Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO 37 |
PolyOne OnFlex™ V 3085A-S0098 Thermoplastic Elastomer (TPE) OnFlex™-V provides the performance of traditional vulcanised rubber, but with the processability of a thermoplastic. OnFlex™-V 3000 series thermoplastic elastomer compounds are based on a polyolef.. |
|||
Tensile Strength at Break | <= 14.0 MPa | <= 2030 psi | ISO/R527 |
Polykemi AB POLYelast TPE RCZ350D UV4 Thermoplastic Elastomer, UV-Resistant Information provided by Polykemi AB |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM 1457-62 T |
Fluorseals PTFE 60% bronze filled Improved compressive strength and thermal conductivity.Information provided by TEKU GmbH Fluorkunststoffe, a distributor of Fluorseals materials. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D 638 |
LyondellBasell Hifaxâ„¢ CA10GC Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ CA10GC fractional melt flow, 100 MPa flexural modulus, precolored, UV-stabilized, reactor grade, extrudable thermoplastic elastomeric olefin (TEO) resin combines good proces.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO 527-1, -2 |
LyondellBasell Hifaxâ„¢ CA287AHF Thermoplastic Polyolefin Elastomer Description: Hifax â„¢ CA287AHF is a thermoplastic polyolefin elastomer suitable for automotive exterior partsFeatures: Good StiffnessGood ProcessabilityGood Impact ResistanceGood Colorability Pa.. |
|||
Tensile Strength at Break | 14.0 - 30.0 MPa @Thickness 2.00 mm |
2030 - 4350 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 32008 Polyvinylidene Fluoride (PVDF) Solef® 32008 PVDF copolymer is a low viscosity and very flexible grade for Wire & Cable applications.Features: Copolymer; Good Flexibility; Low ViscosityUses: Wire & Cable ApplicationsAdditional .. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO 527 |
SABIC Innovative Plastics LNP Stat-kon FX97333 PE LNP* Stat-kon* FX97333 is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for th.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
UBE F522 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | 50mm/min; IEC 60811-1-1 |
Borealis Casico™ FR6082 Reduced Fire Hazard Jacketing Compound Casico™ FR6082 is a thermoplastic, reduced fire hazard, zero halogen black jacketing compound combined with high mechanical strength, toughness and excellent extrusion properties. It is based on th.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
ELASTO UK Dryflex® 500850S SEBS Based Material, Unfilled Qualities, 85A Hardness, Translucent The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO 37 |
ELASTO UK Dryflex® 9035-101 TPE, Modified Injection Molding Grade for Semi Rigid Molding The VTC TPE Group have developed endless formulations to fulfill different properties and application requirements to optimize the finished component. VTC Dryflex® 9035-101 is specifically designe.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO 527-2/50 |
ExxonMobil Exxtral™ BNT 013 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin designed for injection molded automotive interior applications such as door panels.Availability: Africa & Middle East, Asia Pacific, E.. |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds CL 70/2 Flexible PVC, Sheathing General purposes |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds CL 83/1 Flexible PVC, Sheathing Sheath coaxial TV Cable |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds GA 80/1 Flexible PVC, Flame Retardant Sheathing General purposes |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds GK 80 Flexible PVC, Flame Retardant Sheathing Lead Free General purposes |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds GK 85/1 Flexible PVC, Flame Retardant Sheathing Lead Free General purposes |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO R 527 |
Fainplast Compounds GS 70/T Flexible PVC, Injection Molding for Footwear Soles |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds GA 82 Flexible PVC, Flame Retardant Sheathing General purposes |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO R 527 |
Fainplast Compounds GS 74/BT Flexible PVC, Injection Molding for Footwear Soles for cold climates |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds HG 80/2 Flexible PVC, Sheathing for High Temperatures Operating temperature 90°C |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | MSZ ISO 527 |
BorsodChem ONGRO CPE 3602 C Chlorinated Polyethylene IMPACT MODIFIER FOR PVChigh impact resistancegood processabilityexcellent weather resistanceELASTOMERSvariety of cross-linking technologiesexcellent ozone- and weather resistanceexcellent chemical r.. |
|||
Tensile Strength at Break | 14.0 - 24.0 MPa | 2030 - 3480 psi | ASTM D638 |
Arkema Group KYNAR FLEX® 2500-20 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Highest flexibility. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical st.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
Aclo Accutech Polyethylene HD0204UVL High Density UV Stabilized |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO R 527 |
Fainplast Compounds PH 70 Flexible PVC, Transparent Extrusion Transparent profiles and pipes |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO R 527 |
Fainplast Compounds PM 65/FR Flexible PVC, Lead Free Spiral pipes, UL 94 Class V0 |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | 50 mm/min, 1A; ISO 527 |
SABIC Innovative Plastics SABIC PPCOMPOUND 5310 PP SABIC® PPcompound 5310 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and heat stability with exterior automotive weathering stability. The IMDS I.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO 527-1, -2 |
LyondellBasell Hifax™ HSBMF248 Thermoplastic Polyolefin Elastomer Description: Hifax™ HSBMF248 high melt flow, 1,400 MPa flexural modulus, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent combination of flow, rigidity, low t.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
Arkema Group LOTRYL® 17 BA 07 Copolymer Ethylene - Butyl Acrylate LOTRYL® 17 BA 07 is a random copolymer of ethylene and butyl acrylate, prepared by the high pressure polymerization process. LOTRYL® 17 BA 07 is used as tie layer in coextrusion PP/PE, for extrusi.. |