Polymer Property : Tensile Strength at Break = 17.9 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	17.9 MPa	2600 psi	2 in/min; ASTM D638
RheTech Products FT1001-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Facias, claddings, and rocker panelsBodyside moldingsStep pads and bumper componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	17.9 MPa	2600 psi	2 in/min; ASTM D638
RheTech Products FT1004-625UV Thermoplastic Polyolefin, UV Stabilized, Interior DX9 Black Applications: Step padsHitch padsScuff platesInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	17.9 MPa	2600 psi	2 in/min; ASTM D638
RheTech Products FT2400-648UV Thermoplastic Polyolefin, UV Stabilized, 848 Black Applications: Bumper rub stripsHitch padsScuff padsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	17.9 MPa	2600 psi	2 in/min; ASTM D638
RheTech Products FT3080-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Step padsHitch padsScuff padsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	17.9 MPa	2600 psi	2 in/min; ASTM D638
RheTech Products FT3080-425 Thermoplastic Polyolefin, UV Stabilized, YBWA Platinum Applications: Step padsHitch padsScuff platesInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	17.9 MPa	2600 psi	2 in/min; ASTM D638
RheTech Products FT3080-729UV Thermoplastic Polyolefin, UV Stabilized, AG-64 Grey Applications: Step padsHitch padsScuff platesInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	17.9 MPa	2600 psi	2 in/min; ASTM D638
RheTech Products FT4700-01A Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: CladdingsBodyside moldingsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	17.9 MPa	2600 psi	2 in/min; ASTM D638
RheTech Products FT4802-691UV Thermoplastic Polyolefin, UV Stabilized, RJ3 Dark Grey Green Applications: Bodyside moldings and claddingsFacia and bumper coversExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	17.9 MPa	2600 psi	2 in/min; ASTM D638
RheTech Products FT7011-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: Claddings and faciasExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	17.9 MPa @Temperature 23.0 °C	2600 psi @Temperature 73.4 °F	Die C2 hr; ASTM D412
PolyOne OnFlex™ AW 300-02 Thermoplastic Elastomer (TPE) OnFlex™ AW 300-02 is a non-halogen flame retardant material designed for appliance wire applications. New Product. Commercial specifications have not been established.Purge thoroughly before and af..
Tensile Strength at Break	17.9 MPa	2600 psi	ASTM D4745
3M Dyneon™ CC146/S Custom Fluoropolymer Compound (discontinued **) This compound consists of a mixture of 60% bronze blended with PTFE.Information provided by Dyneon, A 3M Company
Tensile Strength at Break	17.9 MPa	2600 psi	Molded; ASTM D638
LyondellBasell PetrotheneÂ® NA942094 Low Density Polyethylene ApplicationsPETROTHENE NA 942 is a series of resins designed especially for heavy duty film applications, such as bags used to package fertilizer, peat moss, decorative stone, and agricultural and c..
Tensile Strength at Break	17.9 MPa	2600 psi	ASTM D1414
Greene Tweed FLUORAZÂ® 890 Fluoroelastomer, FEPM Sanitary gaskets made from FluorazÂ® 890 are ideal for use in standard SIP and CIP applications where EPDMs and FKMs fail. While EDPMs and FKMs can provide a deal for extended periods, changes in..
Tensile Strength at Break	17.9 MPa	2600 psi	ASTM D638
Teknor Apex APEXÂ® 4130 Polyvinyl Chloride, Flexible Notes: 75Â°C Jacket; RoHS Compliant Features: Good UV Resistance; Sunlight Resistant (720 hours) Uses: Flexible Cord Jacketing Forms: Pellets Agency Ratings: UL QMTT2 .E73402 Wire Types: SJTW; STW..
Tensile Strength at Break	17.9 MPa	2600 psi	ASTM D638
Teknor Apex APEXÂ® 92-A2292C-90 Polyvinyl Chloride, Flexible Notes: 105Â°C General Purpose; RoHS Compliant Features: Flame Retardant; High Heat Resistance Uses: Cable JacketingForms: Pellets Processing Method: Injection Molding Agency Ratings: UL QMFZ2 .E54..
