Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 19.5 MPa | 2830 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible 90042 Polyvinyl Chloride, Flexible (PVC, Flexible) Automotive OEM approval(s).Information provided by PolyOne |
|||
Tensile Strength at Break | 19.5 MPa | 2830 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible 90072 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 19.5 MPa | 2830 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible 90071 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 19.5 MPa | 2830 psi | ASTM D412 |
Huntsman IROGRAN® PS 456-202 TPU-Polyester Polyester-based grades with a broad processing window ideally suited for cast, flat die and flown film lines.Information provided by Alliance Polymers |
|||
Tensile Strength at Break | 19.5 MPa | 2830 psi | AVG; ASTM D412 Method A |
Seals Eastern Perflas® 9294 Perfluorinated Rubber Perfluoro rubber for aggressive chemical service. Perflas ® 9294 seals are made of a chemical resistant perfluorinated fluoroelastomer (FFKM). Perflas 9294 seals offer outstanding resistance to.. |
|||
Tensile Strength at Break | >= 19.5 MPa | >= 2830 psi | |
Sibur SKD-ND 2nd Group Butadiene Rubber (BR) Buna CB 24. It is used in tires and the rubber and asbestos technical industries. It is combined with natural butadiene-styrene rubbers in any ratio, which is very important during production of a.. |
|||
Tensile Strength at Break | 19.5 MPa | 2830 psi | |
3M Scotchkote™ EG 515 Urethane Ceramic Rebuild Scotchkote Urethane Ceramic Rebuild EG 515 has been specifically developed as a 100% solids repair system with a degree of flexibility for rebuilding and resurfacing equipment operating in fluid flo.. |
|||
Tensile Strength at Break | 19.5 MPa | 2830 psi | |
3M Scotchkote™ FG 514 Urethane Ceramic Lining Scotchkote Urethane Ceramic Lining FG 514 has been specifically developed as a 100% solids polyceramic coating with a degree of flexibility for lining and resurfacing equipment operating in fluid fl.. |