Polymer Property : Tensile Strength at Break = 42.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	<= 42.0 MPa	<= 6090 psi	ISO/R527
Polykemi AB POLYabs R00 UV4 ABS, High Impact, UV Stabilized Information provided by Polykemi AB
Tensile Strength at Break	<= 42.0 MPa	<= 6090 psi	ISO/R527
Polykemi AB POLYabs XX0 ABS, Extrusion Grade Information provided by Polykemi AB
Tensile Strength at Break	42.0 MPa	6090 psi	Tensile stress at break.
Dow Pellethane® 2102-90AE Polyurethane Elastomer, Polyester Polycaprolactone Based (discontinued **) PELLETHANE® 2102-90AE elastomer is a polyester polycaprolactone based polyurethane elastomer which combines excellent resistance to fuels and oils with good damping capacity and good hydrolytic sta..
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527
Nilit FRIANYL C73 HS28 Nylon 6.6/6 for injection molding Nylon 6.6/6 for injection molding, medium viscosity, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
3M Dyneon™ PVDF 1010/0001 Polyvinylidene Fluoride (discontinued **) Polyvinylidene Fluoride (PVDF) is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, an..
Tensile Strength at Break	42.0 MPa	6090 psi	50mm/min; ASTM D638
3M Dyneon™ PVDF 1015/1001 Polyvinylidene Fluoride (discontinued **) Ultra-high molecular weight grade PVDFPowder gradeExcellent chemical resistance to a wide variety of aggressive fluids and solventsGood permeation resistanceExcellent strength and dimensional stabil..
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DL003P PC (Asia Pacific) LNP LUBRICOMP* DL003P is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Exceptional Processing.
Tensile Strength at Break	42.0 MPa	6090 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP HAL23 PA11 (Europe-Africa-Middle East) LNP* LUBRICOMP* HAL23 is a compound based on PA 11 resin containing Aramid Fiber, PTFE. Added features include: Internally Lubricated.
Tensile Strength at Break	42.0 MPa	6090 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP NL001 PC+ABS LNP LUBRICOMP* NL001 is a compound b ased on PC+ABS resin containing 5% PTFE. Added features include: Wear Resistant, Suitable for Thin Wall Applications.
Tensile Strength at Break	42.0 MPa	6090 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP NXCY620 PC+ABS LNP* LUBRICOMP* NXCY620 is a compound based on Cycoloy* XCY620 containing Silicone. Added feature of this material is: Lubricant.
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527 Type 1A
Solvay TECHNYLÂ® C 236SI PA6, Conditioned Description: Unreinforced polyamide 6 with high impact strength for injection molding.Available in: Europe and North AmericaProduct Applications: TECHNYLÂ® C 236SI has high impact strength and fle..
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP ZP001XXP PPE+PS (Asia Pacific) LNP* Lubricomp* ZP001XXP is a compound based on PPE+PS Blend resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	42.0 MPa	6090 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® 357 PBT+PC PC/PBT, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures.
Tensile Strength at Break	42.0 MPa	6090 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON KX96321 POM LNP* STAT-KON* KX96321 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.
Tensile Strength at Break	42.0 MPa	6090 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics XenoyÂ® ENH2900 PBT+PC (Asia Pacific) Xenoy* ENH2900 is a Non-Braominated, Non Chlorinated flame retarded PC/PBT resin with good flow, high impact and excellent chemical resistance. It was designed quite suitable for E&E housing applic..
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS LNP* STAT-LOY* AF3009 is a compound based on ABS resin containing 10% Glass Fiber. Added features of this material include: Antistatic, Flame Retardant.
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS LNP* STAT-LOY* AF3009 is a compound based on ABS resin containing 10% Glass Fiber. Added features of this material include: Antistatic, Flame Retardant.
Tensile Strength at Break	42.0 MPa	6090 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP NX07354 PC+ABS (Asia Pacific) This is a PC/ABS compound, a good candidate for Laser Direct Structuring applications.
Tensile Strength at Break	42.0 MPa	6090 psi	50 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP YF003S Polyester Elastomer (Europe-Africa-Middle East) LNP* THERMOCOMP* YF003S is a compound based on Polyester Elastomer containing Glass Fiber. Added features include; Heat Stabilized.
Tensile Strength at Break	42.0 MPa	6090 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Noryl GTX LMX171 PPO/PBT (Europe-Africa-Middle East) Noryl LMX171 is a PPO/PBT blend including conductive agent with a balanced heat/impact property profile. Noryl LMX differentiate from Noryl GTX by a lower moisture uptake (0.15%).This data was suppl..
Tensile Strength at Break	42.0 MPa	6090 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics XenoyÂ® X3108UV PBT+PC (Asia Pacific) Unreinforced, UV-stabilized, flame retardant, impact modified PBT+PC with V0 at 0.8mm thickness. For interior and exterior applications like wall switches and electrical enclosures.This data was sup..
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DB008ERP PC LNP* THERMOCOMP* DB008ERP is a compound based on Polycarbonate resin containing 40% Glass Bead. Added features of this material include: Easy Molding, Mold Release.
Tensile Strength at Break	42.0 MPa	6090 psi	ISO R 527
Stir SpA RH I P (PVC) Application: Spiral extrusion - various profilesInformation provided by STIR SpA
Tensile Strength at Break	42.0 MPa	6090 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL BN9003G PPE+HIPS PPE+PS blend. Unfilled. Blow molding. Excellent balance of impact and surface aesthetics. Suitable for automotive exterior components including spoilers.
Tensile Strength at Break	42.0 MPa	6090 psi	Conditioned 15 days at 23°C - 50% RH; ASTM D638
Arkema Group Pebax® MX 1205 SA 01 Polyether Block Amide (PEBA) Polyether block amide PEBAX® MX 1205 SA 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This SA grade is specially designed to food uses.Information provided by Arke..
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
Braskem Green PE SGM7746C Blow Molding and Monofilament High Density Polyethylene Lower greenhouse gas emissions100% made from renewable raw materialsPerformance and Competitiveness: Green Polyethylene has the same characteristics as petrochemical polyethyleneApplications: Mono..
Tensile Strength at Break	42.0 MPa	6090 psi	50mm/min; ASTM D638
3M Dyneon™ PVDF 6010/0000 Polyvinylidene Fluoride Polyvinylidene Fluoride (PVDF) is ideal for multiple applications across a wide array of industries. Widely used in the chemical processing industry, wire and cable industry, semiconductor industry,..
Tensile Strength at Break	<= 42.0 MPa	<= 6090 psi	ISO/R527
Polykemi AB POLYabs F20 GF17 ABS, Glass Fiber Reinforced Information provided by Polykemi AB
Tensile Strength at Break	42.0 MPa	6090 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL RN0612 PPE+HIPS (Europe-Africa-Middle East) Noryl RN0612 is an unfilled Post Consumer recycle (PCR) based injection moldable modified polyphenylene ether resin comprising at least 30% PCR styrenic series resin content. Designed for good dimen..