Tensile Strength at Break	17.9 MPa	2600 psi	ASTM D638
Teknor Apex FlexalloyÂ® 89501-83 Polyvinyl Chloride, Elastomer Notes: 105Â°C Insulation; RoHS Compliant Features: Flame Retardant; High Heat Resistance; Low Temperature Flexibility Uses Wet Rated Insulation Wire Types: NISPE-1; NISPE-2; SE; SEO; SEOW; SEW; SJ..
Tensile Strength at Break	17.9 MPa	2600 psi	ASTM D638
Teknor Apex FlexalloyÂ® 89501-83FR Polyvinyl Chloride, Elastomer Notes: 105Â°C Insulation; RoHS Compliant Features: High Heat Resistance; Low Temperature Flexibility Uses Wet Rated Insulation Wire Types: NISPE-1; NISPE-2; SE; SEO; SEOW; SEW; SJE; SJEO; SJEOW; S..
Tensile Strength at Break	17.9 MPa	2600 psi	ASTM D638
Teknor Apex FireguardÂ® 910-A10-NL2 Polyvinyl Chloride, Flexible Notes: RoHS Compliant Features: Flame Retardant; Low Smoke Emission Wire Types: CL2P; CL3P; CMP; FPLP; MPP; OFNP Agency Ratings: NEC Article 725; NEC Article 760; NEC Article 770; NEC Article 800;..
Tensile Strength at Break	17.9 MPa	2600 psi	ASTM D638
A. Schulman POLYTROPE™ TPP 524E Extrusion Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 524E is an extrusion grade olefinic thermoplastic elastomer. This mineral filled product is suited for profile extrusion or blow molding. TPP 524E is paintable and can be ..
Tensile Strength at Break	17.9 MPa	2600 psi	ASTM D412
Teknor Apex Telcar® TL-1446G Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets P..
Tensile Strength at Break	17.9 MPa	2600 psi	ASTM D638
A. Schulman POLYTROPE™ TPP 524E Extrusion Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 524E is an extrusion grade olefinic thermoplastic elastomer. This mineral filled product is suited for profile extrusion or blow molding. TPP 524E is paintable and can be ..
Tensile Strength at Break	17.9 MPa	2600 psi	ASTM D638
A. Schulman POLYTROPE™ TPP 524E Extrusion Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 524E is an extrusion grade olefinic thermoplastic elastomer. This mineral filled product is suited for profile extrusion or blow molding. TPP 524E is paintable and can be ..
Tensile Strength at Break	17.9 MPa	2600 psi	ASTM D412
Teknor Apex Telcar® TL-2468A Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets ..
Tensile Strength at Break	17.9 MPa	2600 psi	at 2.0 in/min, Tested using a 50 mil. Sheet; ASTM D638
Chevron Phillips EB6755 Rubber Modified Polystyrene DescriptionChevron EB6755 is an extrusion grade, high impact polystyrene developed for use in packaging applications. It is designed for exceptional environmental stress-crack resistance and practi..
Tensile Strength at Break	17.9 MPa	2600 psi	vs. aluminum; 130 s set time
Elmer's Products Aron Alpha® 203 Cyanoacrylate Adhesive (Industrial Krazy Glue™) General purpose adhesive for a variety of applications. Various viscosities and gap filling properties available.High gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair o..
Tensile Strength at Break	17.9 MPa	2600 psi	Molded and tested in accordance with ASTM D4976; ASTM D638
Dow DMDA-8980 NT 7 High Density Polyethylene Resin DOW DMDA-8980 NT 7 is produced using UNIPOL™ process technology. It is intended for use in thin wall injection molding applications such as food containers. Information provided by Dow
Tensile Strength at Break	17.9 MPa	2600 psi	ASTM D638
ExxonMobil Paxon™ AG45-004 Blow Molding Resin (discontinued **) AG45-004 is a blow molding high density polyethylene which offers exceptional stress crack resistance and impact performance. It contains an antistat which permits this resin to be used in all food..