Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Charpy Impact, Notched | 0.250 - 0.350 J/cm² @Temperature 23.0 °C |
1.19 - 1.67 ft-lb/in² @Temperature 73.4 °F |
Injection and Compression; ISO 179/ 1eA |
Raschig Group 3505 Epoxy Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed.. |
|||
Charpy Impact, Notched | 0.250 - 0.350 J/cm² @Temperature 23.0 °C |
1.19 - 1.67 ft-lb/in² @Temperature 73.4 °F |
Injection and Compression; ISO 179/ 1eA |
Raschig Group 3535 Epoxy Glass fiber-reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties adn dimensional stability even at high temperatures. Form: Low dust granulate pack.. |
|||
Charpy Impact, Notched | 0.200 - 0.350 J/cm² | 0.952 - 1.67 ft-lb/in² | Injection; ISO 179/1eA |
Raschig Group 4554 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to 300°C, exceptional electrical properties, good mechanical strength, very good dimensional stability. Processi.. |
|||
Charpy Impact, Notched | 0.150 - 0.350 J/cm² | 0.714 - 1.67 ft-lb/in² | Compression; ISO 179/1eA |
Raschig Group DECAL® 5431 Phenolic Organically and inorganically filled phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/.. |
|||
Charpy Impact, Notched | 0.150 - 0.350 J/cm² | 0.714 - 1.67 ft-lb/in² | Compression; ISO 179/1eA |
Raschig Group DECAL® 937 Phenolic Mica reinforced phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (W.. |
|||
Charpy Impact, Notched | 0.250 - 0.350 J/cm² | 1.19 - 1.67 ft-lb/in² | Compression; ISO 179/1eA |
Raschig Group RALUPOL® 4802 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u.. |
|||
Charpy Impact, Notched | 0.250 - 0.350 J/cm² | 1.19 - 1.67 ft-lb/in² | Compression; ISO 179/1eA |
Raschig Group RALUPOL® 5000 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, excellent heat resistance, good mechanical strength. This product meets the all.. |
|||
Charpy Impact, Notched | 0.250 - 0.350 J/cm² | 1.19 - 1.67 ft-lb/in² | Compression; ISO 179/1eA |
Raschig Group RALUPOL® 802 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength, good heat resistance. This product meets the allowed up.. |
|||
Charpy Impact, Notched | 0.250 - 0.350 J/cm² | 1.19 - 1.67 ft-lb/in² | Compression; ISO 179/1eA |
Raschig Group RALUPOL® 804 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy m.. |
|||
Charpy Impact, Notched | 0.300 - 0.350 J/cm² | 1.43 - 1.67 ft-lb/in² | Average value: 0.338 J/cm² Grade Count:4 |
Overview of materials for Polypropylene with 40% Calcium Carbonate (CaCO3) Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Calcium Carbonate (CaCO3) Filler". Specific grades with primary filler content be.. |
|||
Charpy Impact, Notched | 0.250 - 0.350 J/cm² | 1.19 - 1.67 ft-lb/in² | Compression; ISO 179/1eA |
Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl phthalate molding compound free from halogens. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exc.. |