Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 3414R PC (Asia Pacific) 40% GR, provides improved mechanical properties and UL94V-1 rated at 0.058"". Internal mold release added. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP OCL36A PPS - Branched LNP LUBRICOMP* OCL36A is a compound based on PPS - Branched resin containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP OCL36A PPS - Branched (Asia Pacific) LNP* LUBRICOMP* OCL36A is a compound based on PPS - Branched resin containing Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RFL36U PA 66 LNP* LUBRICOMP* RFL36U is a compound based on Nylon 66 resin containing 15% PTFE, 30% Glass Fiber. Added features of this grade include: Wear Resistant, UV Stabilized. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2300 PEI (Asia Pacific) 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification, KTW certification in recognized colors. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2300R PEI 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2300R PEI (Asia Pacific) 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2310 PEI 30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2310EPR PEI (Asia Pacific) 30% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2310EPR PEI (Europe-Africa-Middle East) 30% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. Resin is RoHS compliant. UL94 V0 listing. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2310F PEI 30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2310R PEI 30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2310R PEI (Asia Pacific) 30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM HU2300 PEI 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP .. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM HU2310 PEI 30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP.. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM HU2310 PEI (Asia Pacific) 30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP.. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM HU2310 PEI (Europe-Africa-Middle East) 30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). RoHS compliant. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP.. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Stat-kon DE008E PC (Europe-Africa-Middle East) LNP* Stat-kon* DE008E is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding.This data was supplied by SA.. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DF008ER PC (Europe-Africa-Middle East) LNP* Thermocomp* DF008ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP LF005 PEEK LNP* THERMOCOMP* LF005 is a compound based on Polyetheretherketone resin containing 25% Glass Fiber. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP VF008A PA 66 LNP* THERMOCOMP* VF008A is a compound based on High Impact Nylon 66 containing 40% Glass Fiber. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp WC006 Polyester, TP LNP* Thermocomp* WC006 is a compound based on Polyester, TP resin containing Carbon Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | Nominal Stress, brk, Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX830 PPE+PS+PA 30% Glass Reinforced PPE+PA Alloy. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX830 PPE+PS+PA (Asia Pacific) GR 30%. Highest stiffness of 1200000 psi (8200 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: under the bonnet. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP WC006 PBT LNP* THERMOCOMP* WC006 is a compound based on PBT resin containing 30% Carbon Fiber. Added feature of this grade is: Electrically Conductive. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | ASTM D638 |
A. Schulman SCHULAMID® 6 GF15H 30% Glass Fiber Reinforced Nylon 6 Information provided by A. Schulman. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | ASTM D638 |
A. Schulman SCHULAMID® 6 GF15H 30% Glass Fiber Reinforced Nylon 6 Information provided by A. Schulman. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | ASTM D638 |
A. Schulman SCHULAMID® 6 GF15H 30% Glass Fiber Reinforced Nylon 6 Information provided by A. Schulman. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp DCL36 PC LNP LUBRICOMP* DCL36 is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP fo.. |
|||
Tensile Strength at Break | 158 MPa | 22900 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® FR50 BK505 Nylon 66
(Unverified Data**) 25% Glass Reinforced Flame Retardant Polyamide 66 Zytel FR50 BK505 is a 25% glass fiber reinforced flame retardant black polyamide 66 resin for injection molding.Information provided by DuPont Perfo.. |