Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 2.07 MPa @Temperature 23.0 °C |
300 psi @Temperature 73.4 °F |
Die C2 hr; ASTM D412 |
PolyOne Versaflex™ CL2000X Thermoplastic Elastomer (TPE) Versaflex™ CL2000X is an ultra-soft TPE designed for use in injection molding applications where exceptional clarity and an extremely soft feel are desired. - Tactile Feel - Ultra-Soft - Water Clar.. |
|||
Tensile Strength at Break | >= 2.07 MPa | >= 300 psi | ASTM D412 |
Parker Chomerics CHO-SEAL 1224 Conductive Elastomer Highest shielding effectiveness and through conductivity performance; higher physical properties; excellent processing; also available in a fabric reinforced format.Molded onlyRoHS CompliantInformat.. |
|||
Tensile Strength at Break | 2.07 MPa @Temperature 23.0 °C |
300 psi @Temperature 73.4 °F |
Die C2 hr; ASTM D412 |
PolyOne Dynalloy™ 8900-30 Thermoplastic Elastomer (TPE) Dynalloy™ 8900-series is an innovative thermoplastic elastomer selection formulated to provide the injection molder with a product capable of overmolding and bonding to both low-density polyethylen.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | ASTM D1708 |
DuPont Elvax® 4310 Ethylene Vinyl Acetate
(discontinued **) DuPont™ Elvax® 4310 is an ethylene-vinyl acetate / acid terpolymer resin for use in industrial applications.Applications:Elvax® 4310 resins can be used for the following applications: adhesives, .. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | ASTM D412 |
Teknor Apex Monprene® MP 1231D Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | ASTM D412 |
Teknor Apex Monprene® MP-1545 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | ASTM D412 |
Teknor Apex Monprene® MP-1672A Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | ASTM D412 |
Teknor Apex Monprene® MP-1900 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | ASTM D412 |
Teknor Apex Monprene® MP-1900-R Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | ASTM D412 |
Teknor Apex Monprene® MP-2720 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | ASTM D412 |
Teknor Apex Uniprene® UN-2598E Thermoplastic Vulcanizate Alloy Notes: Injection Rate: Fast Uses: Expansion Joint; Grommets; Tubing; Gaskets; Plugs; Weatherstripping; Glazing; Shock Absorbing Pads Forms: Pellets Processing Method: Extrusion; Injection Molding Ex.. |
|||
Tensile Strength at Break | 2.07 - 2.76 MPa | 300 - 400 psi | |
Master Bond MasterSil 156 Two Part, Low Viscosity Silicone Description: Master Bond MasterSil 156 is a two component, lower viscosity silicone system for high performance potting, encapsulation and sealing. MasterSil 156 combines high temperature resistance.. |
|||
Tensile Strength at Break | 2.07 - 2.76 MPa | 300 - 400 psi | |
Master Bond MasterSil 708FR One Part, Flame Resistant Silicone Description: MasterSil 708FR is a one component, high performance RTV silicone that is mainly used for its flame retardancy. It is UL listed with a flame classification for 94V.1 for thicknesses of .. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | ASTM D638 |
ExxonMobil Escorene™ UL 7720 Ethylene Vinyl Acetate Copolymer Product Description: Escorene Ultra UL 7720 is a high flow, 27.6% VA copolymer that has very good compatibility with hydrocarbon and natural tackifiers and most waxes. It is suitable for making hot .. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | Standard Cure - 14 days |
3M AC-240 Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-240 Class B is a two-part, polysulfide-based, long application life, quick cure product for use as a sealant for integral fuel tanks and fuselages. This tow-component, mangan.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | Standard Cure - 14 days |
3M AC-240 Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-240 Class B is a two-part, polysulfide-based, long application life, quick cure product for use as a sealant for integral fuel tanks and fuselages. This tow-component, mangan.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | 7 days JRF |
3M AC-360 Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-360 Class B are fast cure, intermediate density two-component, manganese dioxide cure, polysulfide fuel tank and fuselage sealant. 3M AC-360 Class B Sealants have outstanding.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | 7 days JRF |
3M AC-360 Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-360 Class B are fast cure, intermediate density two-component, manganese dioxide cure, polysulfide fuel tank and fuselage sealant. 3M AC-360 Class B Sealants have outstanding.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | JRF 12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C |
3M AC-730 Class B-12 Aerospace Sealant 3M Aerospace Sealant AC-730 Class B are fast cure, two-part, manganese-cured, non-chromate containing corrosion inhabiting sealants. These Sealants provide an effective barrier against the common ca.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | JRF 12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C |
3M AC-730 Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-730 Class B are fast cure, two-part, manganese-cured, non-chromate containing corrosion inhabiting sealants. These Sealants provide an effective barrier against the common ca.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | JRF 12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C + Heat Cycle |
3M AC-730 Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-730 Class B are fast cure, two-part, manganese-cured, non-chromate containing corrosion inhabiting sealants. These Sealants provide an effective barrier against the common ca.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | JRF 12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C |
3M AC-730 Class B-6 Aerospace Sealant 3M Aerospace Sealant AC-730 Class B are fast cure, two-part, manganese-cured, non-chromate containing corrosion inhabiting sealants. These Sealants provide an effective barrier against the common ca.. |
|||
Tensile Strength at Break | 2.07 MPa @Temperature 25.0 °C, Time 259000 sec |
300 psi @Temperature 77.0 °F, Time 72.0 hour |
Cured |
ACC QM 107 QSI Quantum Silicones 7 Durometer Condensation Cure Moldmaking Material QM 107 is a two component, room temperature condensation cure silicone material. The cured rubber is very soft, has excellent mechanical properties and good shelf-life stability. This material is us.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | 50% RH |
3M 4200 Marine Adhesive/Sealant Fast Cure A fast curing, one-part polyurethane that chemically reacts with moisture to deliver strong, flexible bonds to wood, gelcoat and fiberglass. It forms watertight, weather-resistant seals on joints an.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | JRF 12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C |
3M AC-730 Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-730 Class B are fast cure, two-part, manganese-cured, non-chromate containing corrosion inhabiting sealants. These Sealants provide an effective barrier against the common ca.. |
|||
Tensile Strength at Break | 2.07 MPa | 300 psi | JRF 12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C + Heat Cycle |
3M AC-730 Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-730 Class B are fast cure, two-part, manganese-cured, non-chromate containing corrosion inhabiting sealants. These Sealants provide an effective barrier against the common ca.. |