Polymer Property : Tensile Strength at Break = 77.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	77.0 MPa	11200 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 4701R PPC (Asia Pacific) High heat resistant polyphthlate carbonate, provides DTUL of 300F at 264 psi.
Tensile Strength at Break	77.0 MPa	11200 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 4704 PPC High heat resistant polycarbonate copolymer, provides DTUL of 300F at 264 psi. FDA food contact compliant in limited colors. Effective January 15th, 2008 this grade will no longer be supported with ..
Tensile Strength at Break	77.0 MPa	11200 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HPH4704 PPC (Asia Pacific) High heat specialty polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, gamma and e-beam steril..
Tensile Strength at Break	77.0 MPa	11200 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® PPC4701 PPC High heat resistant polyphthlate carbonate, provides DTUL of 300F at 264 psi.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	77.0 MPa	11200 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® PPC4701R PPC High heat resistant polyphthlate carbonate, provides DTUL of 300F at 264 psi. Internal mold release.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	77.0 MPa	11200 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® PPC4704 PPC High heat resistant polycarbonate copolymer, provides DTUL of 300F at 264 psi. FDA food contact compliant in limited colors. Effective January 15th, 2008 this grade will no longer be supported wit..
Tensile Strength at Break	77.0 MPa	11200 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-KON RFD02 PA 66 LNP* STAT-KON* RFD02 is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break	77.0 MPa	11200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP AF004L ABS LNP* THERMOCOMP* AF004L is a compound based on ABS resin containing 20% Glass Fiber. Added feature of this material is: Low Extractible.
Tensile Strength at Break	77.0 MPa	11200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP AF004XXY ABS LNP* Thermocomp* AF004XXY is a compound based on ABS containing 20% glass fiber.
Tensile Strength at Break	77.0 MPa	11200 psi	ASTM D 638
SABIC Innovative Plastics LNP Thermocomp AF008 ABS LNP* Thermocomp* AF008 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	77.0 MPa	11200 psi	ASTM D 638
SABIC Innovative Plastics LNP Thermocomp AF008 ABS (Asia Pacific) LNP* Thermocomp* AF008 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break	77.0 MPa	11200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP AX02749 ABS LNP* THERMOCOMP* AX02749 is a compound based on ABS containing proprietary fillers.
Tensile Strength at Break	77.0 MPa	11200 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DF003E PC LNP* Thermocomp* DF003E is a compound based on Polycarbonate resin containing 15% Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break	77.0 MPa	11200 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DF003E PC (Asia Pacific) LNP* Thermocomp* DF003E is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break	77.0 MPa	11200 psi	50 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP J1000ER PES (Europe-Africa-Middle East) LNP* THERMOCOMP* J1000ER is a compound based on Polyethersulfone resin. Added features include : Easy Molding, Mold Release
Tensile Strength at Break	77.0 MPa	11200 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp RW008XXZ PA 66 LNP* Thermocomp* RW008XXZ is a compound based on Nylon 6/6 resin containing Wollastonite.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	77.0 MPa	11200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp RW008XXZ PA 66 LNP* Thermocomp* RW008XXZ is a compound based on Nylon 6/6 resin containing Wollastonite.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	77.0 MPa	11200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP WF002 PBT LNP* THERMOCOMP* WF002 is a compound based on PBT containing 10% Glass Fiber.
Tensile Strength at Break	77.0 MPa	11200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP EP003 PEI LNP* Lubricomp EP003 is a Polyetherimide containing 15% PTFE/Silicone. Added features include: Internally Lubricated.
Tensile Strength at Break	77.0 MPa	11200 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOTUF VF003 PA 66 (Asia Pacific) LNP* THERMOTUF* VF003 is a compound based on Nylon resin containing Glass Fiber. Added features of this material include: High Impact.
Tensile Strength at Break	77.0 MPa	11200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL EM7304F PPE+PS 15% glass reinforced, high flow with enhanced polyurethane foam adhesion for instrument panel retainers.
Tensile Strength at Break	77.0 MPa	11200 psi	ISO 527-1/-2
Unitika BV2120 PA66, Flame Retardant, Dry Information provided by Unitika Ltd.
Tensile Strength at Break	77.0 MPa	11200 psi	ISO 527-93
Wellman Wellamid® MR409 22H-NBK4 40% Mineral Reinforced Nylon 66 Description: Mineral Reinforced Nylon 66Information provided by Wellman.
Tensile Strength at Break	77.0 MPa	11200 psi	ISO 527-1/-2
Covestro Bayblend® T88-4N Polycarbonate + ABS, 20% Glass Filled Injection molding grade20 % glass fiber filledtensile modulus = 5900 MPaVicat/B 120 temperature = 134 °CPreprocessingMax. Water content
Tensile Strength at Break	77.0 MPa	11200 psi	50%RH; ISO 527-1/-2
DuPont Performance Polymers Zytel® BM70G20HSLX BK537 Nylon 66 (Unverified Data**) 20% Glass Reinforced Heat Stabilized Polyamide 66 Developed for Blow Molding Zytel BM70G20HSLX BK537 is a 20% glass fiber reinforced polyamide 66 for blow molding.Information provided by DuPont Perf..
Tensile Strength at Break	77.0 MPa @Temperature 120 °C	11200 psi @Temperature 248 °F	ISO Data
BASF Ultramid® TG7S 35% Glass Filled PA6 (Dry) Ultramid TG7S is a 34% glass reinforced, heat stabilized, impact modified PA6 injection molding grade. It was developed to meet the demanding requirements of the first North American seat cushion ..
Tensile Strength at Break	77.0 MPa	11200 psi	ISO 527 Type 1A
Solvay TECHNYL® A 31T1 MZ40 PA66, 40% mineral fiber, DRY Description: Flame retardant polyamide PA66, 40% mineral filled, heat stabilized, for injection molding.Available in: Asia Pacific, Europe, Latin America and North America Product Applications: This..