Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Ball Indentation Hardness | 165 MPa | 23900 psi | dry; ISO 2039-1 |
Murtfeldt Murylon® 6 Cast Nylon 6 Murylon® 6 CAST has extremely low levels of residual stress thanks to the casting procedure used to produce it. This material is therefore ideally suited to extensively processed components.Specia.. |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | dry; ISO 2039-1 |
Murtfeldt Murylon® A GF Nylon 66, Glass Reinforced Murylon® A’s impressive characteristics are enhanced with admixed glass fibers. This results in a clear improvement in cold flow behavior and dimensional stability, enabling higher static pressure.. |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
Murtfeldt Murylon® HT Nylon 46 The use of this highly temperature resistant polyamide enables reliable operation up to a constant service temperature of 155°C . The material retains its rigidity and creep strength over the entir.. |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
Nilit FRIANYL A63 HH-GV10 Nylon 6.6 for injection molding, 10% glass fiber reinforced Nylon 6.6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
Nilit FRIANYL B63 KF20 Nylon 6 for injection molding, 20% short glass fiber reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
Nilit FRIANYL B63 H-KV30 Nylon 6 for injection molding, 30% glass ball reinforced Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
Nilit FRIANYL B63 KV30 Nylon 6 for injection molding, 30% glass ball reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
Quadrant EPP Duratron® PEI U1000 PEI, unfilled, extruded (ISO Data) Duratron U1000 PEI is an amber translucent (non-optical quality) amorphous thermoplastic material, offering high strength and heat resistance. It performs continuously to 170 °C, making it ideal fo.. |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
Quadrant EPP Ertalon® 4.6 PA 4.6, extruded (ISO Data) Compared with conventional nylons, Ertalon 4.6 features a better retention of stiffness and creep resistance over a wide range of temperatures as well as superior heat ageing resistance. Therefore, .. |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
Quadrant EPP Ertalon® 6 PLA PA 6, cast (ISO Data) Unmodified cast nylon 6 grade exhibiting characteristics which come very close to those of Ertalon 66 SA. It combines high strength, stiffness and hardness with good creep and wear resistance, heat .. |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
Quadrant EPP Ertalon® 66 GF30 PA 66, 30% glass filled, extruded (ISO Data) Compared with virgin PA 66, this 30 % glass fibre reinforced and heat stabilised nylon grade offers increased strength, stiffness, creep resistance and dimensional stability whilst retaining an exce.. |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
Quadrant EPP Nylatron® GS PA 6 + MoS2, extruded (ISO Data) The addition of MoS2 renders this material somewhat stiffer, harder and dimensionally more stable than Ertalon 66 SA, but results in some loss of impact strength. The nucleating effect of the molybd.. |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
Nilit FRIANYL A63 H-GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced Nylon 6.6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
Nilit FRIANYL A63 KV20 Nylon 6.6 for injection molding, 20% glass ball reinforced Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
Nilit FRIANYL B63 W-KV30 Nylon 6 for injection molding, 30% glass ball reinforced Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
Nilit RECONYL A SG30 Recycled nylon 6.6 for injection molding, 30% mineral filled Recycled nylon 6.6 for injection molding (available only in black).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
Nilit RECONYL B KV30 Recycled nylon 6 for injection molding, 30% glass ball reinforced Recycled nylon 6 for injection molding (available only in black).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Ball Indentation Hardness | 165 - 200 MPa | 23900 - 29000 psi | Average value: 172 MPa Grade Count:3 |
Overview of materials for Nylon 46, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Unreinforced". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039 |
GEHR Plastics PA 6.6-30GF Nylon 6.6, 30% Glass Fiber, Dry Polyamide shows both a high thermostability and high stiffness, hardness and toughness. These are some of the main characteristics. Due to the fact, that the good mechanical characteristics will be .. |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
Styrolution Luran® HD 20 SAN Luran HD 20 is an easy-flow grade of SAN especially designed for the medical market. It is suitable for moldings with very thin walls and / or adverse flow length to wall ratio. It features very goo.. |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | DIN 53456 |
Zell-Metall Engineering Plastics Zellamid 1100 MO Improved sliding and self lubricating properties are achieved by the addition of molybdenum disulphide. UV-radiation resistance is enhanced.Color: blackApplications: For conveyor screws |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | conditioned; ISO 2039-1 |
EMS-Grivory Grivory® XE 4105 nat PA610-GF50 Product description: Grilamid XE 4105 natural is a 50% glass fiber reinforced, heat stabilized polyamide 610 (PA610) injection molding grade. This product is to a large extent based on renewable raw.. |
|||
Ball Indentation Hardness | 165 MPa @Time 30.0 sec |
23900 psi @Time 0.00833 hour |
DIN 53 456 |
Hippe PEI A material with very high mechanical strength and high thermoforming stability which can be used at high temperatures. Distinguished by constant dielectric properties, a wide range of frequency and .. |
|||
Ball Indentation Hardness | 165 MPa @Load 36.5 kg, Time 30.0 sec |
23900 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
BASF Ultraform® S1320 003 POM Description: Is a POM, free-flowing, rapidly solidifying grade for moldings difficult to produce by injection molding and having low wall thicknesses, higher stiffness and thermal stability.Informat.. |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | value at 30 sec.; ISO 2039-1 |
CENTROPLAST CENTROMID 6 G Polyamide 6 Cast This material has good machinability and can be bonded or welded. Its applications include sliding bearings, hammerheads, and toothed gears.Information provided by CENTROPLAST Engineering Plastics .. |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO2039.1 DIN.53456 |
Omnia Plastica Omniamid PA6 G G - Dry Cast nylon 6. The method of production of this polyamide (i.e. the polymerisation of the caprolactam directly in the mould) allows the production of stock shapes in larger than normal dimensions, su.. |
|||
Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
BASF Ultradur® B 4300 K6 30% Glass Bead Filled PBT Description: Is a PBT + ASA, Injection-molding grades containing 30% of glass beads for industrial parts with low warpage.Applications: Precision parts for optical instruments, fuel tank sensor unit.. |
|||
Ball Indentation Hardness | 165 MPa @Load 36.5 kg, Time 30.0 sec |
23900 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
Styrolution Luran® 368 R Crystal Clear Transparent 77851 SAN Description: General-purpose grade with well-balanced properties, suitable for injection molding and extrusion. Especially for applications where highest transparency and low natural color is requir.. |