Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 34.5 MPa | 5000 psi | 2 in/min; ASTM D638 |
RheTech Products P100-01 Polypropylene Homopolymer, Black Applications: Wire harnessesTrim componentsUnderhood applicationsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | 2 in/min; ASTM D638 |
RheTech Products P104-00 Polypropylene, Natural Applications: Consumer goodsIP structural componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | >= 34.5 MPa | >= 5000 psi | Cured |
Resin Technology Group CT-523LV Cationic UV Cure Epoxy Adhesive CT-523-LV is an epoxy-based, low viscosity, cationic-curable adhesive and/or sealant. This product is activated by exposure to medium intensity UV radiation resulting in a high strength, chemical re.. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | ASTM D638 |
Polymer Resources PPX-GP4 Modified PPO, General Purpose with HDT of 210 F
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | ASTM D638 |
Albis Plastics Cellulose Acetate Propionate CP801 (UV Inhibitor Added), 13% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Propionate (CAP)Characteristics: Strength, Hardness, Stiffness, Weatherability and Dimensional StabilityApplications: Brush Handles, Safety Glasses, Optical Products and .. |
|||
Tensile Strength at Break | >= 34.5 MPa @Temperature 23.9 °C |
>= 5000 psi @Temperature 75.0 °F |
|
Master Bond UV15LV One Component, UV Curable Epoxy Based System Product Description: Master Bond UV15LV is a high strength, low viscosity, epoxy based UV curable system for bonding, sealing and coating. It has low viscosity and it is widely used in a variety of .. |
|||
Tensile Strength at Break | >= 34.5 MPa | >= 5000 psi | |
Master Bond EP3HTS Silver Filled, Electrically Conductive Epoxy Description: Master Bond Polymer System EP3HTS is a one component, silver filled, electrically conductive epoxy system featuring high shear strength and good temperature resistance along with a fast.. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | film; ASTM D882 |
Total HDPE 6480 High Density Polyethylene, Clarity Cast Film Resin Polyethylene: Clarity High Density Cast Film ResinCharacteristics:High stiffnessHigh clarityExcellent surface glossHigh tensile strengthGood barrier propertiesLow gel contentApplications:OverwrapFo.. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | vs. rigid PVC; 5 s set time |
Elmer's Products Aron Alpha® 101 Cyanoacrylate Adhesive (Industrial Krazy Glue™) Superior tensile and shear strengths, well suited for metal bondingLow gap fill. Methyl base monomer. Excellent on rubber/plastic substrates. Excellent on metal substrates. Poor on porous substr.. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | vs. rigid PVC; 5 s set time |
Elmer's Products Aron Alpha® 201 Cyanoacrylate Adhesive (Industrial Krazy Glue™) General purpose adhesive for a variety of applications. Various viscosities and gap filling properties available.Low gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on.. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | vs. rigid PVC; 25 s set time |
Elmer's Products Aron Alpha® 203 Cyanoacrylate Adhesive (Industrial Krazy Glue™) General purpose adhesive for a variety of applications. Various viscosities and gap filling properties available.High gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair o.. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | vs. polycarbonate; 100 s set time |
Elmer's Products Aron Alpha® 203 Cyanoacrylate Adhesive (Industrial Krazy Glue™) General purpose adhesive for a variety of applications. Various viscosities and gap filling properties available.High gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair o.. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | vs. rigid PVC; 3 s set time |
Elmer's Products Aron Alpha® 212E Cyanoacrylate Adhesive (Industrial Krazy Glue™) For clean, fast applications. Best for high speed automated assembly.Medium gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on metal substrates. Excellent on porous s.. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | vs. polycarbonate; 3 s set time |
Elmer's Products Aron Alpha® 231F Cyanoacrylate Adhesive (Industrial Krazy Glue™) Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on.. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | vs. polycarbonate; 20 s set time |
Elmer's Products Aron Alpha® 241F Cyanoacrylate Adhesive (Industrial Krazy Glue™) Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on.. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | vs. rigid PVC; 5 s set time |
Elmer's Products Aron Alpha® 401X Cyanoacrylate Adhesive (Industrial Krazy Glue™) Engineered for high temperature and high impact resistance.Low gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Excellent on metal substrates. Poor on porous substrates. Ve.. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | vs. rigid PVC; 25 s set time |
Elmer's Products Aron Alpha® 403X Cyanoacrylate Adhesive (Industrial Krazy Glue™) Engineered for high temperature and high impact resistance.High gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Excellent on metal substrates. Poor on porous substrates. V.. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | vs. polycarbonate; 100 s set time |
Elmer's Products Aron Alpha® 403X Cyanoacrylate Adhesive (Industrial Krazy Glue™) Engineered for high temperature and high impact resistance.High gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Excellent on metal substrates. Poor on porous substrates. V.. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | vs. polycarbonate; 10 s set time |
Elmer's Products Aron Alpha® 241E Cyanoacrylate Adhesive (Industrial Krazy Glue™) For clean, fast applications. Best for high speed automated assembly.Low gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on metal substrates. Excellent on porous subs.. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | vs. polycarbonate; 10 s set time |
Elmer's Products Aron Alpha® 252E Cyanoacrylate Adhesive (Industrial Krazy Glue™) For clean, fast applications. Best for high speed automated assembly.High gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on metal substrates. Excellent on porous sub.. |
|||
Tensile Strength at Break | 34.5 - 75.8 MPa | 5000 - 11000 psi | Compared to 300 for concrete |
Abatron AboJet Structural Crack-Injection Resin Structural crack injection resin for foundations, dikes, columns, load-bearing walls and structures. Offers strength, performance, durability, cost effectiveness and restoration instead of demoliti.. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | ASTM D638 |
Albis Plastics Cellulose Acetate Butyrate B908 , 13% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
Tensile Strength at Break | 34.5 MPa | 5000 psi | ASTM D638 |
Albis Plastics Cellulose Acetate Propionate CP800 (Base Grade), 13% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Propionate (CAP)Characteristics: Strength, Hardness, Stiffness, Weatherability and Dimensional StabilityApplications: Brush Handles, Safety Glasses, Optical Products and .. |