- Polymer Property : Tensile Strength at Break = 16.0 MPa
Polymer Property : Tensile Strength at Break = 16.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ASTM D638 |
| Iran Petrochemical (PCC) 60505 High Density Polyethylene 60505 is a HDPE injection molding grade which combines high stiffness with good physical properties. This resin is well suited for crates and toys applications.Application: crates, injection molding.. |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ISO 527-1, -2 |
| LyondellBasell Hostacomâ„¢ CB271FC Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ CB271FC high melt flow, 2,400 MPa flexural modulus, precolored, UV-stabilized, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent combination of.. |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL WCA875 PPE-TPE (Asia Pacific) Non-halogenated flame retardant Flexible Noryl extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Excellent flame retardant performance with balanced t.. |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL WCD855 PPE-TPE (Asia Pacific) Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as cable jacket of UL 62 SPE and NISPE confiations. Flame retardant performance capable of m.. |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics SABIC PPCOMPOUND 55T1030 PP SABIC® PPcompound 55T1030 is a general purpose, talc filled, heat stabilized copolymer polypropylene compound. This compound exhibits very high impact, and is suitable for multiple processing met.. |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON MD000I PP (Europe-Africa-Middle East) LNP* Stat-kon* MD000I is a compound based on Polypropylene resin. Added features of this material include: Electrically Conductive, High Impact. |
|||
| Tensile Strength at Break | >= 16.0 MPa | >= 2320 psi | ISO R 527 |
| Stir SpA Giesse EPM/78 (PVC) Application: Extrusion medical parts - medium flexibilityInformation provided by STIR SpA |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP TH0815A PUR (Asia Pacific) LNP* THERMOCOMP* TH0815A is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL WCD851 PPE-TPE (Asia Pacific) Flexible, strong flame-retardant, halogen-free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame retardant performance capable of meeting UL VW-.. |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL WCD891B PPE-TPE Non-halogenated flame retardant, flexible Noryl resin intended for evaluation in wire and cable applications. Strong flame retardant performance capable of meeting VW-1 and 80°C end use tempera.. |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ISO R 527 |
| Stir SpA SA 105/2 (PVC) Application: Extrusion sheath CEI 20-11 type TM 3Information provided by STIR SpA |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ASTM D412 |
| Borealis FR4837 Chemically Crosslinkable Polyethylene Compound for Primary Automotive Wires FR4837 is a chemically crosslinkable Non-halogen flame retardant Polyethylene compound for Primary Automotive and Appliance Wire. Applications: FR4837 is intended for use as a 125º C rated primary.. |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | |
| Daikin DAI-EL G-671 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 67% Fluorine Content Offers minimal compression set and excellent sealing. The terpolymer type is able to withstand polarized solvents to realize a wide range of application.Features: Excellent low-temperature sealing .. |
|||
| Tensile Strength at Break | >= 16.0 MPa | >= 2320 psi | ISO R 527 |
| Fainplast Compounds FKA 92 Flexible PVC, Flame Retardant Insulation Lead Free General purposes |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ISO R 527 |
| Fainplast Compounds GS 8502 Flexible PVC, Injection Molding for Footwear Soles |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ISO R 527 |
| Fainplast Compounds GSK 88 Flexible PVC, Injection Molding, Lead Free Technical items |
|||
| Tensile Strength at Break | >= 16.0 MPa | >= 2320 psi | ISO R 527 |
| Fainplast Compounds CL 006 Flexible PVC, Sheathing Mineral oil resistent |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | Compounded, 35 mins.; ISO 37 |
| Dynasol Calprene® 248 Medium CIS Polybutadiene (38%) Calprene 248 is a medium CIS polybutadiene (38 %), polymerized in solution. This product has an excellent mixing and processing behavior. It is used as ingredient in tire compounds and in other appl.. |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ISO R 527 |
| Fainplast Compounds PH 76/A Flexible PVC, Transparent Extrusion Water pipes |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ISO R 527 |
| Fainplast Compounds PK 85/N Flexible PVC, Lead Free Profiles DOP Free |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ASTM D638 |
| Aclo Accutech Polypropylene Copolymer CP0436W30L1 Wollastonite Reinforced |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ASTM D638 |
| Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (3.5 mm Molded Thickness) AZDEL SuperLite® SL551000-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ISO 527-1-2 |
| Breplast Bretene TS COR Plus T15 High Density Polyethylene Recovered polyethylene compositeInformation provided by Breplast S.p.A. |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ASTM D638 |
| Aclo Accutech Polypropylene Copolymer CP0436C20L1 Calcium Reinforced |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ASTM D638 |
| Aclo Accutech Polypropylene Copolymer CP0436W20L Wollastonite Reinforced |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ISO R 527 |
| Fainplast Compounds MGS 79 Medical Flexible PVC, Injection Molding Connectors and special components |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ISO R 527 |
| Fainplast Compounds PM 7005 Flexible PVC, Lead Free Pipes and profiles |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ASTM D638 |
| Lushan M-10F Adhesive Resin for Multi-layer Sausage Casing film Adhesive resin Lushan series for sausages casing film is anhydride-modified polyethylene product and is available in pellet form. Adhesive resin Lushan series for sausages casing film is designed fo.. |
|||
| Tensile Strength at Break | >= 16.0 MPa | >= 2320 psi | ISO R 527 |
| Fainplast Compounds CL 76/1 Flexible PVC, Sheathing General purposes |
|||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Stat-kon MD000IU PP (Asia Pacific) LNP* Stat-kon* MD000IU is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact, UV Stabilized.This data wa.. |
|||