Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 552 - 586 MPa | 80000 - 85000 psi | 304 Stainless Steel butt joint |
Lucas-Milhaupt BRAZE 380 Characteristics:Braze 380 is a free-flowing, low temperature filler metal with excellent wetting of most ferrous and non-ferrous base metals, and is a good substitute for cadmium-bearing filler meta.. |
|||
Tensile Strength at Break | 552 - 586 MPa | 80000 - 85000 psi | 304 Stainless Steel butt joint |
Lucas-Milhaupt BRAZE 452 Characteristics:Braze 452 is a free-flowing, low temperature filler metal commonly used to replace cadmium-bearing filler metals of similar silver content. This alloy is best suited for narrow gap .. |
|||
Tensile Strength at Break | 552 MPa | 80000 psi | |
Shakespeare WP-104 diameter 0.2 mm Weft Polyester Monofilament Paper Machine Clothing MonofilamentStandard molecular weightPolyesterLow modulusWeft yarnLow shrinkage Information provided by Shakespeare Company. |
|||
Tensile Strength at Break | 552 MPa | 80000 psi | |
Shakespeare WP-104 diameter 0.4 mm Weft Polyester Monofilament Paper Machine Clothing MonofilamentStandard molecular weightPolyesterLow modulusWeft yarnLow shrinkage Information provided by Shakespeare Company. |
|||
Tensile Strength at Break | 552 MPa | 80000 psi | |
Shakespeare WP-120 diameter 0.2 mm Weft Polyester Monofilament Paper Machine Clothing MonofilamentHigh molecular weightPolyesterLow modulusWeft yarnLow shrinkage Information provided by Shakespeare Company. |
|||
Tensile Strength at Break | 552 MPa | 80000 psi | |
Shakespeare WP-120 diameter 0.5 mm Weft Polyester Monofilament Paper Machine Clothing MonofilamentHigh molecular weightPolyesterLow modulusWeft yarnLow shrinkage Information provided by Shakespeare Company. |
|||
Tensile Strength at Break | 552 MPa | 80000 psi | |
Shakespeare WP-120 diameter 0.7 mm Weft Polyester Monofilament Paper Machine Clothing MonofilamentHigh molecular weightPolyesterLow modulusWeft yarnLow shrinkage Information provided by Shakespeare Company. |
|||
Tensile Strength at Break | 552 MPa | 80000 psi | |
Shakespeare WP-550 diameter 0.5 mm Hydrolytically Stabilized Polyester Yarn Paper Machine Clothing MonofilamentHigh molecular weightPolyesterHydrolytically stableWarp and weft yarnLow shrinkageLow modulus Information provided by Shakespeare Company. |
|||
Tensile Strength at Break | >= 552 MPa | >= 80000 psi | |
Master Bond EP17HT-3 One component, snap-curing epoxy system Product Description: Master Bond Polymer System EP17HT-3 is a one part epoxy that fully cures in 2-3 minutes at 250-300°F. It is capable of service up to +400°F with excellent strength retention p.. |
|||
Tensile Strength at Break | 552 - 758 MPa | 80100 - 110000 psi | |
ThyssenKrupp 12Ni5 Structural Steel 5% nickel steel for low temperature service down to -165°FApplication for pressure vessels and tanks for the transportation and storage of ethyleneReference: 5.000 t/y in thicknesses up to 2 in.Hea.. |
|||
Tensile Strength at Break | 552 MPa | 80000 psi | Stress relieved |
California Fine Wire Copper Clad 1006 Steel (40% Conductivity) All values may vary dependent on specific design and usage1006 steel core, 99.99% copper cladCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
Tensile Strength at Break | 552 MPa | 80000 psi | Annealed |
California Fine Wire Dumet Nickel Iron Core Copper Clad Alloy All values may vary dependent on specific design and usage99.9% copper cladding over iron-nickel coreCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
Tensile Strength at Break | 552 MPa | 80000 psi | Stress relieved |
California Fine Wire Nickel 220 Super Alloy All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
Tensile Strength at Break | 552 MPa | 80000 psi | Stress relieved |
California Fine Wire Nickel 5900 Nickel Alloy All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
Tensile Strength at Break | >= 552 MPa | >= 80000 psi | |
Carlson 20 Plus Alloy Carlson C20 Plus is a super-austenitic alloy, developed to provide maximum resistance to corrosion by sulfuric acid. Nickel chromium, molybdenum and copper contribute to the excellent overall resist.. |
|||
Tensile Strength at Break | >= 552 MPa | >= 80000 psi | |
Carlson 317L 4N Austenitic Stainless Steel General DescriptionCarlson’s 317L, 317L 4, and 317L 4N are austenitic chromium-nickel-molybdenum stainless steels with alloy contents greater than the 316 grades. The additional chromium, nickel a.. |
|||
Tensile Strength at Break | >= 552 MPa | >= 80000 psi | |
Carlson C 600 Nickel-Chromium-Iron Alloy Carlson Alloy C 600 is nickel-chromium alloy, developed for use in severely corrosive environments at elevated temperatures. The high nickel content of this alloy provides excellent resistance to c.. |
|||
Tensile Strength at Break | >= 552 MPa | >= 80000 psi | |
Carlson C 600ESR Nickel-Chromium-Iron Alloy General DescriptionCarlson Alloy C 600 is nickel-chromium alloy, developed for use in severely corrosive environments at elevated temperatures. The high nickel content of this alloy provides excell.. |
|||
Tensile Strength at Break | >= 552 MPa | >= 80000 psi | |
Carlson C 601 Nickel-Chromium-Iron Alloy General DescriptionCarlson Alloy C 6021 is a nickel-chromium alloy, developed specifically for high –temperature service. This alloy exhibits outstanding resistance to both cyclic and static oxida.. |
|||
Tensile Strength at Break | 552 - 586 MPa | 80000 - 85000 psi | 304 Stainless Steel butt joint |
Lucas-Milhaupt BRAZE 402 Silver Based Cadmium Free Filler Metal Characteristics: Braze 402 is a free-flowing, intermediate temperature filler metal and as such is a good substitute for cadmium-bearing filler metals with similar silver contents. The material is .. |
|||
Tensile Strength at Break | 552 - 621 MPa | 80100 - 90100 psi | Sheet, Cold-rolled & Solution Annealed |
Special Metals INCOLOY® alloy 803 Fe-Ni-Cr Alloy INCOLOY® alloy 803 (UNS S35045), an iron-nickel-chromium alloy, is designed for use in petrochemical, chemical and thermal processing applications. The nickel and chromium contents of alloy 803 ar.. |