Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 16.9 MPa | 2450 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Elastamax™ HTE 3070 Polyvinyl Chloride + NBR (PVC+NBR) Elastamax™ HTE Series thermoplastic elastomers (TPEs) are based upon compounded blends of PVC resins and nitrile rubber. These elastomeric materials provide outstanding resistance to hydrocarbons a.. |
|||
Tensile Strength at Break | 16.9 MPa | 2450 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Elastamax™ HTE 3170 Polyvinyl Chloride + NBR (PVC+NBR) Elastamax™ HTE Series thermoplastic elastomers (TPEs) are based upon compounded blends of PVC resins and nitrile rubber. These elastomeric materials provide outstanding resistance to hydrocarbons a.. |
|||
Tensile Strength at Break | 16.9 MPa | 2450 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible A8504 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 16.9 MPa | 2450 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R264AE Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 16.9 MPa | 2450 psi | ASTM D638 |
Sterigenics Raprex® R100D Branched High Density Polyethylene Applications: ExtrusionRAPREX® R100D is a high density polyethylene based resin that exhibits an excellent balance of melt processability and physical properties due to its unique branched struct.. |
|||
Tensile Strength at Break | 16.9 MPa | 2450 psi | ASTM D638 |
Teknor Apex APEX® 3801-75 Polyvinyl Chloride, Flexible Features: Non-DEHP Plasticizer; Ethylene Oxide Sterilizable; High Heat Resistance Uses: Medical/Healthcare Applications Processing Method: Extrusion Forms: PelletsInformation Provided by Teknor Apex.. |
|||
Tensile Strength at Break | 16.9 MPa | 2450 psi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FC 2174 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2174 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
Tensile Strength at Break | 16.9 MPa | 2450 psi | ASTM D638 |
Teknor Apex APEX® 65009 Polyvinyl Chloride, Flexible Notes: 75°C Jacket; RoHS Compliant Uses: Wire and Cable ApplicationsForms: PelletsInformation Provided by Teknor Apex |