- Polymer Property : Tensile Strength at Break = 130 MPa
Polymer Property : Tensile Strength at Break = 130 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-2 |
| PolyOne OnForce™ LFT PP-50LGF/001 Natural Polypropylene Homopolymer (PP Homopolymer) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. .. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | ASTM D638 |
| PolyOne Stat-Tech™ PI-05CF/000R Black Polyether Imide (PEI) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound.. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 |
| Nilit FRIANYL A63 HH-GV10 Nylon 6.6 for injection molding, 10% glass fiber reinforced Nylon 6.6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Tensile Strength at Break | <= 130 MPa | <= 18900 psi | ISO/R527 |
| Polykemi AB SCANAMID 66 A13^ F15 Nylon 66, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 130 MPa @Temperature 23.0 °C |
18900 psi @Temperature 73.4 °F |
ISO 527-2/5 |
| PolyOne Bergamid™ A700 G25 HW UF Polyamide 66 (Nylon 66) Information provided by PolyOne |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | 10mm/min; ASTM D638 |
| Kingfa PA6-MG45 45% Glass & Mineral Filled PA6 Features:Low tendency to wrapExcellent size stabilityLow abrasionOutstanding surfaceApplications:Injection moldingAutomobile partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1,-2 |
| Lanxess Pocan® B 3233 HR 000000 Polybutylene Terephthalate, 30% Glass Fibers PBT, 30% glass fibers, injection molding, improved flowability, hydrolysis stabilized |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 Type 1A |
| Solvay TECHNYL® A 218W V15 PA66, 15% glass fiber, DRY Description: Polyamide 66, reinforced with 15% of glass fiber, for injection molding, heat stabilized, with improved hydrolysis resistance.Available in: North AmericaProduct Applications: TECHNYL Â.. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Lubricomp LFL36 PEEK (Europe-Africa-Middle East) LNP*LUBRICOMP* LFL36 is a compound based on Polyetheretherketone resin containing Glass Fiber, PTFE.
Added features include: Internally Lubricated.This data was supplied by SABIC-IP for the Europe-A.. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP RX05496 PA 66 LNP* LUBRICOMP* RX05496 is a compound based on Nylon 66 resin containing 30% Mixed Glass, 15% PTFE, Silicone. Added features of this material include: Wear Resistant. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Ultem 2200N PEI (Europe-Africa-Middle East) 20% Glass fiber filled Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® 865 PBT (Europe-Africa-Middle East) VALOX 865 is a 30% glass fibre reinforced, non blooming flame retardant PBT+PET blend with an excellent surface appearance. Applications: External housings, steam irons, appliance housings and light.. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON OEL13I PPS - Linear LNP* STAT-KON* OEL13I is a compound based on PPS-Linear resin containing 15% Carbon Fiber, 5% PTFE. Added features of this grade include: High Impact, Wear Resistant, Electrically Conductive. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp RF0057E PA 66 (Europe-Africa-Middle East) LNP* Thermocomp* RF0057E is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Non-Brominated & Non-Chlorinated Flame Retardant.Thi.. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp LF004 PEEK (Europe-Africa-Middle East) LNP* THERMOCOMP* LF004 Is a compound based on Polyetheretherketone containg Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1/-2 |
| DSM Akulon® S223-G4U (Dry) 23% Glass Reinforced Nylon 66 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | conditioned; ISO 527-1/-2 |
| EMS-Grivory Grivory® BG-40 HM PA6-GF40 Product description: Grilon BG-40 HM is a heat stabilized, normal viscosity, and adhesion modified PA6 injection molding grade with 40% glass fibers. Grilon BG-40 HM has the following important prop.. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1/-2 |
| DSM Stanyl® TE250F8 Nylon 46-40% Glass Reinforced (European and Asian Grade) (Cond) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | 50%RH; ISO 527-1/-2 |
| DuPont Performance Polymers Zytel® FG70G30HSR3 BK309 Nylon 66
(Unverified Data**) Information provided by DuPont Performance Polymers |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 |
| Eurostar Staramide RF004EU PA66/6, 20% Glass Fiber Filled, Injection Molded Staramide RF004EU is a 20% Glass Fiber Reinforced Polyamide 66/6 Injection Molding (also known as Staramide 66C 20V S4)Information provided by Eurostar. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1/-2 |
| DSM Akulon® K224-G3 Nylon 6-15% Glass Reinforced (European and Asian Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 |
| Eurotec® Tecopet® PT70 GR30 NL100 XD70 PET, 30% glass fiber reinforced, flame retardant - halogen (RoHS compliant), long-term heat stabilized, natural Information provided by Eurotec® |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | 5mm/min; ISO 527 |
| BASF Ultraform N 2200 G53 UNC Q600 25% Glass Filled POM Ultraform N2200 G53 UNC Q600 is a 25% glass fiber reinforced POM injection molding grade with enhanced stiffness and toughness. |
|||
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO R 527 |
| Addiplast Addinyl C2 V15 Nylon 66/6, 15% Glass Filled Glass fiber reinforced, high strengthInformation provided by Addiplast. |
|||