Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 36.0 MPa | 5220 psi | Type 1, 2"/min; ASTM D638 |
Proto3000 ABS-M30 Fused Deposition Modeling Polymer Description: ABS-M30 is up to 25-70 percent stronger than standard Stratasys ABS and is an ideal material for conceptual modeling, functional prototyping, manufacturing tools, and end-use-parts. ABS.. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | Type 1, 2"/min; ASTM D638 |
Proto3000 ABS-M30i Fused Deposition Modeling Polymer Description: ABS-M30i is a high strength material well suited for the medical, pharmaceutical and food packaging industries. Parts manufactured with ABS-M30i material are biocompatible (ISO 10993 ce.. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Geloy FXTW26SK ASA Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Geloy XTWM206 ASA (Europe-Africa-Middle East) Next generation ASA optimized for outstanding weatherability, colorability and higher heat applications requiring UV exposure resistance.This data was supplied by SABIC-IP for the Europe-Africa-Midd.. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Geloy FXTW26SK ASA (Asia Pacific) Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Asia Pacific region... |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Geloy FXTW26SK ASA (Asia Pacific) Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Asia Pacific region... |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Geloy FXTW26SK ASA (Europe-Africa-Middle East) Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Europe-Africa-Middle.. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Geloy FXTW26SK ASA (Europe-Africa-Middle East) Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Europe-Africa-Middle.. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO R 527 |
Fainplast Compounds RE 330 Rigid PVC, Extrusion Various profiles |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO R 527 |
Fainplast Compounds RE 425 Rigid PVC, Extrusion Electric channels |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO R 527 |
Fainplast Compounds RE 425/R Rigid PVC, Extrusion Shiny electric channels |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO R 527 |
Fainplast Compounds RI 50 Rigid PVC, Injection Molding Technical items |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO R 527 |
Fainplast Compounds RI 54 Rigid PVC, Injection Molding Fittings for building trade - high fluidity |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO R 527 |
Fainplast Compounds RI 55 Rigid PVC, Injection Molding Fittings for building trade - high fluidity |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | 50 mm/min; ASTM D638 |
Lavergne VYTEEN ABS 2904 Acrylonitrile Butadiene Styrene Vyteen ABS 2904 is a black recycled ABS high impact flow terpolymer with balanced impact/stiffness properties designed for injection molding applications.Features: -Excellent resilience -Good proc.. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | after 7days @136°C; UL 1581 |
SABIC Innovative Plastics NORYL WCA105 PPE-TPE (Europe-Africa-Middle East) Flexible, non-halogenated FR mPPE extrusion grade ideal for evaluation in applications such as wire insulation. Flame retardant performance capable of meeting VW1 and 105C temperature rating requir.. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 364 PBT (Asia Pacific) Designed for outdoor telecommunications enclosure applications. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON WS002I PBT (Asia Pacific) LNP* Stat-kon* WS002I is a compound based on Polybutylene Terephalate resin containing Stainless Steel. Added features of this material include: Electrically Conductive, High Impact. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP WBL36L PBT LNP* LUBRICOMP* WBL36L is a compound based on PBT resin containing 30% Glass Bead, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP WBL36L PBT (Asia Pacific) LNP* Lubricomp* WBL36L is a compound based on Polybutylene Terephalate resin containing Glass Bead, PTFE. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY K3000SZ Acetal Copoly LNP* STAT-LOY* K3000SZ is a compound based on Acetal Copolymer resin. Added feature of this material is: AntiSstatic. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP MC002 PP LNP* THERMOCOMP* MC002 is a compound based on Polypropylene resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | Crosshead speed 100 mm/min; ISO 527 |
SCG Chemicals EL-Leneâ„¢ H1000PYL High Density Polyethylene Pipe Resin Key Characteristics: Good processing, high thermal stability, good resistance to weatheringRecommended Applications: Stripe lines for PE100 pipe, non pressure pipesCertification: Certified by LNE.. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | ASTM D638 |
Total PS CPDS 856S Chlorine and Bromine Free Flame Retardant High Impact Polystyrene Total Petrochemicals Polystyrene 856S is a chlorine and bromine free flame retardant high impact polystyrene with excellent thermal stability and processability for injection molding.Suitable Applic.. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO 527-3/5/500 |
Lubrizol Estane® 54611 Polyester-Based Thermoplastic Polyurethane Feature: Facilitates to produce high coating weight in one pass high production speed. Broad process window and transparent spherical pellets.Uses: Melt roll coated fabrics and unsupported foils.Av.. |
|||
Tensile Strength at Break | 36.0 MPa @Temperature 23.0 °C |
5220 psi @Temperature 73.4 °F |
DAM; ISO 527 |
DuPont Performance Polymers Zytel® FN718 BK230A Nylon 66
(Unverified Data**) Zytel® FN718 BK230A is a flexible, plasticizer free modified black polyamide 66 resin having good heat aging and chemical resistance.Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO R 527 |
Fainplast Compounds RE 121 Rigid PVC, Extrusion Electric pipes |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | ASTM-D638 |
Braskem GP100OR HDPE High Density Extrusion Polyethylene GP100OR is a high-density polyethylene compound specially developed for the manufacturing of extruded pipes for gas distribution. It is produced with bimodal technology and has high molar mass. It s.. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | ASTM D638 |
Asahi Glass Fluon® P-65P PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
Tensile Strength at Break | 36.0 MPa | 5220 psi | |
AorTech Biomaterials ECSil™ 60D Biomedical Carbonate Silicone Pellets Elast-Eon™ Carbonate Silicone (ECSil™) is a family of next generation biomedical polymers. ECSil™ is finding strong interest in cardiac pacing leads, orthopaedics, spinal discs, and generally an.. |