Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 14.8 MPa | 2150 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable WJJC32L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide.. |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible C9000 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible C90B1 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible C90UB Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | ASTM D638 |
LG Chemical LUTENE XL2700BK PE Compound Description: LUTENE XL2700BK has excellent strippability, processability, weather resistance, heat resistance for medium and high voltage power cables. The advantage of LUTENE XL2700BK over conventi.. |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | ASTM D1414 |
Greene Tweed CHEMRAZ® 605 Perfluoroelastomer Chemraz® 605, a perfluoroelastomer, is ideally suited for challenging fluid handling applications. A high temperature compound with superior compression set resistance, physical properties and e.. |
|||
Tensile Strength at Break | 14.8 MPa | 2140 psi | ASTM D638 |
Teknor Apex APEX® 3707-70LG-NT Polyvinyl Chloride, Flexible Notes: RoHS Compliant Uses: Medical/Healthcare Applications Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | ASTM D638 |
Teknor Apex APEX® 3801-70 Polyvinyl Chloride, Flexible Features: Non-DEHP Plasticizer; Ethylene Oxide Sterilizable; High Heat Resistance Uses: Medical/Healthcare Applications Processing Method: Extrusion Forms: PelletsInformation Provided by Teknor Apex.. |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | ASTM D638 |
Teknor Apex APEX® 80328-YFR Polyvinyl Chloride, Flexible Notes: 75°C Insulation; RoHS Compliant Features: Flame Retardant; Good UV Resistance Uses: Cable Jacketing; InsulationAgency Ratings: UL QMTT2 .E73402 Forms: Pellets Wire Types: TWInformation Pro.. |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | ASTM D638 |
Teknor Apex APEX® 80-C118-R Polyvinyl Chloride, Flexible Notes: 105°C Insulation; RoHS Compliant Uses: Wire and Cable Applications Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | ASTM D638 |
Teknor Apex APEX® 90-A471R-75-NT Polyvinyl Chloride, Flexible Features: DEHP Plasticizer; Radiation (Gamma) Resistant; Radiation Sterilizable Uses: Medical/Healthcare Applications; Tubing Processing Method: Extrusion Forms: PelletsInformation Provided by Tekno.. |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | ASTM D412 |
Teknor Apex Monprene® MP-1320F Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | ASTM D412 |
UBE UBEPOL BR130B Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 35 Minutes at 145°C) Description: UBEPOL BR is UBE's line of polybutadiene rubber products.Information provided by UBE. |
|||
Tensile Strength at Break | 14.8 MPa | 2140 psi | ASTM D412 |
Teknor Apex Telcar® TL-86-K902A Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | ASTM D638 |
A. Schulman CP812 Linear, Medium-Density Polyethylene DescriptionCP 812 is a linear medium-density polyethylene resin with excellent molding characteristics and good low temperature impact. Information provided by A. Schulman. |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | ASTM D638 |
A. Schulman CP812 Linear, Medium-Density Polyethylene DescriptionCP 812 is a linear medium-density polyethylene resin with excellent molding characteristics and good low temperature impact. Information provided by A. Schulman. |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | ASTM D638 |
A. Schulman CP812 Linear, Medium-Density Polyethylene DescriptionCP 812 is a linear medium-density polyethylene resin with excellent molding characteristics and good low temperature impact. Information provided by A. Schulman. |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | ASTM D638 |
A. Schulman CP812 Linear, Medium-Density Polyethylene DescriptionCP 812 is a linear medium-density polyethylene resin with excellent molding characteristics and good low temperature impact. Information provided by A. Schulman. |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | |
Daikin DAI-EL G-781 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content Offers minimal compression set and excellent sealing. The copolymer type offers good compression set characteristics.Information provided by Daikin Industries. |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | Press cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 232°C |
3M Dyneon™ 2299X Ultra High Viscosity Fluoroelastomer 3M™ Dyneon™ FC 2299X is an ultra high viscosity fluoroelastomers designed for use in applications such as o-rings, gaskets and seals requiring higher strength than achievable with lower viscosity .. |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FC 2170 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2170 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
Tensile Strength at Break | 14.8 MPa | 2140 psi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FG 5630Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FG 5630Q can be compounded using standard water cooled internal mixers or two-roll mills. The “dry” ingredients should be blended before adding to the masticated gum... |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | Press cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 232°C |
3M Dyneon™ 2299PX Ultra High Viscosity Fluoroelastomer 3M™ Dyneon™ FC 2299PX is an ultra high viscosity fluoroelastomers designed for use in applications such as o-rings, gaskets and seals requiring higher strength than achievable with lower viscosity.. |
|||
Tensile Strength at Break | 14.8 MPa | 2140 psi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FC 2120 Fluoroelastomer 3M™ Dyneon™ Flouroelastomer FC 2120 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | ASTM D638 |
A. Schulman CP812 Linear, Medium-Density Polyethylene DescriptionCP 812 is a linear medium-density polyethylene resin with excellent molding characteristics and good low temperature impact. Information provided by A. Schulman. |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | ASTM D638 |
A. Schulman CP812 Linear, Medium-Density Polyethylene DescriptionCP 812 is a linear medium-density polyethylene resin with excellent molding characteristics and good low temperature impact. Information provided by A. Schulman. |
|||
Tensile Strength at Break | 14.8 MPa | 2150 psi | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FC 2173 Fluoroelastomer
(discontinued **) Composition: di-polymer of vinylidene fluoride and hexafluoropropyleneLow viscosityProcess targets: compression moldingProprietary incorporated cure technologyExcellent mold flow and mold release ch.. |