416 PA 6 (Asia Pacific) LNP* Thermotuf* PX06416 is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: High Impact.