Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | >= 10.3 MPa | >= 1500 psi | ASTM D638 |
S&E Specialty Polymers GPP1001M-P-2986 Grey PP Application: High impact resistance, non-blooming flame retardant polypropylene compound for UL94-V0 injection molding applications.Information provided by S&E Specialty Polymers |
|||
Tensile Strength at Break | 10.3 MPa | 1490 psi | |
NEU NeuSoft™ 455-50A Ester/ether TPU / SBC blend |
|||
Tensile Strength at Break | 10.3 MPa | 1490 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible D80M0 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 10.3 MPa | 1490 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible FC700 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 10.3 MPa | 1490 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ HC 2155G Polyvinyl Chloride, Flexible (PVC, Flexible) Geon HC 2155G is a 55 Shore A non-phthalate, gamma-stable flexible vinyl compound made from FDA sanctioned ingredients. HC 2155G can be used for extrusion and injection molding healthcare applicatio.. |
|||
Tensile Strength at Break | 10.3 MPa | 1490 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible B65U0 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 10.3 MPa | 1490 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible C7500 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 10.3 MPa | 1490 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible C75A0 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D638 |
LyondellBasell Petrothene® GA574189 Linear Low Density Polyethylene, Injection Molding Grade PETROTHENE GA574189 exhibits excellent flow and impact with good stiffness. Typical applications include lids, closures, containers, housewares and medical items.Regulatory Status: GA574189 meets th.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | molding; ASTM D638 |
LyondellBasell Petrothene® NA967000 Low Density Polyethylene, Film Extrusion Grade Petrothene NA967000 is a low density polyethylene resin designed for blown film, general purpose and industrial packaging applications. NA967000 exhibits good processing characteristics and impact s.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D1414 |
Greene Tweed CHEMRAZ® 522 Perfluoroelastomer Chemraz®, a proprietary Greene, Tweed compound, has the broadest chemical resistance of any elastomeric material. Chemraz combines the resilience and sealing force of an elastomer with chemical r.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | |
Shin-Etsu Silicones SV-56000U High Strength Silicone Elastomer SV56000U is one of a series of silicone bases designed for applications requiring high strength. Product Features: Excellent mechanical properties.Typical Applications: Molding and Extrusion applica.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D638 |
Teknor Apex APEX® 4103 Polyvinyl Chloride, Flexible Notes: 60°C General Purpose; RoHS Compliant Uses: Connectors; Grommets; Plugs; Strain ReliefsForms: Pellets Processing Method: Injection Molding Agency Ratings: UL QMFZ2 .E54709 Wire Types: Molde.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D412 |
Teknor Apex Monprene® MP-1671 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D412 |
Teknor Apex Monprene® MP-2955 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D412 |
Teknor Apex Telcar® TL-3260R Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D638 |
ExxonMobil LLDPE LL 4004EL Wire & Cable Linear Low Density Polyethylene Resin (European Grade) Product Description: LL 4004EL is a C4 Ziegler Natta LLDPE, especially designed for Low Voltage power cable insulation, using the two-step silane cross-linking process. Sufficient Cu-inhibitor shoul.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | Compression molded; ASTM D638 |
Dow 620I Linear Low Density Polyethylene (LDPE) For extruded foam applications Complies with U.S. FDA 21 CFR 177.1520 (c) 2.1 Information provided by Dow |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D412 |
Compuestos Dominicanos Polycom C-550170 PVC Description: Compuestos Dominicanos, S.A. produces a wide variety of PVC compounds for the injection molding of foot wear products, everything from full injection, shoe soles, boots, and PVC compoun.. |
|||
Tensile Strength at Break | 10.3 MPa | 1490 psi | ASTM D412 |
Compuestos Dominicanos Polycom CO-550365 PVC Description: Compuestos Dominicanos, S.A. produces a wide variety of PVC compounds for the injection molding of foot wear products, everything from full injection, shoe soles, boots, and PVC compoun.. |
|||
Tensile Strength at Break | 10.3 MPa | 1490 psi | High-K Stress Control Tube; ASTM D412 |
3M 7620-S Cold Shrink QT-III Silicone Rubber Skirted Termination Kits 3M™ Cold Shrink QT-III Silicone Rubber Skirted Termination Kits, 7620-S, 7680-S and 7690-S Series, contain one-piece, skirted, silicone Rubber Skirted Terminations, qualified as IEEE Standard 48 Cl.. |
|||
Tensile Strength at Break | 10.3 MPa | 1490 psi | High-K Stress Control Tube; ASTM D412 |
3M 7690-T Cold Shrink Silicone Rubber Termination Kits QT-III 3M™ Cold Shrink QT-III Silicone Rubber Skirted Termination Kits, 7620-Tand 7690-T Series, contain one-piece, non-skirted, silicone rubber termination, qualified as IEEE Standard 48 Class 1 for indo.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D412 |
Teknor Apex Monprene® MP-2357-L3 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D638 |
ExxonMobil LD 419.MV Wire & Cable Resin
(discontinued **) LD 419.MV is a LDPE designed for wire and cable applications and is suitable for making crosslinkable compounds for medium voltage insulation.Information provided by ExxonMobil Chemical |
|||
Tensile Strength at Break | 10.3 MPa | 1490 psi | Solvent Resistance |
3M MDT Tubing 3M MDT Tubing offers increased flexibility in combination with excellent abrasion, corrosion and environmental resistance properties and meets MIL-DTL-23053/15, Class 2. Uncoated product (without se.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D638 |
Aaron Industries AVPE LD 300-1 MELT 20 Virgin Polyethylene A natural, high flow Low Density Polyethylene resin, specifically designed for high speed injection molding applications. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | TM R050-36 |
Resinlab® EP1282 Clear Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP1282 Clear is a two part unfilled electronic grade epoxy encapsulant designed for medium sized castings. It is recognized under the Component Recognition Program of Underwriters Laborat.. |
|||
Tensile Strength at Break | 10.3 MPa | 1500 psi | TM R050-36 |
Resinlab® EP1240RC Flame Retardant Epoxy Casting Resin Resinlab™ EP1240RC is a medium viscosity, flame retardant epoxy casting resin system. It is recognized under the Component Recognition Program of Underwriters Laboratories Inc., (File# E186034, Pro.. |