Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Charpy Impact Unnotched | 0.800 - 1.20 J/cm² @Temperature 23.0 °C |
3.81 - 5.71 ft-lb/in² @Temperature 73.4 °F |
Injection and Compression; ISO 179/ 1eU |
Raschig Group 3505 Epoxy Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed.. |
|||
Charpy Impact Unnotched | 0.800 - 1.20 J/cm² @Temperature 23.0 °C |
3.81 - 5.71 ft-lb/in² @Temperature 73.4 °F |
Injection and Compression; ISO 179/ 1eU |
Raschig Group 3535 Epoxy Glass fiber-reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties adn dimensional stability even at high temperatures. Form: Low dust granulate pack.. |
|||
Charpy Impact Unnotched | 0.700 - 1.20 J/cm² @Temperature 23.0 °C |
3.33 - 5.71 ft-lb/in² @Temperature 73.4 °F |
Injection; ISO 179/ 1eU |
Raschig Group RALUPOL® 2200 UP Polyester Organically filled polyester molding compound. Low post-shrinkage, good electrical values and mechanical properties, high surface quality and good color stability (non-yellowing). This product meets.. |
|||
Charpy Impact Unnotched | 1.20 - 1.20 J/cm² @Temperature -30.0 - -30.0 °C |
5.71 - 5.71 ft-lb/in² @Temperature -22.0 - -22.0 °F |
Average value: 1.20 J/cm² Grade Count:2 |
Overview of materials for Polyphthalamide (PPA), Aramid Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Aramid Fiber". Each property range of values reported is minimum and maximum values of .. |
|||
Charpy Impact Unnotched | 1.00 - 1.20 J/cm² @Temperature 23.0 °C |
4.76 - 5.71 ft-lb/in² @Temperature 73.4 °F |
Injection; ISO 179/ 1eU |
Raschig Group SURAPLAST UPA 63 UP Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for.. |
|||
Charpy Impact Unnotched | 1.20 - 1.20 J/cm² @Temperature -40.0 - -20.0 °C |
5.71 - 5.71 ft-lb/in² @Temperature -40.0 - -4.00 °F |
Average value: 1.20 J/cm² Grade Count:1 |
Overview of materials for Polyphenylene Sulfide (PPS) with 50% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 50% Glass Fiber Filler". Specific grades with glass content between 45%.. |
|||
Charpy Impact Unnotched | 0.500 - 1.20 J/cm² | 2.38 - 5.71 ft-lb/in² | Average value: 0.975 J/cm² Grade Count:4 |
Overview of materials for Polyphenylene Sulfide (PPS), Aramid Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Aramid Fiber". Each property range of values reported is minimum and maximu.. |
|||
Charpy Impact Unnotched | 1.00 - 1.20 J/cm² | 4.76 - 5.71 ft-lb/in² | Injection; ISO 179/1eU |
Raschig Group RESINOL® 400 EPF Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and very good mechanical properties. This product meets .. |