Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 135 MPa | 19600 psi | |
Plastcom SLOVAMID 66 GF 20 PA66, 20% glass fibre FeaturesChemically reinforced with 20 % glass fibre, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical industry. .. |
|||
Tensile Strength at Break | 135 MPa @Temperature 23.0 °C |
19600 psi @Temperature 73.4 °F |
ISO 527-2/5 |
PolyOne Bergamid™ A700 G20 U-SO Polyamide 66 (Nylon 66) Information provided by PolyOne |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527 |
Nilit FRIANYL B63 GV15 Nylon 6 for injection molding, 15% glass fiber reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | Conditioned; ISO 527-1/-2 |
Lanxess Durethan® AKV 35 H3.0 000000 Nylon 66, 35% Glass Fiber PA 66, injection molding grade, 35% glass fibers, good heat-ageing resistance |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | d.a.m.; ISO 527-1, -2; 5 mm/min |
Lanxess Durethan® ECO PA GF30 909040 Nylon 6, 30% Glass Fiber PA 6 (mainly), 30% glass fibers, injection molding, contains at least 80% pre-consumer recycled material, properties may change considerably from lot to lotInformation provided by LANXESS. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RFN14 PA 66 LNP* LUBRICOMP* RFN14 is a compound based on Nylon 66 containing 20% Glass Fiber, 5% MOS2. Added features of this grade include: Wear Resistant. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RFP36S PA 66 LNP* LUBRICOMP* RFP36S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® 420 PBT (Europe-Africa-Middle East) VALOX 420 is a 30% glass fiber reinforced PBT injection moulding resin with excellent mechanical and thermal properties. Applications: appliance handles, spotlights, electric motors. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® 553 PBT (Europe-Africa-Middle East) VALOX 553 is a 30% glass fibre reinforced, flame retardant PBT+PC blend with good warpage characteristics. Applications: appliance handles, spotlights, electric motors, pumphousings. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | 50mm/min; ISO 527 |
Teijin Panlite® B-8130R Carbon Fiber Reinforced Polycarbonate Resin CF 30% reinforced grade, meeting UL 94 V-2. It has excellent strength, stiffness, heat resistance and electric conductivity. Other features are low molding shrinkage and dimensional accuracy.Applica.. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 216 V33 PA66, 33% glass fiber, Conditioned Description: TECHNYL® A 216 V33 is a polyamide 66, reinforced with 33% of glass fiber, for injection molding. This product is available in natural color.Benefits: The product offers an excellent .. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 218 V30 PA66, 30% glass fiber, Conditioned Description: TECHNYL® A 218 V30 is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding. This product is available in natural and black colors.Benefits: The .. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RF006EUC PA 66 LNP* THERMOCOMP* RF006EUC is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include Easy Molding, UV Stabilized. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ASTM D638 |
A. Schulman ComAlloy® E-14292 Hi-Flow Glass Reinforced PPS Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® LV-50H FWA nat PA12-GF50 Product description: Grilamid LV-50H FWA natural is a 50 % glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: High stiffness combined w.. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® HTN FR52G30NHF BK337 Polyphthalamide (PPA) 30% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide with Improved Flow Zytel HTNFR52G30NHF BK337 is a 30% glass reinforced flame retardant lubricated high performance.. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | 5 mm/min; ISO 527 |
Eurostar Staramide ACF2 PA66, 10% Carbon Fiber Reinforced, Heat stabilized, Injection Molding Staramide ACF2 is a 10% Carbon Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527 |
Eurotec® Tecomid® NB40 GR30 NL IM PA6, 30% glass fiber reinforced, impact modified, natural Information provided by Eurotec® |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527 |
Eurotec® Tecotek® PC40 GR30 NL PC, 30% glass fiber reinforced, natural Information provided by Eurotec® |
|||
Tensile Strength at Break | 135 MPa @Temperature 150 - 160 °C, Time 7.20e+7 sec |
19600 psi @Temperature 302 - 320 °F, Time 20000 hour |
5 [mm/min], 50% Loss of Tensile Strength; ICE 216 |
Akro-Plastic Akromid® T1 GF 50 (3101) PPA Dry, 50% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high.. |
|||
Tensile Strength at Break | 135 MPa @Temperature -40.0 °C |
19600 psi @Temperature -40.0 °F |
ASTM Test |
BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Conditioned) Ultramid 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined wi.. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R530H BK08 Nylon 66, 30% Glass Reinforced, Conditioned Vydyne® R530H BK08 is high-flow, 30% glass-fiber reinforced, heat-stabilized PA66 resin. Available in black, it is specifically designed to maximize the retention of physical properties when expose.. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R530H NAT Nylon 66, 30% Glass Reinforced, Conditioned Vydyne® R530H NAT is general-purpose, heat-stabilized, hydrolysis-resistant, 30% glass-fiber reinforced PA66 resin. Available in natural, it is specifically designed to maximize the retention of ph.. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R530H Nylon 66, 30% Glass Filled, Conditioned Vydyne® R530H is a general-purpose, heat-stabilized, hydrolysis-resistant, 30% glass-fiber reinforced PA66 resin. Available in natural, it is specifically designed to maximize the retention of phys.. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | Conditioned; ISO R 527 |
Addiplast Addinyl A2 ZV30 Nylon 66, 30% Glass Filled Glass fiber reinforced, increased thermal aging stabilityInformation provided by Addiplast. |
|||
Tensile Strength at Break | 135 MPa | 19600 psi | Wet |
Asahi Kasei Leona® 1300G Polyamide 66 Resin, Glass Reinforced Applications: Automotive: Radiator Tanks, Fuel Injectors, ABS Sensors, Engine Mounts Electrical and Industrial: Heater Tanks, Office Furniture, Small EnginesInformation provided by Asahi Kasei |
|||
Tensile Strength at Break | 135 MPa @Temperature 60.0 °C |
19600 psi @Temperature 140 °F |
|
BASF Ultrason E 2010 G6 30% Glass Filled PES Ultrason E 2010 G6 is a 30% glass reinforced, medium viscosity injection molding PES grade with high rigidity and strength. |