Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 29.6 MPa | 4300 psi | 2 in/min; ASTM D638 |
RheTech Products RCT120-01 20% Talc Reinforced Polypropylene, Black, Recycled Content Applications: HVAC and I/P ComponentsUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 29.6 MPa | 4300 psi | 2 in/min; ASTM D638 |
RheTech Products T40P100-01 40% Talc Reinforced Polypropylene, Black Applications: Wire troughBracketsConsolesFan shroudsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 29.6 MPa | 4300 psi | 2 in/min; ASTM D638 |
RheTech Products T40P105-01 40% Talc Reinforced Polypropylene, Black Applications: Underhood componentsHVAC ductworkInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 29.6 MPa | 4300 psi | 2 in/min; ASTM D638 |
RheTech Products T40P106-01 40% Talc Reinforced Polypropylene, Black Applications: Underhood componentsHVAC ductworkFunctional supportsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 29.6 MPa | 4300 psi | 50 mm/min; ASTM D638 |
LyondellBasell Alathon® H6017 High Density Polyethylene, Injection Molding Grade ALATHON H6017 provides good processing characteristics and exhibits excellent toughness and color as well as low odor and good molded-part stability. Typical applications include housewares, caps, c.. |
|||
Tensile Strength at Break | 29.6 MPa @Temperature 316 °C |
4300 psi @Temperature 600 °F |
|
Greene Tweed Arlon® 1000 Polyketone Arlon® is a tough, high-temperature, semi-crystalline, thermoplastic presenting a unique combination of mechanical, thermal, chemical and electrical properties. Greene, Tweed uses several proprie.. |
|||
Tensile Strength at Break | 29.6 MPa | 4300 psi | ASTM D638 |
ITW Devcon Metal Repair Wear Resistant Epoxy (WR-2), Dark Grey Information provided by ITW Devcon |
|||
Tensile Strength at Break | 29.6 MPa | 4300 psi | ASTM D 638 |
LyondellBasell Hifaxâ„¢ AA36H Polypropylene Homopolymer Description: Hifaxâ„¢ AA36H conventional melt flow, 1,400 MPa flexural modulus, UL 94 V-2 flame retardant polypropylene homopolymer resin has an excellent combination of properties and processabi.. |
|||
Tensile Strength at Break | 29.6 MPa | 4300 psi | ASTM D638 |
Plastics Group Polifil® C-10 10% Calcium Carbonate-Reinforced Polypropylene Polifil® C series compounds are homopolymer polypropylene resins reinforced with fine particle size calcium carbonate. They combine high impact with stiffness, heat aging, good colorability, resist.. |
|||
Tensile Strength at Break | 29.6 MPa | 4300 psi | ASTM D638 |
Chesterton ARC MXHT High temperature severe wear compound Description: An advanced ceramic composite for the protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack at elevated temperatures. It is applied at a thickness o.. |
|||
Tensile Strength at Break | 29.6 MPa | 4300 psi | vs. steel; 20 s set time |
Elmer's Products Aron Alpha® GEL 10 Cyanoacrylate Adhesive (Industrial Krazy Glue™) Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on.. |
|||
Tensile Strength at Break | 29.6 MPa | 4300 psi | vs. rigid PVC; 30 s set time |
Elmer's Products Aron Alpha® 403T Cyanoacrylate Adhesive (Industrial Krazy Glue™) Extra tough adhesives with highest heat, peeling, impact and thermal shock resistance.High gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Excellent on metal substrates. Fa.. |
|||
Tensile Strength at Break | 29.6 MPa | 4300 psi | ASTM D3756 |
3M 101+ Value Masking Tape 3M™ Value Masking Tape 101+ is a tan colored crepe paper masking tape for holding, bundling, sealing, and non-critical masking applications where a pressure sensitive tape is needed.Information pro.. |
|||
Tensile Strength at Break | 29.6 MPa | 4300 psi | ASTM D3759 |
3M 2308 Performance Masking Tape Scotch® Performance Masking Tape 2308 is general purpose masking tape for holding, bundling, sealing, general paint masking and a vast number of other jobs where a pressure-sensitive tape is needed.. |
|||
Tensile Strength at Break | 29.6 MPa | 4300 psi | ASTM D638 |
Americas Styrenics STYRON® 498 High Impact Polystyrene Product CharacteristicsHigh glossHigh impactFood Contact CompliantUL Classification 94HBTypical ApplicationsAppliancesMedicalHousewaresConsumer electronicsInformation provided by AmericasStyrenics L.. |
|||
Tensile Strength at Break | 29.6 MPa | 4290 psi | ASTM D638 |
Albis Plastics Cellulose Acetate CA700 , Unreinforced, 33% Plasticizer
(discontinued **) Amorphous Cellulose Acetate (CA)Characteristics: Chemical Resistance, Toughness, Strength, Hardness, Gloss, Clarity and "Feel"Applications: Tool Handles, Optical Products, Toys and Sheet ProductsPro.. |
|||
Tensile Strength at Break | 29.6 MPa | 4290 psi | ASTM D638 |
Albis Plastics Cellulose Acetate CA700 , Unreinforced, 35% Plasticizer
(discontinued **) Amorphous Cellulose Acetate (CA)Characteristics: Chemical Resistance, Toughness, Strength, Hardness, Gloss, Clarity and "Feel"Applications: Tool Handles, Optical Products, Toys and Sheet ProductsPro.. |
|||
Tensile Strength at Break | 29.6 MPa | 4300 psi | ASTM D638 |
PlastxWorld DAICEL STYROL® GW30 HIPS UV stable flame retarded HIPSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |