Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 228 MPa | 33100 psi | ASTM D638 |
PolyOne Stat-Tech™ NN-30CF/000 Black Polyamide 66 (Nylon 66) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound.. |
|||
Tensile Strength at Break | 228 MPa | 33100 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ GF 1200 60 HS Black 22 Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil.. |
|||
Tensile Strength at Break | 228 MPa | 33100 psi | ASTM D638 |
LNP Thermocomp® LC-1006 EM Polyetheretherketone, Carbon Fiber Reinforcement
(discontinued **) Features: Good MoldabilityForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are st.. |
|||
Tensile Strength at Break | 228 MPa | 33100 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RCP36 PA 66 LNP LUBRICOMP* RCP36 is a compound based on Nylon 66 resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this material include: Electrically Conductive, Wear Resistant. |
|||
Tensile Strength at Break | 228 MPa | 33100 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RCP36 PA 66 (Asia Pacific) LNP LUBRICOMP* RCP36 is a compound based on Nylon 66 resin containing Silicone, PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 228 MPa | 33100 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RCP36 PA 66 (Europe-Africa-Middle East) LNP LUBRICOMP* RCP36 is a compound based on Nylon 66 resin containing Carbon Fiber, Silicone, PTFE. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 228 MPa | 33100 psi | ASTM D638 |
Solvay Specialty Polymers Amodel® AS-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Conditioned) Amodel® AS-1145 HS is a 45% glass reinforced heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater tha.. |
|||
Tensile Strength at Break | 228 MPa | 33100 psi | ASTM D638 |
Solvay Specialty Polymers Amodel® AS-4145 HS Polyphthalamide (PPA), 45% Glass Fiber (Dry) Amodel® AS-4145 HS polyphthalamide (PPA) is a 45% glass reinforced resin that is hot-water moldable. Key properties include high heat resistance, high strength and stiffness over a broad tempera.. |
|||
Tensile Strength at Break | 228 MPa | 33100 psi | ISO 527 |
SABIC Innovative Plastics LNP Thermocomp LC006E PEEK LNP THERMOCOMP* LC006E is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Am.. |
|||
Tensile Strength at Break | 228 MPa | 33100 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON RE0069S PA 66 (Asia Pacific) LNP* STAT-KON* RE0069S is a compound based on Nylon 66 resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Heat Stabil.. |
|||
Tensile Strength at Break | 228 MPa | 33100 psi | ISO 527 |
SABIC Innovative Plastics LNP VERTON RVL28 PA 66 LNP* VERTON* RVL28 is a compound based on Nylon 66 resin containing 40% Long Glass Fiber, 10% PTFE. Added features of this material include: Easy Molding, Heat Stabilized, Wear Resistant, Structura.. |
|||
Tensile Strength at Break | 228 MPa | 33100 psi | Conditioned; ASTM D638 |
Solvay Specialty Polymers Amodel® AS-1145 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AS-1145 HS is a 45% glass reinforced heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0... |
|||
Tensile Strength at Break | 228 MPa | 33100 psi | ASTM D638 |
Solvay Specialty Polymers Amodel® AS-4145 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AS-4145 HS polyphthalamide (PPA) is a 45% glass reinforced resin that is hot-water moldable. Key properties include high heat resistance, high strength and stiffness over a broad temperature.. |
|||
Tensile Strength at Break | 228 MPa | 33100 psi | ASTM D638 |
SABIC Innovative Plastics LNP VERTON PX06419 PA 6 LNP* VERTON* PX06419 is a compound based on Nylon 6 resin containing Proprietary Fillers. Added features of this material include: Heat Stabilized, Structural. |
|||
Tensile Strength at Break | 228 MPa | 33100 psi | ASTM D638 |
SABIC Innovative Plastics LNP VERTON PX06419 PA 6 (Asia Pacific) LNP* Verton* PX06419 is a compound based on Nylon 6 resin containing Long Glass Fiber. Added features of this material include: Heat Stabilized. |