Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 15.5 MPa | 2250 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R4510H Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.5 MPa | 2250 psi | ISO R 527 |
Stir SpA G MORBIDO (PVC) Application: Extrusion for refrigerator sealsInformation provided by STIR SpA |
|||
Tensile Strength at Break | 15.5 MPa | 2250 psi | ASTM D638 |
Teknor Apex APEX® 3300-75NT Polyvinyl Chloride, Flexible Features: DEHP Plasticizer; Ethylene Oxide Sterilizable Uses: Food Service Application; Medical/Healthcare Applications; Tubing Processing Method: Extrusion Forms: PelletsInformation Provided by Tek.. |
|||
Tensile Strength at Break | 15.5 MPa | 2250 psi | ASTM D638 |
Teknor Apex APEX® 7500-80 Polyvinyl Chloride, Flexible Notes: 105°C General Purpose; RoHS Compliant Features: High Heat Resistance Uses: Connectors; Grommets; Plugs; Strain ReliefsForms: Pellets Processing Method: Injection Molding Agency Ratings: UL.. |
|||
Tensile Strength at Break | 15.5 MPa | 2250 psi | ASTM D638 |
Teknor Apex APEX® 01-A0087A-91 Polyvinyl Chloride, Flexible Notes: 75°C Jacket; RoHS Compliant Uses: Wire and Cable ApplicationsForms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 15.5 MPa | 2250 psi | ASTM D638 |
Teknor Apex APEX® 3300R-75NT Polyvinyl Chloride, Flexible Notes: RoHS Compliant Uses: Wire and Cable Applications Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 15.5 MPa | 2250 psi | ASTM D412 |
Teknor Apex MF 170 NT Polyvinyl Chloride, Flexible Film Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Film, Medical Applications Forms-PelletsAppearance-ClearInformation provided by Teknor Apex Company |
|||
Tensile Strength at Break | 15.5 MPa | 2250 psi | ASTM D412 |
Teknor Apex Telcar® TL-1934A BLK 111 Thermoplastic Elastomer Information Provided by Teknor Apex |
|||
Tensile Strength at Break | 15.5 MPa | 2250 psi | ASTM D638 |
ExxonMobil Escorene® LD 705.MJ Molding, extrusion and compounding resin Escorene Ultra LD 705.MJ is a fraction melt index, 13.3 wt% vinyl acetate copolymer suitable for use in making blow molded articles, extruded profiles and compounds.Information provided by ExxonMobi.. |
|||
Tensile Strength at Break | 15.5 MPa | 2250 psi | Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638 |
Dow FINGERPRINT™ DFDA-7510 NT Linear Low Density Polyethylene Resin FINGERPRINT™ DFDA-7510 NT resin is produced using UNIPOL™ process technology. It is intended for use in micro irrigation tube, durable hose and tube, profile extrusion, and injection molded fitti.. |
|||
Tensile Strength at Break | 15.5 MPa | 2250 psi | Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638 |
Dow DNDB-7441 NT 7 Linear Low Density Polyethylene Resin DOW DNDB-7441 NT 7 is produced using UNIPOL™ PE process technology. It is intended for use in hose and tube applications. It also has utility in gasketing, spiral wound hose, and corrugated hose .. |
|||
Tensile Strength at Break | 15.5 MPa | 2250 psi | ISO 37 |
Alliance Polymers Viprene™ P45D-22U-BLK Thermoplastic Vulcanizate Elastomer Viprene™ P45D-22U-BLK is a UV and Heat Stabilized TVP (Thermoplastic Vulcanizate Elastomer). This material can be easily processed by extrusion or injection molding. It exhibits easy flowing charac.. |
|||
Tensile Strength at Break | 15.5 MPa | 2250 psi | Transverse; ASTM D3759 |
3M ScotchPad™ 3750P Tape Pad 3M™ ScotchPad™ Tape Pad 3750P is a pre-cut pad formed with layered, high-performance tape sheets featuring durable 3M™Scotchpro™ film backing that is strong, conformable, and resistant to impact.. |
|||
Tensile Strength at Break | 15.5 MPa | 2250 psi | Transverse; ASTM D3759 |
3M ScotchPad™ 809G Custom Tape Pads 3M™ ScotchPad™ Custom Tape Pad 809G is a pre-cut pad formed with layered, high performance tape sheets featuring durable 3M™ Scotchpro™ film backing that is strong, conformable and resistant to .. |
|||
Tensile Strength at Break | 15.5 MPa | 2250 psi | Transverse; ASTM D3759 |
3M ScotchPad™ 822 Label Protection Tape Pad 3M™ ScotchPad™ Label Protection Tape Pad 822 is a pre-cut pad formed with layered high-performance tape sheets featuring durable 3M™ ScotchPad™ polypropylene film backing that is strong, conform.. |
|||
Tensile Strength at Break | 15.5 MPa | 2250 psi | ISO 37 |
Alliance Polymers Viprene™ P45D-22U-NAT Thermoplastic Vulcanizate Elastomer Viprene™ P45D-22U-NAT is a UV and Heat Stabilized TVP (Thermoplastic Vulcanizate Elastomer). This material can be easily processed by extrusion or injection molding. It exhibits easy flowing charac.. |
|||
Tensile Strength at Break | 15.5 MPa | 2240 psi | ASTM D3759 |
3M Tartan™ 8934 Utility Filament Tape Tartan™ Utility Filament Tape 8934 is a glass filament reinforced tape for light duty strapping, bundling and reinforcing. It has a synthetic rubber resin adhesive with good adhesion to most fiberb.. |
|||
Tensile Strength at Break | 15.5 MPa | 2250 psi | ASTM D638 |
Resirene Resirene® 2210 High Impact Polystyrene Features:Very High FlowEasy ProcessingGood GlossFlexibilityFDA Rating: 21 CFR 177.1640High ProductivityApplications:InjectionThin Wall ApplicationsHard to Fill MoldsTelephonical DevicesYot CupsToysC.. |