Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 2.41 MPa | 350 psi | Reinforced Material - Fill; ASTM D412 |
Parker Chomerics CHO-SEAL 1285R Reinforced Conductive Elastomer Seal These materials are fabric-reinforced, silver-plated-aluminum filled EMI seals for airframe shielding applications. These seal materials can also be used to maintain surface electrical continuity at.. |
|||
Tensile Strength at Break | 2.41 MPa | 350 psi | Reinforced Material - Fill; ASTM D412 |
Parker Chomerics CHO-SEAL 1287R Reinforced Conductive Elastomer Seal These materials are fabric-reinforced, silver-plated-aluminum filled EMI seals for airframe shielding applications. These seal materials can also be used to maintain surface electrical continuity at.. |
|||
Tensile Strength at Break | 2.41 MPa | 350 psi | |
Zircar Zirconia Buster M-35 Alumina Board, Disc, and Cylinder Insulation Zircar alumina insulation Type Buster is a rigid, fibrous ceramic material produced by vacuum forming alumina fibers with either a high purity alumina binder in BusterA-30 for use at 1600C or with s.. |
|||
Tensile Strength at Break | 2.41 MPa | 350 psi | ASTM D412 |
Teknor Apex Monprene® MP-2238-R Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 2.41 MPa | 350 psi | ASTM D412 |
Teknor Apex Monprene® MP-2315 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 2.41 MPa | 350 psi | ASTM D412 |
Teknor Apex Monprene® MP 1672 Thermoplastic Elastomer Features: Monprene® TPE gels are softer than the shore A range of hardness. Monprene® TPE gels are high strength and high flow elastomers that may be used in the overmolding processes on poly.. |
|||
Tensile Strength at Break | 2.41 MPa | 350 psi | |
Zircar Zirconia Buster M-35 Alumina Board, Disc, and Cylinder Insulation Zircar alumina insulation Type Buster is a rigid, fibrous ceramic material produced by vacuum forming alumina fibers with either a high purity alumina binder in BusterA-30 for use at 1600C or with s.. |
|||
Tensile Strength at Break | 2.41 MPa | 350 psi | Standard Cure - 14 days |
3M AC-236 Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-236 Class B are two-component, manganese dioxide cured, liquid polysulfide polymer system providing excellent fuel tank and fuselage seals. They have outstanding resistance t.. |
|||
Tensile Strength at Break | 2.41 MPa | 350 psi | Standard Cure - 14 days |
3M AC-236 Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-236 Class B are two-component, manganese dioxide cured, liquid polysulfide polymer system providing excellent fuel tank and fuselage seals. They have outstanding resistance t.. |
|||
Tensile Strength at Break | 2.41 MPa @Time 1.21e+6 sec |
350 psi @Time 336 hour |
Standard Cure |
3M AC-251 Black Class B-1 Aerospace Sealant 3M Aerospace Sealant AC-251 Black Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate ai.. |
|||
Tensile Strength at Break | 2.41 MPa @Time 1.21e+6 sec |
350 psi @Time 336 hour |
Standard Cure |
3M AC-251 Black Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-251 Black Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate ai.. |
|||
Tensile Strength at Break | 2.41 MPa @Time 1.21e+6 sec |
350 psi @Time 336 hour |
Standard Cure |
3M AC-251 Black Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-251 Black Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate ai.. |
|||
Tensile Strength at Break | 2.41 MPa @Time 1.21e+6 sec |
350 psi @Time 336 hour |
Standard Cure |
3M AC-251 Gray Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-251 Gray Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate air.. |
|||
Tensile Strength at Break | 2.41 MPa @Time 1.21e+6 sec |
350 psi @Time 336 hour |
Standard Cure |
3M AC-251 Gray Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-251 Gray Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate air.. |
|||
Tensile Strength at Break | 2.41 MPa | 350 psi | Standard Cure - 14 days; AMS3276 |
3M AC-275 Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-275 Class B is a high temperature two-component manganese dioxide cured, liquid polysulfide polymer sealants providing excellent fuel tank and fuselage seals. They have outst.. |
|||
Tensile Strength at Break | 2.41 MPa | 350 psi | Standard Cure - 14 days; AMS3276 |
3M AC-275 Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-275 Class B is a high temperature two-component manganese dioxide cured, liquid polysulfide polymer sealants providing excellent fuel tank and fuselage seals. They have outst.. |
|||
Tensile Strength at Break | 2.41 MPa | 350 psi | Standard Cure - 14 days; AMS3276 |
3M AC-275 Class B-4 Aerospace Sealant 3M Aerospace Sealant AC-275 Class B is a high temperature two-component manganese dioxide cured, liquid polysulfide polymer sealants providing excellent fuel tank and fuselage seals. They have outst.. |
|||
Tensile Strength at Break | 2.41 MPa | 350 psi | Standard Heat Cycle +JRF - 7 days @ 60°C |
3M AC-350 Class A-1 Aerospace Sealant 3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have.. |
|||
Tensile Strength at Break | 2.41 MPa @Temperature 182 °C, Time 28800 sec |
350 psi @Temperature 360 °F, Time 8.00 hour |
|
3M AC-350 Class A-1 Aerospace Sealant 3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have.. |
|||
Tensile Strength at Break | 2.41 MPa | 350 psi | Standard Heat Cycle +JRF - 7 days @ 60°C |
3M AC-350 Class A-1/2 Aerospace Sealant 3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have.. |
|||
Tensile Strength at Break | 2.41 MPa @Temperature 182 °C, Time 28800 sec |
350 psi @Temperature 360 °F, Time 8.00 hour |
|
3M AC-350 Class A-1/2 Aerospace Sealant 3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have.. |
|||
Tensile Strength at Break | 2.41 MPa | 350 psi | Standard Heat Cycle +JRF - 7 days @ 60°C |
3M AC-350 Class A-2 Aerospace Sealant 3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have.. |
|||
Tensile Strength at Break | 2.41 MPa @Temperature 182 °C, Time 28800 sec |
350 psi @Temperature 360 °F, Time 8.00 hour |
|
3M AC-350 Class A-2 Aerospace Sealant 3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have.. |
|||
Tensile Strength at Break | 2.41 MPa | 350 psi | Standard Cure - 14 days |
3M AC-236 Class B-4 Aerospace Sealant 3M Aerospace Sealant AC-236 Class B are two-component, manganese dioxide cured, liquid polysulfide polymer system providing excellent fuel tank and fuselage seals. They have outstanding resistance t.. |