Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | >= 0.414 MPa | >= 60.0 psi | ASTM D412 |
Parker Chomerics CHO-FORM 5532 EMI Shielding Material One component, moisture cure, form-in-place EMI gasketing material. This electrically conductive formulation contains silver-plated copper particles dispersed in a silicone elastomer. Cho-Form® 553.. |
|||
Tensile Strength at Break | 0.414 MPa | 60.0 psi | ASTM D624 |
Arlon A3020-B004-12 Silicone Rubber/Fiberglass Laminate
(discontinued **) Side 1: cured fusible silicone rubber; Substrate: 25% sinusoidal fiberglass; Side 2: cured fusible silicone rubber; Interleave: 1 mil PE film |
|||
Tensile Strength at Break | 0.414 MPa | 60.0 psi | T Block, 1 in<sup>2</sup> (6.45 cm<sup>2</sup>) Jaw Speed 2 in/min (50 mm/min) |
3M 4032 Double Coated Urethane Foam Tape 3M™ Double Coated Urethane Foam Tapes are conformable foams that offer high shear strength and are available with either a high temperature holding acrylic adhesive system or a rubber adhesive syst.. |