Polymer Property : Tensile Strength at Break = 48.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	48.0 MPa	6960 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Cycoloy® CY2000 PC+ABS Cycoloy resin CY2000 is a flame retardant (FR) PC/ABS blend free from halogen containing FR agents. It was designed to meet CA133 application requirements.This data was supplied by SABIC-IP for the ..
Tensile Strength at Break	48.0 MPa	6960 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Cycoloy® CY2010 PC+ABS (Europe-Africa-Middle East) Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow for a wide variety of thin wall or large size applicat..
Tensile Strength at Break	48.0 MPa	6960 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Cycoloy® CY5005 PC+ABS (Europe-Africa-Middle East) Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow for a wide variety of thin wall or large size applicat..
Tensile Strength at Break	48.0 MPa	6960 psi	ISO 527
Nilit FRIANYL B63 AL40 Nylon 6.6 for injection molding, 40% aluminum filled Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	48.0 MPa	6960 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Geloy FXW751SK ASA+PC (Europe-Africa-Middle East) Sparkle Metallic VisualFx ASA+PC Resin - Weatherable, High Heat & Impact ResinThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength at Break	48.0 MPa	6960 psi	50 mm/min; ISO 527-1,2
Qualchem Danamid FEWLX2-25 Polyamide 6, 25% Mineral Filled Filled with minerals. Flame retardant, halogen-free (V-2)Information provided by Qualchem Zrt.
Tensile Strength at Break	48.0 MPa	6960 psi	ASTM D 638
SABIC Innovative Plastics LNP Colorcomp D10009 PC (Asia Pacific) LNP* Colorcomp* D10009 is a compound based on Polycarbonate resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant.This data was supplied ..
Tensile Strength at Break	<= 48.0 MPa	<= 6960 psi	ISO/R527
Polykemi AB POLYabs H00 HF ABS, Heat Resistant, High Flow Information provided by Polykemi AB
Tensile Strength at Break	<= 48.0 MPa	<= 6960 psi	ISO/R527
Polykemi AB POLYabs HF0 ABS Information provided by Polykemi AB
Tensile Strength at Break	48.0 MPa	6960 psi	10mm/min; ASTM D638
Kingfa PA66-C111 Toughened PA66 Features:High impactLow tendency to wrapExcellent balance propertiesApplications:Injection moldingSport applianceAutomobile partsPower toolsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Tensile Strength at Break	48.0 MPa	6960 psi	ASTM D638
LG Chemical LUCEL HI-515 High Impact POM, Unreinforced LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Tensile Strength at Break	48.0 MPa	6960 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Lubricomp GX07409X PSU Wear resistant PSUThis data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	48.0 MPa	6960 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP KG002 Acetal Copolymer LNP* LUBRICOMP* KG002 is a compound based on Acetal Copolymer resin containing 10% Graphite. Added feature of this material is: Wear Resistant.
Tensile Strength at Break	48.0 MPa	6960 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP KL002 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KL002 is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	48.0 MPa	6960 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KP002 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	48.0 MPa	6960 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KP002 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	48.0 MPa	6960 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP WH0200B PBT LNP* Thermocomp* WH0200B is a compound based on PBT resin containing proprietary fillers. Added features include: High Specific Gravity.
Tensile Strength at Break	48.0 MPa	6960 psi	ASTM D638
Sumitomo Bakelite North America EM 7302XLD Long Glass Fiber Reinforced Epoxy EM 7302XLD is a long fiberglass reinforced epoxy molding compound with a low density inert filler. This compound is designed for applications where moderate strength and weight savings are desirable..
Tensile Strength at Break	48.0 MPa	6960 psi	ASTM D638
Total PSC 1441 Easy Flow, High Heat Resistance Polystyrene Total Petrochemicals Polystyrene 1441 is an easy flowing crystal polystyrene designed for extrusion or injection applications. In extrusion, it improves extruder output and thermoforming cycle time..
Tensile Strength at Break	48.0 MPa	6960 psi	ISO 527-2
Total PSC 1450N High Heat Resistance Polystyrene 1450N is a high heat resistance, easy flowing crystal polystyrene for the production of thick insulation board. The low viscosity of this grade makes it particularly suitable for the production of ..
Tensile Strength at Break	48.0 MPa	6960 psi	ISO 527-2
Total PSC 1160/1160N Crystal Polystyrene 1160 is a high resistance, high molecular weight crystal polystyrene mainly for the extrusion industry. Most notable for the production of bi-oriented polystyrene (BOPS). It is particularly useful..
Tensile Strength at Break	48.0 MPa	6960 psi	ASTM D638
Eastman Provista ST Copolymer Provista Copolymer ST is a resin specifically developed for profile extrusion where high clarity and gloss, toughness, and processability are critical. Provista Copolymer ST is a second-generation m..
Tensile Strength at Break	48.0 MPa	6960 psi	ASTM D638
Eastman Eastar GN078 Copolyester, Natural Eastar Copolyester GN078 builds on the strength of Eastar Copolyester GN077 by offering improved melt strength and toughness. Eastar Copolyester GN078 does not meet FDA compliance but is an excellen..
Tensile Strength at Break	48.0 MPa	6960 psi	ASTM D638
Aclo Accutech Polypropylene Copolymer CP0437G30CL Glass Reinforced Coupled
Tensile Strength at Break	48.0 MPa	6960 psi	ASTM D412
Alliance Polymers Zythane™ 4085A Thermoplastic Polyurethane Elastomer Zythane™ 4085A is a polycaprolactone-based TPU specifically formulated for injection molding applications .It exhibits excellent low compression set, abrasion resistance and toughness and has good ..
Tensile Strength at Break	48.0 MPa	6960 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Noryl FXN119LG PPE+HIPS (Asia Pacific) Noryl FXN119LG is a low gloss PPE/HIPS grade. It provides a balance of mechanical properties and heat performance with intrinsic low gloss appreance. FXN119LG is available in mutliple colors.This da..
Tensile Strength at Break	48.0 MPa	6960 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Noryl FXN119LG PPE+HIPS (Europe-Africa-Middle East) Noryl FXN119LG is a low gloss PPE/HIPS grade. It provides a balance of mechanical properties and heat performance with intrinsic low gloss appreance. FXN119LG is available in mutliple colors.This da..
Tensile Strength at Break	48.0 MPa	6960 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Xenoy® X6800BM PBT (Europe-Africa-Middle East) Blow moldable, impact modifed XENOY
Tensile Strength at Break	48.0 MPa	6960 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DL002ER PC (Asia Pacific) LNP* Lubricomp* DL002ER is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated, Easy Molding, Mold Release.
Tensile Strength at Break	48.0 MPa	6960 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRILOY Z20001 PPO LNP* Lubriloy* Z20001 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, Flame Retardant.