Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 22.0 MPa | 3190 psi | 50 mm/min; ISO 527 |
Polimeri Europa Edistir RK 451G Polystyrene UL94 V-0, polybromobiphenylether (PBBE) free, flame retarded, high impact polystyrene. This grade combines medium flow, heat resistance and good light stability for injection moulding of technical p.. |
|||
Tensile Strength at Break | <= 22.0 MPa | <= 3190 psi | ISO/R527 |
Polykemi AB POLYfill PP EIP5025 F VT2 Polypropylene, Mineral Reinforced, Extrusion grade, Low CLTE Information provided by Polykemi AB |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP CBL36XXC PS (Asia Pacific) LNP* Lubricomp* CBL36XXC is a compound based on Polystyrene resin containing Glass Bead, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | ASTM D638 |
SABIC M40060 Series High Density Polyethylene for Injection Molding Product Description: M40060 is a high density polyethylene grade with a narrow molecular weight distribution suitable for injection molding applications. It has been designed to provide good rigid.. |
|||
Tensile Strength at Break | <= 22.0 MPa | <= 3190 psi | ISO/R527 |
Polykemi AB POLYfill PPH K20040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | |
JPJ Technologies 6380M HDPE Extrusion Information provided by JPJ Technologies |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | |
JPJ Technologies 7300M HDPE Extrusion Information provided by JPJ Technologies |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | ISO 37 |
Huntsman AVALON® 70 AE Thermoplastic Polyurethane Introduction: AVALON 70 AE is a general purpose polyester based thermoplastic polyurethane for injection molding. AVALON 70 AE is part of the AVALON Soft Range and offers a premium soiling material .. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL WCA901 PPE-TPE (Asia Pacific) Non-Halogenated flame retardant, flexible Noryl resin intended for evaluation in wire and cable applications, capable of meeting VW-1 and 105°C end use temperature requirements as defined by UL.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Lubricomp ML002S PP LNP* Lubricomp* ML002S is a compound based on Polypropylene containing PTFE. Characteristics of this grade are: Heat Stabilized and Internally Lubricated.This data was supplied by SABIC-IP for the.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP ML004LS PP LNP* LUBRICOMP* ML004LS is a compound based on Polypropylene resin containing 20% PTFE. Added features of this matLNP* Lubricomp* ML004LS is a compound based on Polypropylene resin containing PTFE... |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP YL003C Polyester Elastomer LUBRICOMP* YL003C is a compound based on Polyester Elastomer resin containing 15% PTFE. Added features of this grade include: Clean Compound System, Wear Resistant. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON MX01767C PP LNP* STAT-KON* MX01767C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System. |
|||
Tensile Strength at Break | >= 22.0 MPa | >= 3190 psi | |
Sibur SKS-30 ARKM-27 1st Group Oil-Filled Styrene-Butadiene Rubber SBR 1712. For use in the tire industry for production of tire thread and other parts for tires, in the rubber technical industry for production of a wide assortment of rubber technical articles, an.. |
|||
Tensile Strength at Break | 22.0 MPa @Temperature 23.0 °C |
3190 psi @Temperature 73.4 °F |
50mm/min; ISO 527-2/1A/50 |
SYNTHOS Krasten® FB28 High Impact Polystyrene And Polyethylene Blend Polymer blend HIPS/PE. High toughness, very good tensile properties and environmental stress cracking resistance. Processed mainly by extrusion and thermoforming. Production of sheets and films, tec.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 25mm/min; ISO 527 |
Borealis LE0592 Polyethylene LE0592 is a crosslinkable black polyethylene compound, specially designed for bonded semi conductive screen applications. Applications: LE0592 is intended for semi conductive applications in XLPE m.. |
|||
Tensile Strength at Break | >= 22.0 MPa | >= 3190 psi | 25mm/min; ISO 527 |
Borealis Supersmooth™ LE0592S Polyethylene Supersmooth™ LE0592S is a crosslinkable black polyethylene compound, specially designed for bonded semiconductive screen applications. Supersmooth™ LE0592S is intended for semiconductive applicat.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | ASTM D638 |
Eastman Eastman AP006 Copolyester Applications:Automotive componentsBreathable filmsElectrical/electronic componentsFilm ModificationFlexible hingesHose mandrelIndustrial componentsIndustrial hoses/beltsOffice furniturePackagingPoly.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | ASTM D 638 |
Cossa Polimeri ESTAPROP HK 2540 T8 Polypropylene, 20% Mineral Filled PP homo/copolymer 20% mineral fillerGood physical and mechanical propertiesInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | ASTM D 638 |
Cossa Polimeri ESTASTIR HI 10 V0 Flame Retardant Polystyrene Flame retardant class V0, with PBDE, for injection molding or extrusionInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | |
Daikin DAI-EL G-801 Fluoroelastomer Copolymer, Peroxide Curable Grade, 66% Fluorine Content Offers excellent chemical and steam resistance. Offers good mechanical characteristics.Features: Good low-temperature and elasticity characteristics.Information provided by Daikin Industries. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | |
Daikin DAI-EL G-901 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 71% Fluorine Content Offers excellent chemical and steam resistance. Offers good mechanical characteristics.Features: Excellent solvent resistance.Information provided by Daikin Industries. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | |
Daikin DAI-EL G-902 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 71% Fluorine Content Offers excellent chemical and steam resistance. Offers good mechanical characteristics.Features: Excellent solvent resistance, good mold flow.Information provided by Daikin Industries. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 50mm/min; ASTM D638 |
3M Dyneon™ PVDF 31508/0003 Polyvinylidene Fluoride 3M™ Dyneon™ PVDF 31508/0003 is a flexible copolymer of VF2 and CTFE, exhibiting very low shrinkage and excellent impact resistance. PVDF 31508/0003 also has a very low brittleness temperature, for.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | Film Property, 50 µm thickness; ASTM D882 |
Arkema Group OREVAC® 9309 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | ISO 527-1 |
Barlog Plastics KEBAFLEX E D 50.1 TPE-V, Shore D50 TPE-VInformation provided by BARLOG plastics GmbH. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 50mm/min; ASTM D638 |
3M Dyneon™ PVDF 32008/0003 Polyvinylidene Fluoride
(discontinued **) Copolymer of VF2 and CTFEUltra-flexibleVery low shrinkage ratesWide operating temperature windowProcessable using a variety of thermoplastic conversion techniquesExcellent low flame and low smoke pe.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 50mm/min; ASTM D638 |
3M Dyneon™ PVDF 31508/0009 Polyvinylidene Fluoride 3M™ Dyneon™ PVDF 31508/0009 is a flexible copolymer of VF2 and CTFE, exhibiting very low shrinkage and excellent impact resistance. Dyneon PVDF 31508/0009 also has a very low brittleness temperatu.. |
|||
Tensile Strength at Break | 22.0 MPa | 3190 psi | 50mm/min; ASTM D638 |
3M Dyneon™ PVDF 31008/0009 Polyvinylidene Fluoride
(discontinued **) Copolymer of VF2 and CTFEUltra-flexibleVery low shrinkage ratesWide operating temperature windowProcessable using a variety of thermoplastic conversation techniquesExcellent low flame and low smoke .. |