Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 55.2 MPa | 8000 psi | Mixed 2:1; TM R050-36 |
Resinlab® EP1215 Clear Unfilled Epoxy Structural Adhesive Resinlab™ EP1215 Clear is a two part unfilled epoxy structural adhesive designed for bonding applications requiring high strength and good impact resistance. It cures completely at room temperature.. |
|||
Tensile Strength at Break | 55.2 MPa | 8000 psi | 2 in/min; ASTM D638 |
RheTech Products F43-01 35% Glass Fiber/Mineral Co-Reinforced Polypropylene Copolymer, Chemically Coupled, Black Applications: Fan shroudsDip trayFunctional supportsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 55.2 MPa | 8000 psi | 2 in/min; ASTM D638 |
RheTech Products G13P100-332UV 13% Glass Fiber Reinforced Polypropylene, UV Stabilized, (GM 9772) Light Neutral Applications: Interior trimAir ducts - distributionFuel filler pocketInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 55.2 MPa | 8010 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne LubriOne™ PC-000/15T Polycarbonate (PC) Information provided by PolyOne |
|||
Tensile Strength at Break | 55.2 MPa | 8000 psi | ASTM D638 |
Niche Polymer PA66MIBK Nylon 66, Medium Impact Information provided by Niche Polymer |
|||
Tensile Strength at Break | 55.2 MPa | 8000 psi | ASTM D638 |
Polymer Resources PC-GP3-TFE10 Polycarbonate, 10% PTFE, High Flow, Wear Resistant Polycarbonate, General Purpose, High Flow, Wear ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informa.. |
|||
Tensile Strength at Break | 55.2 MPa | 8000 psi | ASTM D638 |
Polymer Resources PPX-GP1-[color]EN Modified PPO, Extrusion Grade with HDT of 265 F Process: Extrusion Notes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength at Break | 55.2 MPa | 8010 psi | ASTM D 638 |
NOVA Chemicals Dylark® FG7300 High-Heat Styrenic Copolymer Product Description and Features: Styrene/maleic anhydride copolymer with high-heat resistance and high modulus. Resins designed for use in foam extrusion.Processing: Contact NOVA Chemicals techn.. |
|||
Tensile Strength at Break | 55.2 MPa | 8000 psi | ASTM D638 |
Ravago Manufacturing Americas Hylex® P1010LLT Polycarbonate Information provided by Ravago. |
|||
Tensile Strength at Break | 55.2 MPa | 8000 psi | TM R050-36 |
Resinlab® EP1385 Clear Epoxy Formulation Resinlab™ EP1385 Clear is an epoxy formulation designed for applications requiring resistance to E-85 type fuels. It has good wetting and adhesion to most surfaces. It has very good resistance to w.. |
|||
Tensile Strength at Break | 55.2 MPa | 8000 psi | ASTM D638 |
Polymer Resources PC/TP-GP1 PC Polyester, High Impact, Good Chemical Resistance
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength at Break | 55.2 MPa | 8000 psi | ASTM D638 |
Ravago Manufacturing Americas Enviramid™ N1300THL BK Post Consumer Recycle Nylon 66 Impact Modified, Heat Stabilized, Lubricated, Black and Made from EnViramid Post Consumer Recycled NylonInformation provided by Ravago. |
|||
Tensile Strength at Break | 55.2 MPa @Thickness 50.8 mm |
8000 psi @Thickness 2.00 in |
ASTM D638 |
Teknor Apex Synres® PP G10 17 Polypropylene, Glass Reinforced Notes: The Specialty Compounding Division offers a proprietary line of glass reinforced polypropylene. Typical applications include automotive, building and construction, industrial as well as many .. |
|||
Tensile Strength at Break | 55.2 MPa | 8000 psi | ASTM D882 |
Total PPH 3576XHD Polypropylene Homopolymer, Film Grade Low Residuals TOTAL Polypropylene 3576XHD utilizes the new ATOFINA proprietary process technology to provide extremely low residuals for improved color stability and clarity.Antiblock. 3576XHD is .. |
|||
Tensile Strength at Break | 55.2 MPa | 8000 psi | 2.0 in/min; ASTM D638 |
LTL Color Compounds ColorFast® FRPC100 Polycarbonate, Flame-Retarded Flame-retarded V0, high impact injection molding polycarbonateAll information provided by LTL Color Compounders, Inc. |