Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | <= 8.00 MPa | <= 1160 psi | ISO/R527 |
Polykemi AB POLYelast TPE Z600 Thermoplastic Elastomer, SEBS-based Information provided by Polykemi AB |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
SABIC M500026 Linear Low Density Polyethylene for Injection Molding Product Description: M500026 is a Linear Low Density Polyethylene grade with a narrow molecular weight distribution suitable for injection molding applications. It has been designed to give excell.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | |
ExxonMobil LL 5202.09 Compounding Resin
(discontinued **) LL 5202.09 is a linear low density polyethylene resin designed to provide good processability and ease of blending. The granular form of LL 5202.09 makes for efficient blending with pigments, slip .. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
ICO Polymers ICOTEXâ„¢ 520-5019 300 Micron LDPE Powder Description: ICOTEX 520-5019 is a low density polyethylene powder that has been developed to meet the special requirements of the textile coating industry. Key Characteristics: good melt flow and a .. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ISO 527 |
SABIC Innovative Plastics LNP Lubricomp FX00617 PE (Asia Pacific) LNP* Lubricomp* FX00617 is a compound based on Polyethylene resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL WCP761 PPE-TPE (Asia Pacific) Flexible Noryl injection molding grade. Low specific gravity with very good non-halogenated flame retardant performance. Developed for evaluation in overmolding applications such as plugs, strain re.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP PDXF89080 PE LNP* LUBRICOMP* PDXF89080 is a compound based on Polyethylene containing Proprietary Fillers. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | After Curing |
Silikony Polskie Gumosil AD-1 A/B Silicone Rubber Flexible with high resistance to tension |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | 500mm/min; ASTM D638 Type IV Specimen |
Westlake EMAC® SP2268 24% Ethylene-Methyl Acrylate Copolymer Westlake EMAC® SP2268 is a 24% EMA copolymer designed for extrusion coating, tie-layers, compounding, and extrusions where flexibility, compatibility, low heat seal temperatures, or high coefficien.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
ELASTO UK Dryflex® 500650S SEBS Based Material, Unfilled Qualities, 65A Hardness, Translucent The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
ELASTO UK Dryflex® 602700S SEBS Based Material, Filled Qualities, 70A Hardness, Black The most significant features of the 600-series are the improved heat stability, the sound reduction and that the material enables an easy and secure pigmenting for the customer. A filled material .. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
ELASTO UK Dryflex® 662700S SEBS Based Material, Semi-Filled Qualities, 70A Hardness, Black The 660-series is recommended when the properties of the produced detail requires the advantages of the 500-series in combination with the 600-series. A semi-filled material can therefore combine t.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ISO R 527 |
Fainplast Compounds GS 59/T Flexible PVC, Injection Molding for Footwear Crystal sandals |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ISO R 527 |
Fainplast Compounds GS 62/T Flexible PVC, Injection Molding for Footwear Sandals |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ISO R 527 |
Fainplast Compounds GS 6520 Flexible PVC, Injection Molding for Footwear Soles |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ISO R 527 |
Fainplast Compounds PM 5740 Flexible PVC, Extrusion Gaskets for frames |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
Aclo Accucomp Polyethylene LD0109L Low Density |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
Azdel SuperLite® SL552000-100 PP Resin Matrix / 55% Glass Fiber (10 mm Molded Thickness) AZDEL SuperLite® SL552000-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
Arkema Group LOTADER® 8200 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride LOTADER 8200 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized under high pressure in an autoclave process. Due to its properties (reactivity, fluidity), LOTADER 82.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
Arkema Group LOTADER® AX 8840 Copolymer Ethylene - Glycidyl Methacrylate LOTADER AX 8840 is a random copolymer of Ethylene and Glycidyl Methacrylate, polymerized under high pressure in an autoclave process. Due to the reactivity induced by the Glycidyl methacrylate, LOTA.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | 500mm/min; ASTM D638 Type IV Specimen |
Westlake EMAC® SP2403 24% Ethylene-Methyl Acrylate Copolymer Westlake EMAC® SP2403 is a 24% EMA copolymer designed for extrusion coating, tie-layers, compounding, and extrusions where flexibility, compatibility, low heat seal temperatures, or high coefficien.. |
|||
Tensile Strength at Break | 8.00 MPa | 1160 psi | |
LATI Latimass 53-04 D009 PP Homopolymer, Impact Modified Specific density compound based on Polypropylene homopolymer (PPh), impact modified. Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation.. |