Polymer Property : Tensile Strength at Break = 58.6 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	58.6 MPa	8500 psi	2 in/min; ASTM D638
RheTech Products F38-04 35% Glass Fiber/Mineral Co-Reinforced Polypropylene, Chemically Coupled, White Applications: HousingsBracketsSupport ductsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	58.6 MPa	8500 psi	ASTM D638
Oxford Polymers PC 714-FR Series PC, Flame retardant Product Description: Amorphous, Polycarbonate injection molding grade, flame retardant Processing and Delivery Form: Pellets and Injection MoldingAdditives: Release Agents and UV stabilizersSpecial..
Tensile Strength at Break	58.6 MPa	8500 psi	ASTM D638
Polymer Resources PC-GP2-TFE5 Polycarbonate, 5% PTFE, Wear Resistant, Medium Flow Polycarbonate, 5% PTFE, General Purpose, Medium Flow, Wear ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samp..
Tensile Strength at Break	58.6 MPa	8500 psi	ASTM D638
Polymer Resources PPX-GP6 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 290F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati..
Tensile Strength at Break	58.6 MPa	8500 psi	ASTM D638
Ravago Manufacturing Americas Hysun™ A3525 ASA+PC Available in North America Features: Good Impact Resistance RoHS CompliantForm: PelletsInformation provided by Ravago
Tensile Strength at Break	58.6 MPa	8500 psi	2.0 in/min; ASTM D638
LTL Color Compounds ColorFastÂ® FRPBT200 PBT, Flame Retarded V-0 rated, unfilled PBTAll information provided by LTL Color Compounders, Inc.
Tensile Strength at Break	58.6 MPa	8500 psi	50 mm/min; ASTM D638
Styron CALIBREâ„¢ 891-10 Polycarbonate Resin Overview: CALIBREâ„¢ 891-10 Series provides superior ignition resistance in opaque applications. The CALIBRE 891-10 series products are available in 2 additive packages: CALIBRE 891: Mold release..
Tensile Strength at Break	58.6 MPa	8500 psi	ASTM D638
Chase Plastics CP Pryme® PC300HFR Polycarbonate (Utility Grade), High Flow, Mold Release Information provided by Chase Plastics.
Tensile Strength at Break	58.6 MPa	8500 psi	ASTM D638
Chase Plastics CP Pryme® PC300R Polycarbonate (Utility Grade), Mold Release Information provided by Chase Plastics.
Tensile Strength at Break	58.6 MPa	8500 psi	ASTM D638
Chase Plastics CP Pryme® PC300RUV Polycarbonate (Utility Grade), UV Stabilizer, Mold Release Information provided by Chase Plastics.
Tensile Strength at Break	58.6 MPa	8500 psi	TM R050-36
Resinlab® EP1238 Acrylic / Epoxy Hybrid Adhesive Resinlab™ EP1238 is a two part acrylic / epoxy hybrid adhesive designed for bonding metals and plastics. It cures quickly at room temperature to a tough, semi-rigid material. It has good wetting to..
Tensile Strength at Break	>= 58.6 MPa	>= 8500 psi
Master Bond EP33LV Epoxy Has Dimensional Stability and Machinability Description: Master Bond EP33LV is a two part, room temperature curing epoxy system used for bonding, sealing and coating featuring high temperature resistance, good dimensional stability and very g..