Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 15.2 MPa | 2200 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable JJX20A Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength at Break | 15.2 MPa @Temperature 23.0 °C |
2200 psi @Temperature 73.4 °F |
Die C2 hr; ASTM D412 |
PolyOne OnFlex™ HFFR 310-01 Thermoplastic Elastomer (TPE) OnFlex™ HFFR 310-01 is a non-halogen flame retardant material designed for cable jackets. New Product. Commercial specifications have not been established. - Non-halogen flame retardant - UL62 comp.. |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible B87FB Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R208AE Polyvinyl Chloride + NBR (PVC+NBR) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R9788A Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D4894 |
3M Dyneon™ CCM605 PTFE, 25% Glass Filled
(discontinued **) Type II, free flowing.Typical Applications: Finished or semi-finished parts: sheets, rods, tubes, billets for skiving of films or machining into complex shapes.Information provided by the Dyneon div.. |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D638 |
LyondellBasell Petrothene® GA808093 Linear Low Density Polyethylene ApplicationsPETROTHENE GA 808-093 is a broad molecular weight, linear low density polyethylene resin designed for use as a wire and cable insulation. An antioxidant package is added to ensure therm.. |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D638 |
LyondellBasell Purell® PE3020D Low Density Polyethylene, Injection Molding, Blow Fill & Seal, Extrusion Blow Molding Purell PE 3020 D is a low density polyethylene with high rigidity, good opticals and good chemical resistance. It is delivered in pellet form. Target markets are small blow molding including packagi.. |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D1414 |
Greene Tweed CHEMRAZ® E38 Perfluoroelastomer Chemraz® E38 was specifically developed for high-density plasma systems and diffusion processes where seal reliability and very minimal contamination are essential. The material provides excelle.. |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | |
Taiwan PU Corporation CPU-69-A/B Mixing Ratio 100/42 Polyurethane Casting Elastomer Compound of CPU-69-A/B with a mixing ratio of 100/42.Information provided by Taiwan PU Corporation.MatWeb has a separate entry for the unmixed A nd B components. |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | ISO R 527 |
Stir SpA AF 80 3 GEC (PVC) Application: Insulation CEI 20-11 type TI 1 low acid fumes emissionInformation provided by STIR SpA |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | ISO R 527 |
Stir SpA SR 90 CZ (PVC) Application: Extrusion insulation CEI 20-11 type TI-1Information provided by STIR SpA |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D638 |
Teknor Apex APEX® CX 2001-84 Polyvinyl Chloride, Flexible Notes: RoHS Compliant Features: Flame Retardant Uses: Cable Jacketing; Coaxial Cable Jacketing Agency Ratings: UL 444; UL 62Processing Method: Extrusion Forms: Pellets Additional Information: Temper.. |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D412 |
Teknor Apex MF 569 Polyvinyl Chloride, Flexible Film Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Film, Medical Applications Forms-PelletsInformation provided by Teknor Apex Company |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D412 |
Teknor Apex Monprene® MP-2100-S-L3 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D412 |
Teknor Apex MF 181 NT Polyvinyl Chloride, Flexible Film Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Film, Medical Applications Forms-PelletsAppearance-ClearAgency Ratings- FDA Unspecified RatingInformatio.. |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D412 |
Teknor Apex Telcar® TL-88-N809C Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets P.. |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D412 |
Teknor Apex Uniprene® UN-2678C Thermoplastic Vulcanizate Notes: Injection Rate: Fast Uses: Expansion Joint; Grommets; Tubing; Gaskets; Plugs; Weatherstripping; Glazing; Shock Absorbing Pads Forms: Pellets Processing Method: Extrusion; Injection Molding Ex.. |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | Across Flow; ASTM D412 |
ExxonMobil Santoprene® 121-87 Thermoplastic Elastomer A hard, black, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide ran.. |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | Transverse to Flow; ASTM D882 |
Diamond Polymers NPP10-0218 Low Density Polyethylene Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D638 |
Americas Styrenics STYRON A-TECH® 1290 High Impact Polystyrene Product CharacteristicsEasy processingGood impact resistanceESCRFood Contact CompliantUL Classification 94HBTypical ApplicationsCreamer and yot containersExtrusion/ thermoformingInformation provided.. |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FLS 2530 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FLS 2530 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu.. |
|||
Tensile Strength at Break | 15.2 MPa | 2200 psi | ASTM D412 |
Teknor Apex Monprene® MP-1878 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |