Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Creep Strength | 20.0 MPa @Temperature 788 °C, Time 3.60e+7 sec |
2900 psi @Temperature 1450 °F, Time 10000 hour |
1% creep |
ATI Allegheny Ludlum 310 Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Creep Strength | 20.0 MPa @Temperature 788 °C, Time 3.60e+7 sec |
2900 psi @Temperature 1450 °F, Time 10000 hour |
1% creep |
ATI Allegheny Ludlum 310H Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Creep Strength | 20.0 MPa @Temperature 788 °C, Time 3.60e+7 sec |
2900 psi @Temperature 1450 °F, Time 10000 hour |
1% creep |
ATI Allegheny Ludlum 310S Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Creep Strength | 20.0 MPa @Temperature 788 °C, Time 3.60e+7 sec |
2900 psi @Temperature 1450 °F, Time 10000 hour |
1% creep |
ATI Allegheny Ludlum 310Si Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Creep Strength | 20.0 MPa @Time 3.60e+6 sec |
2900 psi @Time 1000 hour |
in water at 95°C |
BASF Ultrason S 3010 PSU Ultrason S 3010 is an unreinforced, higher viscosity injection molding and extrusion PSU grade, tougher and with improved chemical resistance. It conforms to FDA requirements of 21 CFR 177.1655. |