Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 34.0 MPa | 4930 psi | |
Plastcom SLOVALEN PH 78 T 40 PP, 40% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 40% microground, floated, chemically modified talc. Stable towards detergents. General application in all industry branches.. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Cycolac® MG8000SR ABS This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics GELOY CR7020 ASA (Asia Pacific) ASA copolymer. Profile/sheet coextrusion over ABS. Excellent weatherability, good flow/aesthetics and high impact. |
|||
Tensile Strength at Break | <= 34.0 MPa | <= 4930 psi | ISO/R527 |
Polykemi AB POLYfill PPH T15020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 34.0 MPa | <= 4930 psi | ISO/R527 |
Polykemi AB POLYfill PPH T16020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics GELOY CR7520 ASA General purpose ASA. Excellent weatherability, good flow/aesthetics and high impact. Rated F2 by UL. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | ISO R 527 |
Fainplast Compounds RK 115 Rigid PVC, Extrusion Lead Free Small tubes for shoes |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | ISO R 527 |
Fainplast Compounds RK 316 Rigid PVC, Extrusion Lead Free Indoor profiles |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | ISO 37 |
Huntsman AVALON® 98 AE Thermoplastic Polyurethane Introduction: AVALON 98 AE is a general purpose polyester based thermoplastic polyurethane for injection molding. AVALON 98 AE is part of the AVALON Perform Range and offers a premium soiling materi.. |
|||
Tensile Strength at Break | 34.0 MPa @Temperature 23.0 °C |
4930 psi @Temperature 73.4 °F |
50-mm/min; ISO 527 |
Ineos ABS Lustran® Guardian™ 682 ABS, Injection Molding Grade Lustran® ABS 682 is a high performance, HCFC-141b resistant grade of ABS for injection molded refrigerator and freezer components. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | ISO 37 |
Huntsman AVALON® 92 AB Thermoplastic Polyurethane Introduction: AVALON 92 AB is a high performance polyester based thermoplastic polyurethane for injection molding. AVALON 92 AB is part of the AVALON Performance Range and offers a premium soling ma.. |
|||
Tensile Strength at Break | 34.0 MPa @Temperature 23.0 °C |
4930 psi @Temperature 73.4 °F |
50mm/min; ISO 527-2/1A/50 |
SYNTHOS Forsan® 573 Acrylonitrile Butadiene Styrene (ABS) Increased heat resistant, glossy, good mechanical properties, suitable for electroplating.Applications: Electrotechnics, automotiveHousehold appliances, electric switches, car interior parts, profil.. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Lubricomp KZL34 POM LNP* Lubricomp* KZL34 is a compound based on Acetal resin containing Milled Glass and PTFE. Characteristic of this grade is Internally Lubricated.This data was supplied by SABIC-IP for the Americas.. |
|||
Tensile Strength at Break | >= 34.0 MPa | >= 4930 psi | ISO R 527 |
Stir SpA Giesse RJA/9 (PVC) Application: Injection moldingInformation provided by STIR SpA |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp FF008L PE LNP* Thermocomp* FF008L is a compounding based on Polyethylene containing glass fiber. Added characteristics include Low Extractible.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL PPX PPX7112 PPE+PP (Europe-Africa-Middle East) PPE+PP blend. Suitable for painted exterior automotive applications. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PPX PPX7115 PPE+PP High modulus/impact/heat PPE+PP |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP MF002AS PP LNP THERMOCOMP* MF002AS is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | 67% Ret. |
UBE UBESTA® 3030U Nylon 12 (After Ethanol for 1000 hours) Description: UBESTA has a strong resistance to chemicals. Under normal conditions, it is not significantly affected by alkalis, alcohols, ethers, ketones, hydrocarbons, lubricating oils, gasoline, c.. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | ISO 527 |
Unitika TERRAMAC TE-1070 Polylactic Acid (PLA) High-Impact grade, Injection grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | ASTM D638 |
Eastman Tenite 572E3720012 Cellulose Acetate Butyrate, Clear, Trsp Applications:FilmsProfilesSheetProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a wa.. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® BM-30 FR PA6-MD30 FR Information provided by EMS Grivory |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | |
AorTech Biomaterials ECSil™ 90A Biomedical Carbonate Silicone Pellets Elast-Eon™ Carbonate Silicone (ECSil™) is a family of next generation biomedical polymers. ECSil™ is finding strong interest in cardiac pacing leads, orthopaedics, spinal discs, and generally an.. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Sintered Sheet; DIN EN ISO 527-3 |
3M Dyneon™ TFM™ 2001Z PTFE Dyneon™ TFM™ 2001 Z PTFE is an ideal grade for high-performance applications with reduction ratios up to 1000:1. This product has a denser polymer texture providing lower gas permeability than sta.. |
|||
Tensile Strength at Break | 34.0 - 55.0 MPa | 4930 - 7980 psi | ASTM D638 |
Arkema Group KYNAR® 760 Polyvinylidene Fluoride Homopolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili.. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | ASTM D1457 |
Asahi Glass Fluon® CD090 PTFE Coagulated Dispersion Powder Fluon®PTFE coagulated dispersion powders (fine powders) are used for paste extrusion to make tapes, tubes, rods and wire coatings.Information provided by Asahi Glass Company, Inc. |
|||
Tensile Strength at Break | 34.0 - 40.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
4930 - 5800 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 60512 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 60512 PVDF copolymer has high viscosity of the melt and it is a grade for offshore piping.Information provided by Solvay Specialty Polymers. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Sintered Molding; DIN 53455 (film, 0.2mm) |
3M Dyneon™ TFM™ 1630 PTFE
(discontinued **) Semi-free-flowing resin for convenient handlingHigh bulk density leading to more economical processingVery dense polymer structure; low permeabilityGood electrical and mechanical propertiesSmoother .. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | Sintered Molding; DIN 53455 (film, 0.2 mm) |
3M Dyneon™ TFM™ X 1630 PTFE
(discontinued **) Semi-free-flowing resin for convenient handlingHigh bulk density leading to more economical processingVery dense polymer structure; low permeabilityGood electrical and mechanical propertiesSmoother .. |
|||
Tensile Strength at Break | 34.0 MPa | 4930 psi | ASTM D638 |
Azdel SuperLite® SL551400-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness) AZDEL SuperLite® SL551400-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |