Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Cycoloy® C3650 PC+ABS (Europe-Africa-Middle East) Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering high impact and excellent extrusion and thermoforming characteristics. Halogen free according .. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® C6850REC PC+ABS (Europe-Africa-Middle East) PC+ABS Industrial quality. Flame retardant. Limited colors only (Black and Grey)This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® CX3222ME PC+ABS Cycoloy* resin grade CX3222ME is an extrudable & thermoformable PC/ABS blend with non brominated and non chlorinated flame retardant systems. Key features of low gloss and good impact make it ideal .. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® XCY620 PC+ABS PC+ ABS Automotive applications, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® XCY620 PC+ABS (Asia Pacific) PC+ ABS Automotive applications, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Geloy HRA222 ASA (Europe-Africa-Middle East) GELOY HRA222 is a multi-purpose, chlorine and bromine free flame retardant ASA+PC alloy for injection moulding processes. Typical properties as measured on natural material.This data was supplied by.. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics GELOY HRA222 ASA+PC (Europe-Africa-Middle East) GELOY HRA222 is a multi-purpose, chlorine and bromine free flame retardant ASA+PC alloy for injection moulding processes. Typical properties as measured on natural material. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics GELOY HRA222F ASA+PC Geloy HRA222F is a multi-purpose, chlorine and bromine free flame retardant PC+ASA alloy for injection molding processes. F1 rating according UL746C. Use for exterior/interior electrical application.. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® BPL1000 PC Lexan* BPL1000 Polycarbonate (PC) resin is an injection moldable grade featuring high flow and good impact peroformance. It contains non-chlorinated and non-brominated flame retardant systems with U.. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP KONDUIT PX09322 PA 6 (Asia Pacific) White colored thermally conductive mineral filled PA6 FR compound |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP Cycoloy_C2801 PC+ABS LNP* Lubricomp* Cycoloy_C2801 compound is a 5% PTFE reinforced PC+ABS, wear resistant, flame retardant compound for moving components in business equipment. Medium heat performance |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® FXD1414T PC Copolymer PC-siloxane copolymer in special light diffusion colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP WL002 PBT LNP* LUBRICOMP WL002 is a compound based on PBT resin containing 10% PTFE. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRILOY K2000XXH Acetal LNP LUBRILOY* K2000XXH is a compound based on Acetal resin containing Proprietary Lubricant. Added features of this material are: Wear Resistant, Healthcare. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DX96717C PC LNP STAT-KON* DX96717C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Flame Retardant. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Xenoy® 5220U PBT+PC Unreinforced PBT+PC Alloy. Impact Modified. Improved retention of mechanical properties under UV exposure. Excellent low temperature impact and chemical resistance. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP 9X07430 PBT+PC LNP* THERMOCOMP* 9X07430 is a compoud based on a PBT+PC Blend containing Glass Fiber, Talc. Added features of this material include: Opaque, Weatherable. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP CX05470 PS LNP* THERMOCOMP* CX05470 is a compound based on Polystyrene resin containing 20% Glass Fiber. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Noryl GTX GTX9200 PPE+PS+PA66 High Flow GTX for Automotive applicationsThis data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® IQ3001 PBT Valox IQ3001 is an unfilled environmentally responsible iQ-PBT resin modified with elastomer. Targeted for flexible hinge applications. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP MF002S PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MF002S is a compound based on Polypropylene resin containing Glass Fiber. Added features include: Heat Stabilized. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP NF001XXX PC+ABS LNP* THERMOCOMP* PCA-F-1001 is a compound based on PC+ABS resin containing 5% Glass Fiber. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL EXNL0357 PPE+PS |
|||
Tensile Strength at Break | 51.0 - 53.0 MPa | 7400 - 7690 psi | DIN 53455 |
Zell-Metall Engineering Plastics Zellamid 1100 OIL at 50% RH Zellamid® 1100 OIL: A new type of cast nylon produced by addition of a special oil to the polymer structure. By laboratory test it was proven that this second generation oil filled product reduces .. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | ISO 527 |
Unitika TERRAMAC TE-1030 Polylactic Acid (PLA) High-Impact grade, Injection grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | ASTM D638 |
Eastman Tenite 285E3720005 Butyrate Clear, Trsp Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite cellulosi.. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | ASTM D638 |
Diamond Polymers NPP 60-1010 PCTA Polyester Alloy Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | Conditioned 15 days at 23°C - 50% RH; ASTM D638 |
Arkema Group Pebax® Rnew 63R53 SP 01 Polyether Block Amide (PEBA) Polyether block amide Pebax® 63R53 SP 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide based on renewable resources. This SP grade has been developed to be heat and UV.. |
|||
Tensile Strength at Break | 51.0 MPa | 7400 psi | ASTM D412 |
Alliance Polymers Zythane™ 6065D Thermoplastic Polyurethane Elastomer Zythane™ 6065D is a polycaprolactone-based TPU specifically formulated for injection molding applications .It exhibits excellent low compression set, abrasion resistance and toughness and has good .. |
|||
Tensile Strength at Break | 51.0 MPa @Temperature 120 °C |
7400 psi @Temperature 248 °F |
ISO Data |
BASF Ultramid® 8267G HS BK-106 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid 8267G HS BK-106 is a heat stabilized, weather resistant, 40% mineral and glass fiber reinforced PA6 injection molding compound with improved UV resistance and sink mark resistance. The com.. |